US4419245A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Copolymer process and product therefrom consisting of crosslinked seed bead swollen by styrene monomer
Assignee: Rohm and Haas Co
•
Filing: 1982-06-30
•
Granted: 1983-12-06
•
Expires: 2002-06-30
Abstract
Abstract A process for the manufacture of crosslinked ion exchange copolymer particles wherein small seed particles are swollen to final size by concurrently feeding monomer and polymerizing the same under controlled suspension conditions and the unique ion exchange particles produced thereby.
Inventors
- 👤 James H. Barrett
- 👤 Thomas J. Howell
- 👤 George M. Lein, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 17:28
CPC Classifications
C; C08; C08F; C08F291/00; B; B01; B01J; B01J20/00; B01J20/22; B01J20/26; B01J39/00; B01J39/08; B01J39/16; B01J39/18; B01J39/20; C08F257/00; C08F257/02; C08F271/00; C08F271/02; C08L; C08L51/00; C08L51/003
Claims Analysis
Total Claims: 26
Claim 1
Independent Claim
198 words
A seed process for manufacturing crosslinked ion exchange copolymer particles capable of withstanding swelling pressures without fracturing upon subsequent functionalization which comprises: (a) forming an agitated aqueous suspension of polymerized lightly crosslinked styrenic or ethylenic seed particles in the absence of an amount of polymeric protective colloids which would prevent imbibition of monomers into the seed particles; (b) feeding to said suspended seed particles under polymerization conditions from 2:20 parts by weight of the seed of a monomer or monomer mixture comprising (I) 0 to 98% by weight of said monomer or monomer mixture of at least one monoethylenically unsaturated styrenic or ethylenic monomer and (II) 2-100% by weight of said monomer or monomer mixture of at least one polyethylenically unsaturated styrenic or ethylenic crosslinking monomer, while balancing the suspension conditions, the feed rate, the agitation and the polymerization rate to avoid particle agglomeration and ultimately produce said ion exchange copolymer particles, until the seed particles have swollen to the desired size by imbibition of the monomer or monomer mixture; (c) continuing polymerization of the swollen seed particles until said ion exchange copolymer particles result; and (d) separating said ion exchange copolymer particles from the aqueous suspension medium.
Claim 2
Dependent Claim
198 words
A seed process for manufacturing crosslinked ion exchange copolymer particles capable of withstanding swelling pressures without fracturing upon subsequent functionalization which comprises: (a) forming an agitated aqueous suspension of polymerized lightly crosslinked styrenic or ethylenic seed particles in the absence of an amount of polymeric protective colloids which would prevent imbibition of monomers into the seed particles; (b) feeding to said suspended seed particles under polymerization conditions from 2:20 parts by weight of the seed of a monomer or monomer mixture comprising (I) 0 to 98% by weight of said monomer or monomer mixture of at least one monoethylenically unsaturated styrenic or ethylenic monomer and (II) 2-100% by weight of said monomer or monomer mixture of at least one polyethylenically unsaturated styrenic or ethylenic crosslinking monomer, while balancing the suspension conditions, the feed rate, the agitation and the polymerization rate to avoid particle agglomeration and ultimately produce said ion exchange copolymer particles, until the seed particles have swollen to the desired size by imbibition of the monomer or monomer mixture; (c) continuing polymerization of the swollen seed particles until said ion exchange copolymer particles result; and (d) separating said ion exchange copolymer particles from the aqueous suspension medium.
Claim 3
Dependent Claim
43 words
The process of claim 1 wherein the seed particles and monomers are styrenic, said styrenic monomers consisting essentially of one or more of the class including styrene, ethylvinylbenzene, vinyltoluene, methylstyrene, vinylbenzyl chloride, halogenated styrenes, and heterocyclic aromatics such as vinylpyridine and alkyl-substituted vinylpyridines.
Claim 4
Dependent Claim
13 words
The process of claim 1 wherein the seed particles and monomers are ethylenic.
Claim 5
Dependent Claim
35 words
The process of claim 1 wherein the seed particles are crosslinked polystyrene and the monomers in the feed are predominantly styrene and divinylbenzene, said monomers in the feed mixture comprising 80%-98% by weight of styrene.
Claim 6
Dependent Claim
21 words
The process of claim 4 wherein the polystyrene seed is lightly crosslinked with between 0.1 and 1.5% by weight of divinylbenzene.
Claim 7
Dependent Claim
26 words
The process of claim 1 wherein the monomers fed to the seed particles comprise between 2 and 10 times the weight of the original seed particles.
Claim 8
Dependent Claim
36 words
The process of claim 1 wherein the monomer feed or the aqueous suspension contains a phase-separating amount of an organic material capable of causing phase separation of the polymerizing monomers to produce a substantially macroreticular copolymer.
