Method for molding concrete blocks or bricks
Assignee: Individual
•
Filing: 1985-12-31
•
Granted: 1987-10-27
•
Expires: 2005-12-31
Abstract
Abstract Concrete elements, such as blocks or bricks, are molded or cast by forming in a primary mold cavity a secondary mold made of a portion of a thermoplastic film which has been contacted with a flat heater surface to assure a uniformly heated film portion which is then sucked into the primary mold cavity without wrinkles and filled with concrete mix. The secondary mold with the concrete mix in it is withdrawn, for example, sucked out of the primary mold cavity well before any effective hardening of the concrete mix, so that curing and hardening takes place in the secondary mold outside the primary mold cavity. This early withdrawing is important because it avoids expansion of the curing mix in the primary mold, whereby removal from the primary mold is facilitated. Additionally, the early removal with the aid of the secondary mold assures a more efficient use of the primary molds which are used again while the hardening is still going on in the secondary mold. The apparatus for performing the method includes a turntable and stepwise drive means for sequentially stepping the turntable carrying a plurality of primary molds into cooperation with several work stations which are so controlled that the early withdrawal of the filled secondary mold from the primary mold cavity is assured.
Inventors
- 👤 Lindsey B. Davis, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 15:06
CPC Classifications
B; B28; B28B; B28B7/00; B28B7/36; B28B7/364; B28B13/00; B28B13/02; B28B13/0215; B28B13/023; B28B13/04; B28B13/06; B28B5/00; B28B5/06; B28B5/08; B28B7/34; B28B7/348; B29; B29C; B29C51/00; B29C51/10; B29C33/00; B29C33/56; B29C33/68
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
346 words
In a method for molding concrete elements in an open top mold having a primary mold cavity defined by walls lined with a thermoplastic film which is first moved onto said open top of said mold, heated and sucked by vacuum into said primary mold cavity which is then filled with a concrete mix for the formation of the element, the improvement comprising the following steps: (a) contacting at least that portion of said thermoplastic film which smoothly covers said open top, with a flat heater surface of a solid heating device for uniformly and entirely heating said portion of said thermoplastic film on said open top through said flat heater surface, while simultaneously closing said open top with said solid heating device, said heating softening said film portion sufficiently for pulling the heated film portion into said primary mold cavity by suction, (b) evacuating said primary mold cavity while it is still closed by said heating device, sufficiently for lining the primary mold cavity with a secondary mold formed of said thermoplastic film in said primary mold cavity, (c) removing the heating device for opening said secondary mold in said primary mold cavity, (d) filling the secondary mold in said primary mold cavity with a concrete mix, and (e) compacting said concrete mix in said secondary mold while the seconsary mold is still in said primary mold and withdrawing the secondary mold filled with compacted concrete mix from said primary mold cavity prior to any substantially noticeable or effective hardening of said concrete mix in said secondary mold which together with the compacted but not yet effectively hardened concrete mix forms a unit sufficiently shape retaining for an immediate transportation and completing the curing and hardening of the concrete mix in said secondary mold outside said primary mold with the curing concrete mix a sufficiently shape retaining unit so that expansion forces resulting from the hardening and curing are substantially prevented from becoming effective in the primary mold and for permitting the renewed use of said primary mold cavity before the formed concrete mix hardens.
