Preparation and renovation of a fusion roller for a xerographic machine, fusion roller and vulcanizable composition
Assignee: ATELIERS DE CONCEPTIONS ET D'INNOVATIONS INDUSTRIELLES A CORP OF FRANCE
•
Filing: 1986-02-11
•
Granted: 1987-10-20
•
Expires: 2006-02-11
Abstract
Abstract The invention relates to a method of preparation of an outer cover of a fusion roller for a xerographic machine, this cover being constituted by a homogeneous layer covering a hollow metal core receiving heating means. According to the invention, this method comprises the steps of (a) cold kneading a mixture having, for 100 parts of fluorine-containing rubber, 55 to 60 parts of carbon black, 2 to 6 parts of magnesium oxide, 4 to 8 parts of calcium hydroxyde and 0 to 2 parts of polyethylene wax; (b) forming the covering material by extrusion or calendering of this mixture; (c) application of this material in a homogeneous layer to the surface of the metallic core of the roller; (d) vulvanization at elevated temperature and under pressure of the material thus applied to the core; (e) dressing of the cover to a constant thickness.
Inventors
- 👤 Lucien P. Michel
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 16:01
CPC Classifications
G; G03; G03G; G03G15/00; G03G15/20; G03G15/2003; G03G15/2014; G03G15/2053; G03G15/2057; B; B29; B29D; B29D99/00; B29D99/0032; B29D99/0035; B29L; B29L2031/00; B29L2031/32; B29L2031/324; Y; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49544; Y10T29/49545; Y10T29/4956; Y10T29/49563; Y10T29/4998; Y10T29/49982
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
139 words
A method of preparation of an external cover of a fusion roller for a xerographic machine, said cover being constituted by a homogeneous layer covering a hollow core receiving heating means, said method comprising the stages of: (a) cold kneading a mixture having, for 100 parts of a rubber of a fluorine-containing elastomer, 55 to 60 parts of carbon black, 2 to 6 parts of magnesium oxide, 4 to 8 parts of calcium hydroxide and 0 to 2 parts of polyethylene wax, (b) forming said mixture by extrusion or calendering into a cover material, (c) application of said cover material in a homogeneous layer to the surface of said core of said roller, (d) vulcanisation at elevated temperature and under pressure of said cover material thus applied onto said core, (e) dressing of said cover to a constant thickness.
Claim 2
Independent Claim
139 words
A method of preparation of an external cover of a fusion roller for a xerographic machine, said cover being constituted by a homogeneous layer covering a hollow core receiving heating means, said method comprising the stages of: (a) cold kneading a mixture having, for 100 parts of a rubber of a fluorine-containing elastomer, 55 to 60 parts of carbon black, 2 to 6 parts of magnesium oxide, 4 to 8 parts of calcium hydroxide and 0 to 2 parts of polyethylene wax, (b) forming said mixture by extrusion or calendering into a cover material, (c) application of said cover material in a homogeneous layer to the surface of said core of said roller, (d) vulcanisation at elevated temperature and under pressure of said cover material thus applied onto said core, (e) dressing of said cover to a constant thickness.
Claim 3
Dependent Claim
36 words
A method according to claim 1, in which there is provided, during said dressing stage, a final cut of the surface of said cover permitting the closing by polishing of the cells of said cover material.
Claim 4
Dependent Claim
25 words
A method according to claim 1, comprising, after the vulcanisation stage, a stoving stage for permitting the degassing and stabilisation of said vulcanised cover material.
Claim 5
Dependent Claim
19 words
A method according to claim 1, in which said cover is dressed to a thickness less than 0.25 mm.
Claim 6
Dependent Claim
63 words
A method according to claim 1, in which said roller comprises a central cylindrical region and two divergent truncoconical end regions, said dressing stage being carried out to a constant thickness throughout the surface of said roller and the relative speed of the dressing tool with respect to the surface to be dressed being maintained constant at all points in said truncoconical regions.
Claim 7
Dependent Claim
20 words
A method according to claim 1, having in addition a final stage of matting the inside wall of the core.
