US4695294A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Vibratory grinding of silicon carbide
Assignee: Stemcor Corp
•
Filing: 1985-04-11
•
Granted: 1987-09-22
•
Expires: 2005-04-11
Abstract
Abstract A method for reducing the particle size of an initial silicon carbide powder to a milled powder having an average particle size of below 1 micron but greater than an average of about 0.2 micron, without grinding media contamination. The method comprises milling the larger particles in a vibratory mill in the presence of sintered silicon carbide media comprising silicon carbide pellets having both curved and flat surfaces and a maximum dimension of from about 0.5 to 5 centimeters. The grinding occurs in the presence of a fluid, preferably a liquid, for a sufficient time and at a sufficient vibrational energy to obtain said milled powder having such smaller average particle size. At least 90% of the pellets in the silicon carbide media have a specific gravity (density) greater than 3.05 g/cm 3 . The invention includes the unique media, which may be used for various grinding operations, and includes unique milled powders. One of the unique powders has particles which have an average length to width ratio of greater than 2.5. Another of the unique powders is black silicon carbide containing from 200 to 2,000 parts per million of aluminum in solid solution.
Inventors
- 👤 Tadeusz M. Korzekwa
- 👤 Carl H. McMurtry
- 👤 Wolfgang D. G. Boecker
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 10:56
CPC Classifications
B; B02; B02C; B02C17/00; B02C17/14; B02C17/18; B02C17/20
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
57 words
A grinding mixture comprising silicon carbide pellets and a suspension of silicon carbide powder, having a particle size of less than 150 microns, in a fluid, said silicon carbide pellets having a maximum dimension of from about 0.5 to 5 centimeters, at least 90 percent of the pellets having a density greater than 3.05 g/cm 3 .
Claim 2
Dependent Claim
57 words
A grinding mixture comprising silicon carbide pellets and a suspension of silicon carbide powder, having a particle size of less than 150 microns, in a fluid, said silicon carbide pellets having a maximum dimension of from about 0.5 to 5 centimeters, at least 90 percent of the pellets having a density greater than 3.05 g/cm 3 .
Claim 3
Dependent Claim
14 words
The mixture of claim 1 wherein the pellets have both flat and curved surfaces.
Claim 4
Dependent Claim
47 words
The mixture of claim 2 wherein the pellets have a cylindrical shape and the diameter of the cylinder is from 0.3 to 3 times the length of the cylinder and the density of at least 90 percent of the pellets is greater than 3.10 g/cm 3 .
Claim 5
Dependent Claim
31 words
The mixture of claim 3 wherein the diameter of the cylinder is between 0.8 and 1.5 centimeters and the diameter is from 0.75 to 1.25 times the length of the cylinder.
Claim 6
Independent Claim
110 words
A method for reducing the particle size of silicon carbide powder to an average particle size of from about 0.2 to less than 1 micron, said method comprising milling the powder while suspended in a fluid in a vibratory mill in the presence of silicon carbide pellets grinding media for a sufficient time and at a sufficient vibrational energy to obtain milled silicon carbide powder having an average particle size of from about 0.2 to less than 1 micron; said silicon carbide pellets having a maximum dimension of from about 0.5 to 5 centimeters, at least 90 percent of the pellets having a density greater than 3.05 g/cm 3 .
Claim 7
Independent Claim
110 words
A method for reducing the particle size of silicon carbide powder to an average particle size of from about 0.2 to less than 1 micron, said method comprising milling the powder while suspended in a fluid in a vibratory mill in the presence of silicon carbide pellets grinding media for a sufficient time and at a sufficient vibrational energy to obtain milled silicon carbide powder having an average particle size of from about 0.2 to less than 1 micron; said silicon carbide pellets having a maximum dimension of from about 0.5 to 5 centimeters, at least 90 percent of the pellets having a density greater than 3.05 g/cm 3 .
Claim 8
Dependent Claim
19 words
The method of claim 5 wherein the fluid is water and the pellets have both flat and curved surfaces.
Claim 9
Dependent Claim
44 words
The method of claim 6 wherein the pellets have a cylindrical shape and the diameter is from 0.3 to 3 times the length of the cylinder and the density of at least 90 percent of the pellets is greater than 3.10 g/cm 3 .
Claim 10
Dependent Claim
21 words
The method of claim 6 wherein the vibratory mill is vibrated at from about 750 to about 1,800 cycles per minute.
Claim 11
Dependent Claim
21 words
The method of claim 6 wherein the vibratory mill is vibrated at from about 1,000 to about 1,300 cycles per minute.
Claim 12
Dependent Claim
34 words
The method of claim 6 wherein the initial powder has an average particle size of from about 15 to about 40 microns and the milling time is from about 15 to about 50 hours.
Claim 13
Dependent Claim
31 words
The method of claim 6 wherein the initial powder has an average particle size of less than 15 microns and the milling time is from about 2 to about 20 hours.
Claim 14
Dependent Claim
21 words
The method of claim 6 wherein finished milled powder contains less than 5% by weight silicon carbide resulting from media wear.
Claim 15
Dependent Claim
32 words
The method of claim 6 wherein the media wears at a rate of less than 0.5 percent per 24 hours of operation in the absence of feed powder in a ball mill.
Claim 16
Dependent Claim
33 words
The mixture of claim 3 wherein the pellets wear at a rate of less than 0.5 percent per 24 hours of operation in the absence of silicon carbide powder in a ball mill.
Claim 17
Dependent Claim
29 words
The method of claim 6 wherein the fluid is water forming a slurry of silicon carbide and the slurry is circulated through a heat exchanger to reduce its temperature.
Claim 18
Dependent Claim
63 words
A silicon carbide milled powder wherein the average particle size is less than 1 micron, less than 7 numerical percent of the powder particles having a particle size smaller than 0.04 microns and greater than 95 numerical percent of the particles have a particle size less than 6 microns, said silicon carbide containing between 200 and 2,000 ppm of aluminum in solid solution.
Claim 19
Dependent Claim
63 words
A silicon carbide milled powder wherein the average particle size is less than 1 micron, less than 7 numerical percent of the powder particles having a particle size smaller than 0.04 microns and greater than 95 numerical percent of the particles have a particle size less than 6 microns, said silicon carbide containing between 200 and 2,000 ppm of aluminum in solid solution.
Claim 20
Dependent Claim
21 words
The silicon carbide milled powder of claim 16 wherein the silicon carbide comprises at least 50 weight percent alpha silicon carbide.
Claim 21
Dependent Claim
42 words
The silicon carbide milled powder of claim 16 wherein greater than 97 numerical percent of the particles have a particle size less than 6 microns and greater than 84 numerical percent of the particles have a particle size less than 3.5 microns.
Claim 22
Dependent Claim
19 words
The powder of claim 16 wherein the silicon carbide contains between 400 and 1500 ppm aluminum in solid solution.
Claim 23
Dependent Claim
20 words
The powder of claim 16 wherein the powder particles have an average length to width ratio of greater than 2.5.
References Cited (Backward Citations)
US3100088A
Cited
US3268177A
Cited
US3615301A
Cited
US3954483A
Cited
US3966855A
Cited
DE2737521A1
Cited
US4117096A
Cited
US4123286A
Cited
US4275026A
Cited
US4544376A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-09-21 | 1991-03-23 | 1991-09-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-09-21 | 1995-03-23 | 1995-09-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-09-21 | 1999-03-23 | 1999-09-22 | $7700.00 | Window Closed / Lapsed |