US4698386A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Polyorganosiloxane compositions
Assignee: Momentive Performance Materials Japan LLC
•
Filing: 1986-05-28
•
Granted: 1987-10-06
•
Expires: 2006-05-28
Abstract
Abstract Polyorganosiloxane compositions comprising: (A) a linear and/or branched polyorganosiloxane, with a viscosity of 50 to 100,000 cP at 25 DEG C., wherein 0.7 to 1.8 vinyl radicals bonded to silicon atoms, on average, are present in each molecule, and the remaining organic radicals bonded to silicon atoms are substituted or unsubstituted monovalent hydrocarbon radicals which does not include unsaturated aliphatic radicals, and 30% or more portion of the molecules has only one silicon-bonded vinyl radical in the molecule; (B) a polyorganohydrogensiloxane, wherein more than two hydrogen atoms bonded to silicon atoms, on average, are present in each molecule, in an amount such that the number of silicon-bonded hydrogen atoms may be 0.5 to 5 per vinyl radical in the molecule (A); (C) a catalytic amount of platinum compounds; and (D) anthraquinone dyes and/or azo dyes, in an amount from 1 to 2,000 ppm to (A).
Inventors
- 👤 Tetsuo Fujimoto
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 08:29
CPC Classifications
C; C08; C08L; C08L83/00; C08L83/04; C08K; C08K5/00; C08K5/0008; C08K5/0041; C08G; C08G77/00; C08G77/04; C08G77/12; C08G77/20; C08G77/70
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
175 words
A polyorganosiloxane composition comprising: (A) a linear and/or branched polyorganosiloxane (A), with a viscosity of 50 to 100,000 cP at 25° C., wherein 0.7 to 1.8 silicon-bonded vinyl radicals, on average, are present in each molecule, and the remaining organic radicals bonded to a silicon atom are substituted or unsubstituted monovalent hydrocarbon radicals which do not include unsaturated aliphatic radicals, and 30% or more portion of the molecules have only one silicon-bonded vinyl radical in the molecule; (B) a polyorganohydrogensiloxane (B), wherein more than two silicon-bonded hydrogen atoms, on average, are present in each molecule and the remaining organic radicals bonded to a silicon atom are substituted or unsubstituted monovalent hydrocarbon radicals which do not include unsaturated aliphatic radicals, in an amount such that the number of silicon-bonded hydrogen atoms may be 0.5 to 5 per vinyl radical in polyorganosiloxane (A); (C) a catalytic amount of platinum compound; and (D) a dye selected from the group consisting of anthraquinone dye and azo dye in an amount from 1 to 2,000 ppm based on polyorganosiloxane (A).
Claim 2
Dependent Claim
175 words
A polyorganosiloxane composition comprising: (A) a linear and/or branched polyorganosiloxane (A), with a viscosity of 50 to 100,000 cP at 25° C., wherein 0.7 to 1.8 silicon-bonded vinyl radicals, on average, are present in each molecule, and the remaining organic radicals bonded to a silicon atom are substituted or unsubstituted monovalent hydrocarbon radicals which do not include unsaturated aliphatic radicals, and 30% or more portion of the molecules have only one silicon-bonded vinyl radical in the molecule; (B) a polyorganohydrogensiloxane (B), wherein more than two silicon-bonded hydrogen atoms, on average, are present in each molecule and the remaining organic radicals bonded to a silicon atom are substituted or unsubstituted monovalent hydrocarbon radicals which do not include unsaturated aliphatic radicals, in an amount such that the number of silicon-bonded hydrogen atoms may be 0.5 to 5 per vinyl radical in polyorganosiloxane (A); (C) a catalytic amount of platinum compound; and (D) a dye selected from the group consisting of anthraquinone dye and azo dye in an amount from 1 to 2,000 ppm based on polyorganosiloxane (A).
Claim 3
Dependent Claim
16 words
The composition according to claim 1, wherein vinyl radicals are attached to a terminal silicon atom.
Claim 4
Dependent Claim
12 words
The composition according to claim 1, wherein polyorganopolysiloxane (A) is substantially linear.
Claim 5
Dependent Claim
23 words
The composition according to claim 1, wherein 40 to 85% of said molecules of said polyorganosiloxane (A) have only one silicon-bonded vinyl radical.
Claim 6
Dependent Claim
28 words
The composition according to claim 1, wherein vinyl radicals attached to a silicon atom in each molecule of polyorganopolysiloxane (A) are ranging, on average, from 0.75 to 1.4.
Claim 7
Dependent Claim
45 words
The composition according to claim 1, wherein organic radicals attached to a silicone atom in each molecule of polyorganopolysiloxane (A), other than vinyl radicals, are either methyl or phenyl radicals, and phenyl radical content is 50 mole % or less of the total organic radicals.
Claim 8
Dependent Claim
27 words
The composition according to claim 1, wherein organic radicals attached to a silicon atom in each molecule of polyorganopolysiloxane (A), other than vinyl radicals, are methyl radicals.
Claim 9
Dependent Claim
21 words
The composition according to claim 1, wherein viscosity of polyorganopolysiloxane (A) at 25° C. is ranging from 300 to 5,000 cP.
Claim 10
Dependent Claim
34 words
The composition according to claim 1, wherein polyorganopolysiloxane (A) is synthesized by equilibration of vinyl endblocked polyorganosiloxanes, linear and/or branched polyorganosiloxanes without vinyl radicals, and if necessary with cyclic polyorganosiloxanes having no vinyl radicals.
Claim 11
Dependent Claim
12 words
The composition according to claim 1, wherein polyorganopolysiloxane (B) is linear polyorganohydrogensiloxane.
Claim 12
Dependent Claim
23 words
The composition according to claim 1, wherein organic radicals attached to a silicon atom in each molecule of polyorganohydrogensiloxane (B) are methyl radicals.
Claim 13
Dependent Claim
34 words
The composition according to claim 1, wherein the amount of polyorganohydrogensiloxane (B) is such that silicon-bonded hydrogen atoms in polyorganohydrogensiloxane (B) are ranging from 0.8 to 1.8 per silicon-bonded vinyl radical in polyorganosiloxane (A).
References Cited (Backward Citations)
US3458469A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-10-05 | 1991-04-06 | 1991-10-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-10-05 | 1995-04-06 | 1995-10-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-10-05 | 1999-04-06 | 1999-10-06 | $7700.00 | Window Closed / Lapsed |