US3966855A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of fabricating silicon carbide articles
Assignee: United States Department of the Air Force
•
Filing: 1974-02-22
•
Granted: 1976-06-29
•
Expires: 1994-02-22
Abstract
Abstract A method is provided for fabricating silicon carbide articles which comprises hot pressing a homogeneous mixture of carbonaceous particles and silicon carbide powder. The presence of the carbon limits grain growth so that a silicon carbide product having greatly improved physical properties is obtained. The method is suitable for fabricating structural elements, e.g., structural components in the hot sections of air breathing propulsion systems.
Inventors
- 👤 Glenn W. Hollenberg
- 👤 Robert L. Crane
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 00:14
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/515; C04B35/56; C04B35/565; C04B35/575
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
113 words
A method of fabricating an article of α silicon carbide which comprises compressing a homogeneous mixture consisting essentially of α silicon carbide powder and about 0.75 to 20 weight percent of finely divided carbon particles, based upon the weight of silicon carbide, at an elevated temperature in the range of about 1950° to 2250°C, a pressure ranging from about 4000 to 6000 psi and under a vacuum or in an inert atmosphere in a compression zone formed of graphite and lined with a sheet of graphite; and continuing the compression step until there is otained an article of α silicon carbide having a density substantially equal to the theoretical density of silicon carbide.
Claim 2
Independent Claim
113 words
A method of fabricating an article of α silicon carbide which comprises compressing a homogeneous mixture consisting essentially of α silicon carbide powder and about 0.75 to 20 weight percent of finely divided carbon particles, based upon the weight of silicon carbide, at an elevated temperature in the range of about 1950° to 2250°C, a pressure ranging from about 4000 to 6000 psi and under a vacuum or in an inert atmosphere in a compression zone formed of graphite and lined with a sheet of graphite; and continuing the compression step until there is otained an article of α silicon carbide having a density substantially equal to the theoretical density of silicon carbide.
Claim 3
Dependent Claim
61 words
The method according to claim 1 in which the mixture consists essentially of α silicon carbide powder, about 0.75 to 20 weight percent of finely divided carbon powder and about 1 to 5 weight percent of densification agent selected from the group consisting of aluminum, alumina and boron, both weight percentages being based upon the weight of the silicon carbide powder.
Claim 4
Dependent Claim
43 words
The method according to claim 2 in which the mixture is compressed at a temperature in the range of about 1950° to 2250°C and at a pressure ranging from about 4000 to 6000 psi for a period of about 10 to 20 minutes.
Claim 5
Dependent Claim
23 words
The method according to claim 5 in which the mixture is compressed under a vacuum of about 10.sup. -5 to 10.sup. -3 torr.
Claim 6
Dependent Claim
108 words
The method according to claim 2 in which the mixture is initially compressed at a tempeature ranging from about 700° to 1200°C and at a pressure ranging from about 400 to 600 psi for a period of about 15 minutes to 1 hour; the resulting compacted article is compressed at a temperature in the range of about 1950° to 2250°C and at a pressure ranging from about 4000 to 6000 psi for a period of about 10 to 20 minutes; the compression zone is cooled to room temperature over a period of about 1 to 4 hours; and the silicon carbide article is recovered from the compression zone.
Claim 7
Dependent Claim
23 words
The method according to claim 5 in which the mixture is compressed under a vacuum of about 10.sup. -5 to 10.sup. -3 torr.
Claim 8
Dependent Claim
39 words
The method according to claim 5 in which the mixture consists essentially of silicon carbide powder; finely divided carbon particles selected from the group consisting of chopped carbon fibers, chopped graphite fibers, carbon black and graphite powder; and boron.
Claim 9
Dependent Claim
39 words
In a method of fabricating an article from silicon carbide powder by hot pressing, the improvement which comprises adding particulate carbon to the silicon carbide powder prior to hot pressing so as to inhibit grain growth during hot pressing.
Claim 10
Dependent Claim
39 words
In a method of fabricating an article from silicon carbide powder by hot pressing, the improvement which comprises adding particulate carbon to the silicon carbide powder prior to hot pressing so as to inhibit grain growth during hot pressing.
