Filter membrane and method of manufacturing it
Assignee: Ceraver SA
•
Filing: 1985-08-05
•
Granted: 1987-10-06
•
Expires: 2005-08-05
Abstract
Abstract A filter membrane for filtering liquid food stuffs or hot gases and including at least one filter layer. The membrane is constituted by a sintered inorganic material comprising grains which are fixedly connected to one another and the average roughness of the surface of said filter layer over a distance along said surface equal to at least five times the average grain size is less than one fifth of the average grain size in the region in question.
Inventors
- 👤 Jacques Gillot
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 22:37
CPC Classifications
B; B01; B01D; B01D67/00; B01D67/0039; B01D67/0046; B01D39/00; B01D39/14; B01D39/20; B01D39/2003; B01D39/2006; B01D39/201; B01D39/2068; B01D39/2072; B01D39/2075; B01D69/00; B01D69/02; B01D69/04; B01D69/12; B01D69/1216; B01D71/00; B01D71/02; B01D71/0215; B01D2323/00; B01D2323/08; B01D2325/00; B01D2325/04
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
177 words
A method of manufacturing a granular filter membrane having an average surface roughness measured over a distance equal to at least five times an average grain size of said membrane that is less than one fifth of said average grain size in the region in question, wherein the method comprises preparing a thin slip comprising a suspension in a liquid vehicle of fine grains of an inorganic material selected from the group consisting of metal oxides, silicon carbide, silicon nitride, silicon and aluminum oxynitrides (SiALON), borides, and glasses, together with a dispersing agent in an amount sufficient to obtain a thoroughly deflocculated suspension of fine grains, and a thickening agent which does not hinder deflocculation; depositing the slip onto a porous support layer having pores of greater size than said filter layer; draining off excess slip so as to leave a thin uniform layer on the support; drying the deposited thin layer; and then baking the support layer with the thin layer it is supporting at a temperature suitable for sintering the grains of the inorganic material.
Claim 2
Independent Claim
177 words
A method of manufacturing a granular filter membrane having an average surface roughness measured over a distance equal to at least five times an average grain size of said membrane that is less than one fifth of said average grain size in the region in question, wherein the method comprises preparing a thin slip comprising a suspension in a liquid vehicle of fine grains of an inorganic material selected from the group consisting of metal oxides, silicon carbide, silicon nitride, silicon and aluminum oxynitrides (SiALON), borides, and glasses, together with a dispersing agent in an amount sufficient to obtain a thoroughly deflocculated suspension of fine grains, and a thickening agent which does not hinder deflocculation; depositing the slip onto a porous support layer having pores of greater size than said filter layer; draining off excess slip so as to leave a thin uniform layer on the support; drying the deposited thin layer; and then baking the support layer with the thin layer it is supporting at a temperature suitable for sintering the grains of the inorganic material.
Claim 3
Dependent Claim
27 words
A method according to claim 1, including an intermediate step of filtering the slip through the support layer after it has been applied thereto, and before drying.
Claim 4
Dependent Claim
21 words
A method according to claim 1, wherein the slip is subjected to prolonged grinding before being applied to the support layer.
Claim 5
Independent Claim
179 words
A method of manufacturing a granular filter membrane having an average surface roughness measured over a distance equal to at least five times an average grain size of said membrane that is less than one fifth of said average grain size in the region in question, wherein the method comprises preparing a thin slip consisting essentially of a suspension in a liquid vehicle of fine grains of an inorganic material selected from the group consisting of metal oxides, silicon carbide, silicon nitride, silicon and aluminum oxynitrides (SiALON), borides, and glasses, together with a dispersing agent in an amount sufficient to obtain a thoroughly deflocculated suspension of fine grains, and a thickening agent which does not hinder deflocculation; depositing the slip onto a porous support layer having pores of greater size than said filter layer; draining off excess slip so as to leave a thin uniform layer on the support; drying the deposited thin layer; and then baking the support layer with the thin layer it is supporting at a temperature suitable for sintering the grains of the inorganic material.
Claim 6
Independent Claim
179 words
A method of manufacturing a granular filter membrane having an average surface roughness measured over a distance equal to at least five times an average grain size of said membrane that is less than one fifth of said average grain size in the region in question, wherein the method comprises preparing a thin slip consisting essentially of a suspension in a liquid vehicle of fine grains of an inorganic material selected from the group consisting of metal oxides, silicon carbide, silicon nitride, silicon and aluminum oxynitrides (SiALON), borides, and glasses, together with a dispersing agent in an amount sufficient to obtain a thoroughly deflocculated suspension of fine grains, and a thickening agent which does not hinder deflocculation; depositing the slip onto a porous support layer having pores of greater size than said filter layer; draining off excess slip so as to leave a thin uniform layer on the support; drying the deposited thin layer; and then baking the support layer with the thin layer it is supporting at a temperature suitable for sintering the grains of the inorganic material.
Claim 7
Dependent Claim
209 words
A filter membrane including at least one filter layer having an exposed surface and being composed of a sintered inorganic material in the form of grains which are fixedly connected to one another, said inorganic material being selected from the group consisting of metal oxides, silicon carbide, silicon nitride, silicon and aluminum oxynitrides (SiALON), borides, and glasses, wherein the improvement comprises the filter layer having been formed by depositing onto a porous support layer a thin slip consisting essentially of a thoroughly deflocculated suspension of fine grains of said organic material in a liquid vehicle, together with a dispersing agent in an amount sufficient to obtain thorough deflocculation of said grains and a thickening agent which does not hinder deflocculation, the porous support layer having pores of greater size than said filter layer, draining off excess slip so as to leave a thin uniform layer on the support, and baking the filter membrane at a temperature sufficient to sinter the grains of the inorganic material, such that the average roughness of the surface of said sintered filter layer over a distance along said surface equal to at least five times the average grain size is less than one fifth of the average grain size in the region in question.
Claim 8
Dependent Claim
209 words
A filter membrane including at least one filter layer having an exposed surface and being composed of a sintered inorganic material in the form of grains which are fixedly connected to one another, said inorganic material being selected from the group consisting of metal oxides, silicon carbide, silicon nitride, silicon and aluminum oxynitrides (SiALON), borides, and glasses, wherein the improvement comprises the filter layer having been formed by depositing onto a porous support layer a thin slip consisting essentially of a thoroughly deflocculated suspension of fine grains of said organic material in a liquid vehicle, together with a dispersing agent in an amount sufficient to obtain thorough deflocculation of said grains and a thickening agent which does not hinder deflocculation, the porous support layer having pores of greater size than said filter layer, draining off excess slip so as to leave a thin uniform layer on the support, and baking the filter membrane at a temperature sufficient to sinter the grains of the inorganic material, such that the average roughness of the surface of said sintered filter layer over a distance along said surface equal to at least five times the average grain size is less than one fifth of the average grain size in the region in question.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-10-05 | 1991-04-06 | 1991-10-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-10-05 | 1995-04-06 | 1995-10-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-10-05 | 1999-04-06 | 1999-10-06 | $7700.00 | Window Closed / Lapsed |