Assignee: Mitsubishi Chemical Corp
•
Filing: 1984-06-15
•
Granted: 1986-04-29
•
Expires: 2004-06-15
Abstract
Abstract A process for producing an air-permeable film, which comprises: (a) biaxially stretching a tubular unstretched film of a composition comprising 42 to 87 vol % of a thermoplastic resin and 58 to 13 vol % of an inorganic filler along a truncated-conical mandrel; (b) blowing a gas over the outside of the biaxially stretched tubular film to cool said film; and (c) simultaneously blowing a gas continuously into the tube of the film so as to penetrate the gas through the film and go outside.
Inventors
- 👤 Katsumi Okuyama
- 👤 Hiroyasu Mizutani
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 22:28
CPC Classifications
B; B29; B29D; B29D7/00; B29D7/01; B29C; B29C55/00; B29C55/28; B29D99/00; B29D99/005; C; C08; C08J; C08J5/00; C08J5/18; B29C48/00; B29C48/03; B29C48/09; B29C48/10; B29K; B29K2023/00; B29K2105/00; B29K2105/06; B29K2105/16; B29L; B29L2031/00; B29L2031/48; B29L2031/4871; B29L2031/4878; B29L2031/755
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
95 words
A process for producing an air-permeable film, which comprises: (a) biaxially stretching a tubular unstretched film of a composition comprising 42 to 87 vol % of a thermoplastic resin and 58 to 13 vol % of an inorganic filler along a truncated-conical mandrel; (b) blowing a gas over the outside of the biaxially stretched tubular film to cool said film; and (c) simultaneously and, continuously blowing a gas under controlled pressure into the tube of the film such that the gas penetrates through the film around its entire circumference to the exterior of the film.
Claim 2
Dependent Claim
95 words
A process for producing an air-permeable film, which comprises: (a) biaxially stretching a tubular unstretched film of a composition comprising 42 to 87 vol % of a thermoplastic resin and 58 to 13 vol % of an inorganic filler along a truncated-conical mandrel; (b) blowing a gas over the outside of the biaxially stretched tubular film to cool said film; and (c) simultaneously and, continuously blowing a gas under controlled pressure into the tube of the film such that the gas penetrates through the film around its entire circumference to the exterior of the film.
Claim 3
Dependent Claim
34 words
The process according to claim 1, wherein said thermoplastic resin is an ethylene/α-olefin copolymer having a density of 0.910 to 0.940 g/cm 3 and a melt flow rate of 0.1 to 5 g/10 min.
Claim 4
Dependent Claim
34 words
The process according to claim 1, wherein said thermoplastic resin is a high-density polyethylene having a density of 0.941 g/cm 3 or more and a melt flow rate of 1.0 g/10 min or less.
Claim 5
Dependent Claim
62 words
The process according to claim 1, wherein said thermoplastic resin is an ethylene/α-olefin copolymer having a density of 0.910 to 0.940 g/cm 3 , a melt flow rate of 0.1 to 5 g/10 min and a Q value of 4 or more, said Q value being defined as the ratio of the weight average molecular weight to the number average molecular weight.
Claim 6
Dependent Claim
102 words
The process according to claim 1, wherein said thermoplastic resin is a mixture of 10 to 90 wt % of an ethylene/α-olefin copolymer having a density of 0.910 to 0.940 g/cm 3 and a melt flow rate of 0.1 to 5 g/10 min and 90 to 10 wt % of a high-density polyethylene having a density of at least 0.941 g/cm 3 , a melt flow rate of no more than 1.0 g/10 min and a Q value of at least 8, said Q value being defined as the ratio of the weight average molecular weight to the number average molecular weight.
Claim 7
Dependent Claim
20 words
The process according to claim 1, wherein said inorganic filler has an average particle size of 0.05 to 4 μm.
Claim 8
Dependent Claim
85 words
The process according to claim 1, wherein said inorganic filler is a mixture of 50 to 97 vol % of a first inorganic filler having an average particle size of 0.7 to 4 μm and 50 to 3 vol % of a second inorganic filler having an average particle size of 0.05 to 0.7 μm, the two fillers being mixed in such proportions that the ratio of the average particle size of the first filler to that of the second filler is 2 to 20.
Claim 9
Dependent Claim
26 words
The process according to claim 1, wherein the biaxial stretching ratio is in the range of 1.5 to 4 in both the machine and transverse directions.
Claim 10
Dependent Claim
26 words
The process according to claim 1, wherein said inorganic filler is calcium carbonate, calcium oxide, talc, clay, silica, titanium oxide, alumina, aluminum sulfate, or mixtures thereof.
Claim 11
Dependent Claim
39 words
The process according to claim 7, wherein said first inorganic filler has an average particle size of 0.8 to 2 μm, and said second inorganic filler has an average particle size in the range of 0.1 to 0.6 μm.
Claim 12
Dependent Claim
27 words
The process according to claim 7, wherein the ratio of the average particle size of said first filler to said second filler ranges from 2.5 to 15.
Claim 13
Dependent Claim
29 words
The process according to claim 7, wherein 60 to 95 vol % of said first inorganic filler is mixed with 40 to 5 vol % of said second filler.
Claim 14
Dependent Claim
32 words
The process according to claim 1, wherein the composition of step (a) comprises 55 to 80 vol % of said thermoplastic resin and 45 to 20 vol % of said inorganic filler.
Claim 15
Dependent Claim
28 words
The process according to claim 1, wherein the stretching temperature (Ts) (°C.) and the melting point (Tm) (°C.) of the film being stretched have the relationship: Tm-50≦Ts≦Tm-5 (°C.).
Claim 16
Dependent Claim
29 words
The process according to claim 1, wherein gas is blown into the tube of film in step (c) at a rate of from 0.1 to 150 Nl/m 2 .min.
Claim 17
Dependent Claim
19 words
The process according to claim 15, wherein said gas flow rate ranges from 1 to 70 Nl/m 2 .min.
Claim 18
Dependent Claim
48 words
The process according to claim 1, wherein said product air-permeable film, having a thickness ranging from 25 to 150 μm, has an air-permeability within the range of 25 to 30,000 seconds/100 cc and a moisture permeability within the range of 300 to 25,000 g/m 2 in 24 hours.
References Cited (Backward Citations)
US2987767A
Cited
US3154461A
Cited
US3765999A
Cited
JPS4819229B1
Cited
US3758661A
Cited
US4350655A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-04-28 | 1989-10-28 | 1990-04-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-04-28 | 1993-10-28 | 1994-04-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-04-28 | 1997-10-28 | 1998-04-29 | $7700.00 | Window Closed / Lapsed |