Claim 11
Dependent Claim
83 words
The method according to claim 8 in which 5 to 15 weight percent particulate carbon, based upon the weight of silicon carbide powder, is added; the particulate carbon and silicon carbide powder are blended; the resulting blend is ball milled in a medium selected from the group consisting of an alcohol, a ketone and a hydrocarbon; and the milled material is dried so as to remove the medium and thereby provide a homogeneous mixture consisting essentially of silicon carbide powder and particulate carbon.
Claim 12
Independent Claim
278 words
A method of fabricating an article of silicon carbide which comprises the following steps: a. blending α silicon carbide powder with about 0.75 to 20 weight percent of finely divided carbon particles, based upon the weight of the silicon carbide, so as to form a homogeneous mixture consisting essentially of the aforementioned ingredients; b. milling the homogeneous mixture of step (a) in a liquid mixing medium which is inert to the ingredients of the mixture until the ingredients are completely dispersed; c. drying the mixture of step (b) so as to evaporate the mixing medium; d. initially compressing the dried mixture of step (c) in a compression zone formed of graphite and lined with a sheet of graphite at a temperature in the range of about 700° to 1200°C and at a pressure ranging from about 400 to 600 psi, the compressing being carried out under a vacuum of about 10.sup. -5 to 10.sup. -3 torr or under a blanket of an inert gas for a period of about 15 minutes to 1 hour; e. compressing the resulting compacted article in the compression zone at a temperature in the range of about 1950° to 2250°C and at a pressure ranging from about 4000 to 6000 psi for a period of about 10 to 20 minutes, the compressing being carried out under a vacuum of about 10.sup. -5 to 10.sup. -3 torr or under a blanket of an inert gas for a period of about 10 to 20 minutes; f. allowing the compression zone to cool to room temperature over a period of about 1 to 4 hours; and g. recovering the silicon carbide article from the compression zone.
Claim 13
Independent Claim
278 words
A method of fabricating an article of silicon carbide which comprises the following steps: a. blending α silicon carbide powder with about 0.75 to 20 weight percent of finely divided carbon particles, based upon the weight of the silicon carbide, so as to form a homogeneous mixture consisting essentially of the aforementioned ingredients; b. milling the homogeneous mixture of step (a) in a liquid mixing medium which is inert to the ingredients of the mixture until the ingredients are completely dispersed; c. drying the mixture of step (b) so as to evaporate the mixing medium; d. initially compressing the dried mixture of step (c) in a compression zone formed of graphite and lined with a sheet of graphite at a temperature in the range of about 700° to 1200°C and at a pressure ranging from about 400 to 600 psi, the compressing being carried out under a vacuum of about 10.sup. -5 to 10.sup. -3 torr or under a blanket of an inert gas for a period of about 15 minutes to 1 hour; e. compressing the resulting compacted article in the compression zone at a temperature in the range of about 1950° to 2250°C and at a pressure ranging from about 4000 to 6000 psi for a period of about 10 to 20 minutes, the compressing being carried out under a vacuum of about 10.sup. -5 to 10.sup. -3 torr or under a blanket of an inert gas for a period of about 10 to 20 minutes; f. allowing the compression zone to cool to room temperature over a period of about 1 to 4 hours; and g. recovering the silicon carbide article from the compression zone.
Claim 14
Dependent Claim
76 words
The method according to claim 10 in which the α silicon carbide in step (a) is blended with about 0.75 to 20 weight percent of finely divided carbon particles and about 1 to 5 weight percent of a densification agent selected from the group consisting of aluminum, alumina and boron, both weight percentages being based upon the weight of the silicon carbide powder, so as to form a homogeneous mixture consisting essentially of the aforementioned ingredients.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-06-29 | 1979-12-29 | 1980-06-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-06-29 | 1983-12-29 | 1984-06-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-06-29 | 1987-12-29 | 1988-06-29 | $7700.00 | Window Closed / Lapsed |