Claim 8
Independent Claim
128 words
A method of renovation of fusion rollers or a xerographic machine comprising the stages of: (a) stripping a core of a roller by grinding to a desired shape; (b) cold kneading a mixture having, for 100 parts of a rubber of a flourine-containing elastomer, 55 to 60 parts of carbon black, 2 to 6 parts of magnesium oxide, 4 to 8 parts of calcium hydroxide and 0 to 2 parts of polyethylene wax; (c) forming said mixture by extrusion or calendering into a cover material; (d) applying said cover material in a homogeneous layer to the surface of said core of said roller, (e) vulcanizing said cover material thus applied onto said core at an elevated temperature and under pressure, (f) dressing said cover to a constant thickness.
Claim 9
Independent Claim
128 words
A method of renovation of fusion rollers or a xerographic machine comprising the stages of: (a) stripping a core of a roller by grinding to a desired shape; (b) cold kneading a mixture having, for 100 parts of a rubber of a flourine-containing elastomer, 55 to 60 parts of carbon black, 2 to 6 parts of magnesium oxide, 4 to 8 parts of calcium hydroxide and 0 to 2 parts of polyethylene wax; (c) forming said mixture by extrusion or calendering into a cover material; (d) applying said cover material in a homogeneous layer to the surface of said core of said roller, (e) vulcanizing said cover material thus applied onto said core at an elevated temperature and under pressure, (f) dressing said cover to a constant thickness.
Claim 10
Dependent Claim
14 words
A fusion roller for a xerographic machine, obtained by said method of claim 1.
Claim 11
Dependent Claim
14 words
A fusion roller for a xerographic machine, obtained by said method of claim 7.
Claim 12
Dependent Claim
61 words
A vulcanisable composition for a covering material for a fusion roller for a xerographic machine, said vulcanisable composition formed of a mixture having, for 100 parts of rubber of a fluorine-and-hydrogen-containing elastomer, 55 to 60 parts of carbon black, 2 to 6 parts of magnesium oxide, 4 to 8 parts of calcium hydroxide and 0 to 2 parts of polyethylene wax.
Claim 13
Dependent Claim
61 words
A vulcanisable composition for a covering material for a fusion roller for a xerographic machine, said vulcanisable composition formed of a mixture having, for 100 parts of rubber of a fluorine-and-hydrogen-containing elastomer, 55 to 60 parts of carbon black, 2 to 6 parts of magnesium oxide, 4 to 8 parts of calcium hydroxide and 0 to 2 parts of polyethylene wax.
Claim 14
Dependent Claim
61 words
A vulcanizable composition for a covering material for a fusion roller for a xerographic machine, said vulcanizable composition formed of a mixture having, for 100 parts of rubber of a fluorine-containing elastomer, 55 to 60 parts of carbon black, 2 to 6 parts of magnesium oxide, 4 to 8 parts of calcium hydroxide and 1/2 to 2 parts of polyethylene wax.
Claim 15
Dependent Claim
61 words
A vulcanizable composition for a covering material for a fusion roller for a xerographic machine, said vulcanizable composition formed of a mixture having, for 100 parts of rubber of a fluorine-containing elastomer, 55 to 60 parts of carbon black, 2 to 6 parts of magnesium oxide, 4 to 8 parts of calcium hydroxide and 1/2 to 2 parts of polyethylene wax.
References Cited (Backward Citations)
GB1143562A
Cited
US3877125A
Cited
US3934547A
Cited
DE2442173A1
Cited
US3999038A
Cited
US3929095A
Cited
US4083092A
Cited
US4149797A
Cited
DE2824994A1
Cited
US4375505A
Cited
JPS5946666A
Cited
JPS5946667A
Cited
US4446270A
Cited
US4503171A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-10-19 | 1991-04-20 | 1991-10-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-10-19 | 1995-04-20 | 1995-10-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-10-19 | 1999-04-20 | 1999-10-20 | $7700.00 | Window Closed / Lapsed |