Claim 2
Dependent Claim
346 words
In a method for molding concrete elements in an open top mold having a primary mold cavity defined by walls lined with a thermoplastic film which is first moved onto said open top of said mold, heated and sucked by vacuum into said primary mold cavity which is then filled with a concrete mix for the formation of the element, the improvement comprising the following steps: (a) contacting at least that portion of said thermoplastic film which smoothly covers said open top, with a flat heater surface of a solid heating device for uniformly and entirely heating said portion of said thermoplastic film on said open top through said flat heater surface, while simultaneously closing said open top with said solid heating device, said heating softening said film portion sufficiently for pulling the heated film portion into said primary mold cavity by suction, (b) evacuating said primary mold cavity while it is still closed by said heating device, sufficiently for lining the primary mold cavity with a secondary mold formed of said thermoplastic film in said primary mold cavity, (c) removing the heating device for opening said secondary mold in said primary mold cavity, (d) filling the secondary mold in said primary mold cavity with a concrete mix, and (e) compacting said concrete mix in said secondary mold while the seconsary mold is still in said primary mold and withdrawing the secondary mold filled with compacted concrete mix from said primary mold cavity prior to any substantially noticeable or effective hardening of said concrete mix in said secondary mold which together with the compacted but not yet effectively hardened concrete mix forms a unit sufficiently shape retaining for an immediate transportation and completing the curing and hardening of the concrete mix in said secondary mold outside said primary mold with the curing concrete mix a sufficiently shape retaining unit so that expansion forces resulting from the hardening and curing are substantially prevented from becoming effective in the primary mold and for permitting the renewed use of said primary mold cavity before the formed concrete mix hardens.
Claim 3
Dependent Claim
48 words
The method of claim 1, comprising pulling-off said thermoplastic film from a film supply roller providing a continuous web of film, smoothly drawing said portion of said thermoplastic film onto said open mold top, performing said contacting step, and cutting off said portion from said continuous film web.
Claim 4
Dependent Claim
39 words
The method of claim 1, further comprising temporarily increasing the pressure inside said primary mold cavity during said heating for uniformly pressing the entire film portion on said open top against said flat heater surface of said heating device.
Claim 5
Dependent Claim
43 words
The method of claim 1, comprising maintaining said flat heater surface of said heater member at a uniform temperature within a temperature range sufficient for making the entire volume of said film portion uniformly supple and pliant in response to said evacuating step.
Claim 6
Dependent Claim
39 words
The method of claim 1, wherein said thermoplastic film has a thickness within the range of about 100 μm to about 300 μm (about 4 to about 12 mils), for forming said secondary mold in said primary mols cavity.
Claim 7
Dependent Claim
25 words
The method of claim 1, wherein said contacting of the thermoplastic film by the flat heater surface is maintained for about 8 to 16 seconds.
Claim 8
Dependent Claim
57 words
The method of claim 1, wherein said compacting comprises applying a pressure to the open top mold, said pressure being in the range of about 10 to 80 tons per square foot sufficient for compacting said concrete mix to about 90% of its original uncompacted volume, thereby precisely filling the secondary mold in said primary mold cavity.
Claim 9
Dependent Claim
38 words
The method of claim 7, wherein said withdrawing of said filled secondary mold from said primary mold cavity takes place substantially immediately after said compacting, within about 5 to about 20 seconds after the completion of said compacting.
Claim 10
Dependent Claim
29 words
The method of claim 1, further comprising inserting a pattern forming member into said primary mold cavity prior to covering said open mold top with said thermoplastic film portion.
Claim 11
Dependent Claim
26 words
The method of claim 1, further comprising performing said filling in at least two steps for filling different types of concrete mix into said secondary mold.
Claim 12
Dependent Claim
47 words
The method of claim 1, wherein said step of withdrawing is performed by applying suction to said secondary mold for withdrawing the secondary mold with the concrete mix therein, from the primary mold cavity prior to any effective hardening of the concrete mix into a concrete block.
References Cited (Backward Citations)
US29945A
Cited
US1584595A
Cited
US2058295A
Cited
US2926385A
Cited
US3021569A
Cited
US3159695A
Cited
US3113345A
Cited
US3193599A
Cited
US3492384A
Cited
US3703572A
Cited
US3712771A
Cited
USRE29945E
Cited
US3848034A
Cited
US4060364A
Cited
US4331628A
Cited
US4098562A
Cited
US4213926A
Cited
GB2040214A
Cited
GB2153738A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-10-26 | 1991-04-27 | 1991-10-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-10-26 | 1995-04-27 | 1995-10-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-10-26 | 1999-04-27 | 1999-10-27 | $7700.00 | Window Closed / Lapsed |