Method for joining ceramic parts to metallic parts
Assignee: Toyota Central R&D Labs Inc
•
Filing: 1987-01-09
•
Granted: 1987-10-06
•
Expires: 2007-01-09
Abstract
Abstract A method for joining a ceramic material to a metallic material includes: forming a metallic film on the surface of the joining area of the ceramic material; irradiating the metallic film with high energy ions to allow the metallic film to stick firm to the surface of the ceramic material and to strengthen the surface of the ceramic material; and mechanically joining the ceramic material to the counterpart metallic material through the metallic film. The ceramic material subjected to these steps hardly breaks at the joining area where breaking otherwise occurs easily, thus enabling high-strength joining of ceramic and metallic materials.
Inventors
- 👤 Osami Kamigaito
- 👤 Haruo Doi
- 👤 Shoji Noda
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 01:06
CPC Classifications
F; F16; F16D; F16D1/00; F16D1/06; F16D1/08; C; C04; C04B; C04B37/00; C04B37/02; C04B37/023; C04B37/026; F01; F01D; F01D5/00; F01D5/02; F01D5/026; F16B; F16B4/00; F16B4/006; C04B2235/00; C04B2235/65; C04B2235/66; C04B2235/667; C04B2237/00; C04B2237/02; C04B2237/12; C04B2237/122; C04B2237/123; C04B2237/124; C04B2237/30; C04B2237/32; C04B2237/34; C04B2237/343; C04B2237/345; C04B2237/348; C04B2237/36; C04B2237/365; C04B2237/368; C04B2237/50; C04B2237/70; C04B2237/708; C04B2237/72; C04B2237/84; F16B2200/00; F16B2200/85; Y; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49316; Y10T29/4932; Y10T29/49826; Y10T29/49863; Y10T29/49865; Y10T29/49885; Y10T29/49945; Y10T403/00; Y10T403/48
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
210 words
A method for producing a jointed article composed of a ceramic article and a metallic article, said ceramic article being selected from the group consisting of aluminum oxide (Al 2 O 3 ), zirconium oxide (ZrO 2 ), silicon nitride (Si 3 N 4 ), and silicon carbide (SiC), which comprises the steps of: forming a metallic film on the surface of said ceramic article over a joining part and a part adjacent to the joining part where tensile stresses are formed as the result of the subsequent joining step, said metallic film being formed of at least one metal selected from the group consisting of Ti, Zr, Hf, V, Nb, Cr, Ni and Co, and having a thickness of 0.1 to 0.5 μm; irradiating the surface of said metallic film with high-energy ions causing mixture of atoms between said metallic film and said ceramic article so as to fast adhere said metallic film and said ceramic article; and joining said ceramic article to said metallic article through said metallic film held between said ceramic article and said metallic article so as to produce said jointed article composed of both articles fixedly fitted under pressure, thereby preventing the breakage of said ceramic surface near the end of said metallic article.
Claim 2
Independent Claim
210 words
A method for producing a jointed article composed of a ceramic article and a metallic article, said ceramic article being selected from the group consisting of aluminum oxide (Al 2 O 3 ), zirconium oxide (ZrO 2 ), silicon nitride (Si 3 N 4 ), and silicon carbide (SiC), which comprises the steps of: forming a metallic film on the surface of said ceramic article over a joining part and a part adjacent to the joining part where tensile stresses are formed as the result of the subsequent joining step, said metallic film being formed of at least one metal selected from the group consisting of Ti, Zr, Hf, V, Nb, Cr, Ni and Co, and having a thickness of 0.1 to 0.5 μm; irradiating the surface of said metallic film with high-energy ions causing mixture of atoms between said metallic film and said ceramic article so as to fast adhere said metallic film and said ceramic article; and joining said ceramic article to said metallic article through said metallic film held between said ceramic article and said metallic article so as to produce said jointed article composed of both articles fixedly fitted under pressure, thereby preventing the breakage of said ceramic surface near the end of said metallic article.
Claim 3
Dependent Claim
18 words
A method according to claim 1, wherein said ions are selected from N, Ar, Ne, and Xe ions.
Claim 4
Dependent Claim
33 words
A method according to claim 2, wherein said irradiating is carried out with the distance of ion penetration into said metallic film being 1 to 1.1 times the thickness of said metallic film.
Claim 5
Dependent Claim
25 words
A method according to claim 3, wherein the dosage of said ions is in the range of 1×10 13 to 1×10 18 ions/cm 2 .
Claim 6
Dependent Claim
17 words
A method according to claim 4, wherein said joining under pressure is carried out by shrinkage fit.
Claim 7
Dependent Claim
20 words
A method according to claim 4, wherein said joining under pressure is carried out by fastening with bolts or nuts.
Claim 8
Dependent Claim
20 words
A method according to claim 1, wherein said metallic film is formed by physical vapor deposition or chemical vapor deposition.
Claim 9
Dependent Claim
23 words
A method according to claim 7, wherein said ceramic article is a turbine shaft in a super charger for an internal combustion engine.
Claim 10
Dependent Claim
23 words
A method according to claim 3, further comprising, after the step of said irradiating, subjecting the surface of said metallic film to plating.
Claim 11
Dependent Claim
20 words
A method according to claim 9, wherein said plating forms at least one metallic film selected from Cu and Ni.
Claim 12
Dependent Claim
55 words
A method according to claim 10, wherein said ceramic article is selected from aluminum oxide (Al 2 O 3 ), zirconium oxide (ZrO 2 ), silicon nitride (Si 3 N 4 ), and silicon carbide (SiC), and the dosage of said ions is in the range of 1×10 13 to 1×10 18 ions/cm 2 .
Claim 13
Dependent Claim
20 words
A method according to claim 11, wherein said metallic film is formed by physical vapor deposition or chemical vapor deposition.
Claim 14
Dependent Claim
23 words
A method according to claim 12, wherein said ceramic article is a turbine shaft in a super charger for an internal combustion engine.
References Cited (Backward Citations)
US1191547A
Cited
US2274961A
Cited
US3099083A
Cited
US3317988A
Cited
US3371413A
Cited
US4167351A
Cited
DE2734747A1
Cited
US4402994A
Cited
US4518315A
Cited
US4532149A
Cited
US4480010A
Cited
US4526624A
Cited
US4566925A
Cited
US4468309A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-10-05 | 1991-04-06 | 1991-10-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-10-05 | 1995-04-06 | 1995-10-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-10-05 | 1999-04-06 | 1999-10-06 | $7700.00 | Window Closed / Lapsed |