Process for preparing large-sized polymer particles
Assignee: JSR Corp
•
Filing: 1986-01-27
•
Granted: 1987-09-15
•
Expires: 2006-01-27
Abstract
Abstract A process for preparing large-sized polymer particles having a particle diameter in a range of 0.1 to 500 μm by seeded polymerization is described, comprising: finely dispersing a polymerizable monomer in an aqueous medium to prepare a monomer dispersion in which a number average particle diameter of the resulting monomer droplets is not larger than that of seed particles, and a number average particle diameter in a semi-stable condition (Dm) of the monomer droplets satisfies, with a desired number average particle diameter of the final polymer particle as D, the following relation: 0.5×D<Dm<3.5×D combining said monomer dispersion with a dispersion of seed particles to make the polymerizable monomer absorbed or adsorbed on the seed particles; and polymerizing the polymerizable monomer in the presence of a polymerization initiator.
Inventors
- 👤 Kiyoshi Kasai
- 👤 Masayuki Hattori
- 👤 Osamu Kikuchi
- 👤 Hiromi Takeuchi
- 👤 Haruhiro Hirai
- 👤 Nobuo Sakurai
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 19:04
CPC Classifications
C; C08; C08F; C08F257/00; C08F257/02; C08F291/00
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
160 words
A process for preparing large-sized polymer particles having a particular diameter in the range of 0.1 to 500 μm by seed polymerization, comprising: (a) preparing a dispersion of finely dispersed polymerizable monomer by dispersing a monomer in an aqueous medium so that the number average particle diameter of the resulting monomer droplets is not larger than 0.8 μm and not larger than the number average particle diameter of seed particles in a dispersion of seed particles and so that the relationship of the number average particle diameter, Dm, of said monomer droplets in a semistable condition in the monomer dispersion and the desired number average particle diameter, D, of the final polymer particles produced upon polymerization of the monomer, satisifies the expression: 0.5×D<Dm<3.5×D; (b) combining said monomer dispersion with said dispersion of seed particles in order to absorb or adsorb the polymerizable monomer on the seed particles; and (c) polymerizing the polymerizable monomer in the presence of a polymerization initiator.
Claim 2
Dependent Claim
160 words
A process for preparing large-sized polymer particles having a particular diameter in the range of 0.1 to 500 μm by seed polymerization, comprising: (a) preparing a dispersion of finely dispersed polymerizable monomer by dispersing a monomer in an aqueous medium so that the number average particle diameter of the resulting monomer droplets is not larger than 0.8 μm and not larger than the number average particle diameter of seed particles in a dispersion of seed particles and so that the relationship of the number average particle diameter, Dm, of said monomer droplets in a semistable condition in the monomer dispersion and the desired number average particle diameter, D, of the final polymer particles produced upon polymerization of the monomer, satisifies the expression: 0.5×D<Dm<3.5×D; (b) combining said monomer dispersion with said dispersion of seed particles in order to absorb or adsorb the polymerizable monomer on the seed particles; and (c) polymerizing the polymerizable monomer in the presence of a polymerization initiator.
Claim 3
Dependent Claim
50 words
The process of claim 1, wherein the relationship of the number average particle diameter, Dm, of said monomer droplets in a semistable condition in the monomer dispersion and the desired number average particle diameter, D, of the final polymer particles produced upon polymerization of the monomer, satisifies the expression: 0.6×D<Dm<1.8×D.
Claim 4
Dependent Claim
37 words
The process of claim 1, wherein the monomer dispersion is prepared in such a manner that the maximum particle diameter of said monomer droplets is not larger than the number average particle diameter of seed polymer particles.
Claim 5
Dependent Claim
49 words
The process of claim 1, wherein the number average particle diameter, Dm, of said monomer droplets in semistable condition in the monomer dispersion is controlled by adding to the monomer an oily substance which has a water solubility of not more than 1/100 of that of the polymerizable monomer.
Claim 6
Dependent Claim
44 words
The process of claim 1, wherein the number average particle diameter, Dm, of said monomer droplets in a semistable condition in said monomer dispersion in controlled by adding an organic solvent completely miscible with water or an inorganic metal salt to said monomer dispersion.
Claim 7
Dependent Claim
35 words
The process of claim 1, wherein the polymerization initiator is finely dispersed in an aqueous medium and is combined with the dispersion of see particles in said seed particle dispersion independently from the polymerizable monomer.
Claim 8
Dependent Claim
14 words
The process of claim 1, wherein the polymerization initiator is an oil-soluble polymerization initiator.
Claim 9
Dependent Claim
46 words
The process of claim 1, wherein the polymerizable monomer is a monomer mixture containing 40 to 100 wt.% of a monomer of the formula (I): ##STR2## wherein R 1 is hydrogen or methyl and R 2 is an alkyl group of 6 to 18 carbon atoms.
Claim 10
Dependent Claim
33 words
The process of claim 1, wherein the polymerizable monomer is a monomer mixture containing at least 10 wt.% of a fluorine-containing polymerizable monomer having a fluorine content of not less than 25 wt.%.
Claim 11
Dependent Claim
64 words
The process of claim 1, wherein the desired number average particle diameter, D (μm) of the polymer particles of the product of polymerization is determined by the expression: ##EQU3## wherein Ds is the average particle diameter (μm) of said seed particles, Mm is the amount (g) of the polymerizable monomer employed and Ms is the amount (calculated as solids) (g) of the seed particles.
Claim 12
Dependent Claim
73 words
The process of claim 1, wherein the polymerization is conducted in the presence of a dispersion stabilizer which is a member selected from the group consisting of anionic or nonionic surface active agents, organic or inorganic suspension protective agents, and mixtures thereof with the provision that when a surface active agent is employed in the dispersion stabilizer, the concentration of the same is below the critical micelle concentration of the surface active agent.
Claim 13
Dependent Claim
25 words
The process of claim 1, wherein the polymer particles in the product of polymerization have a particle size ranging from 5 μm to 500 μm.
References Cited (Backward Citations)
US3424706A
Cited
US3642680A
Cited
US4186120A
Cited
US4459378A
Cited
US4247434A
Cited
US4254004A
Cited
US4331788A
Cited
US4530956A
Cited
US4419245A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-09-14 | 1991-03-16 | 1991-09-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-09-14 | 1995-03-16 | 1995-09-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-09-14 | 1999-03-16 | 1999-09-15 | $7700.00 | Window Closed / Lapsed |