Claim 9
Dependent Claim
25 words
The process of claim 1 wherein the monomers are fed to the suspended seed particles over a period of between about 2 and 5 hours.
Claim 10
Dependent Claim
44 words
The process of claim 1 wherein the feed mixture comprises 80-99% by weight of the mixture of at least one monoethylenically unsaturated styrenic or ethylenic monomer and 1-20% by weight of the mixture of at least one polyethylenically unsaturated styrenic or ethylenic crosslinking monomer.
Claim 11
Dependent Claim
11 words
The process of claim 1 wherein the monomer feed is emulsified.
Claim 12
Dependent Claim
17 words
The process of claim 1 wherein the monomer feed comprises styrene and 2-12% by weight of divinylbenzene.
Claim 13
Dependent Claim
118 words
A seed process for manufacturing crosslinked polystyrene particles which comprises (a) forming, in the substantial absence of polymeric protective colloids, an agitated aqueous suspension of crosslinked polystyrene seed particles containing between 0.5% and 1.5% by weight of divinylbenzene crosslinker; (b) feeding to said suspended seed 2:20 parts by weight of the seed, under polymerization conditions, monomers comprising (I) 88%-98% by weight of styrene and (II) 12%-2% by weight of divinylbenzene over a 3-5 hour period until the ratio of the weight of the monomers fed to the original seed is within the range of 3:1 to 6:1; (c) continuing polymerization for 1-3 hours to completely polymerize the monomers; and (d) separating the crosslinked polystyrene particles from the suspension.
Claim 14
Dependent Claim
118 words
A seed process for manufacturing crosslinked polystyrene particles which comprises (a) forming, in the substantial absence of polymeric protective colloids, an agitated aqueous suspension of crosslinked polystyrene seed particles containing between 0.5% and 1.5% by weight of divinylbenzene crosslinker; (b) feeding to said suspended seed 2:20 parts by weight of the seed, under polymerization conditions, monomers comprising (I) 88%-98% by weight of styrene and (II) 12%-2% by weight of divinylbenzene over a 3-5 hour period until the ratio of the weight of the monomers fed to the original seed is within the range of 3:1 to 6:1; (c) continuing polymerization for 1-3 hours to completely polymerize the monomers; and (d) separating the crosslinked polystyrene particles from the suspension.
Claim 15
Dependent Claim
30 words
Crosslinked styrenic or ethylenic ion exchange copolymer beads exhibiting two-stage swelling in a polar solvent and having a Maltese cross birefringence pattern under polarized light characteristic of high bead stress.
Claim 16
Dependent Claim
30 words
Crosslinked styrenic or ethylenic ion exchange copolymer beads exhibiting two-stage swelling in a polar solvent and having a Maltese cross birefringence pattern under polarized light characteristic of high bead stress.
Claim 17
Dependent Claim
25 words
The copolymer beads of claim 13 wherein the polymer is crosslinked polystyrene, the swelling solvent is toluene, and the birefringence pattern is a Maltese cross.
Claim 18
Dependent Claim
9 words
Copolymer beads produced by the process of claim 1.
Claim 19
Dependent Claim
9 words
Copolymer beads produced by the process of claim 12.
Claim 20
Dependent Claim
21 words
Ion exchange resins produced by functionalizing a copolymer produced by the process of claim 1 with an ion exchange functional group.
Claim 21
Dependent Claim
21 words
Ion exchange resins produced by functionalizing a copolymer produced by the process of claim 2 with an ion exchange functional group.
Claim 22
Dependent Claim
21 words
Ion exchange resins produced by functionalizing a copolymer produced by the process of claim 12 with an ion exchange functional group.
Claim 23
Dependent Claim
18 words
Ion exchange resins produced by functionalizing the copolymer beads of claim 13 with an ion exchange functional group.
Claim 24
Dependent Claim
18 words
Ion exchange resins produced by functionalizing the polystyrene beads of claim 14 with an ion exchange functional group.
Claim 25
Dependent Claim
26 words
A method for removing ions from a fluid medium containing the same which comprises contacting said fluid medium with the ion exchange resin of claim 17.
Claim 26
Dependent Claim
32 words
A method for removing ions from a fluid medium containing the same which comprises contacting said fluid medium with an ion exchange resin produced in accordance with the process of claim 4.
References Cited (Backward Citations)
US4224415A
Cited
US4224415B1
Cited
US4085169A
Cited
US4091054A
Cited
US3907730A
Cited
US3959189A
Cited
US4186120A
Cited
US4192921A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-12-05 | 1987-06-06 | 1987-12-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-12-05 | 1991-06-06 | 1991-12-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-12-05 | 1995-06-06 | 1995-12-06 | $7700.00 | Window Closed / Lapsed |