Surface-coated wear-resistant member of cermet and process for producing same
Assignee: Mitsubishi Materials Corp
•
Filing: 1986-09-23
•
Granted: 1987-09-15
•
Expires: 2006-09-23
Abstract
Abstract A surface-coated wear-resistant member of cermet which includes a substrate of cermet and a hard coating vapor-deposited on a surface of the substrate. The coating is composed of at least one titanium compound selected from the group consisting of titanium carbide, titanium nitride, carbonitride of titanium, oxy-carbide of titanium, oxy-nitride of titanium and oxy-carbo-nitride of titanium. An atomic ratio of one of carbon, nitrogen, carbon plus nitrogen, carbon plus oxygen, nitrogen plus oxygen and carbon plus nitrogen plus oxygen to titanium(Ti) in the coating is in the range of between 0.3 and 0.8. The coating contains a compound of TiX and a compound of Ti2X wherein X is one of carbon and nitrogen or at least two of carbon, nitrogen and oxygen. The coating may further includes titanium metal. The coating having an average thickness of 1 to 10 mu m. There is also disclosed a process for producing such a surface-coated wear-resistant member.
Inventors
- 👤 Taijiro Sugisawa
- 👤 Akio Nishiyama
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 02:24
CPC Classifications
C; C23; C23C; C23C30/00; C23C30/005; C23C16/00; C23C16/22; C23C16/30; C23C16/301
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
148 words
A surface-coated wear-resistant member of cermet comprising: (a) a substrate of cermet; and (b) a hard coating vapor-deposited on a surface of said substrate, said coating composed of at least one titanium compound selected from the group consisting of titanium carbide, titanium nitride, carbo-nitride of titanium, oxy-carbide of titanium, oxy-nitride of titanium and oxy-carbo-nitride of titanium, the atomic ratio of one of carbon, nitrogen, carbon plus nitrogen, carbon plus oxygen, nitrogen plus oxygen and carbon plus nitrogen plus oxygen to titanium (Ti) in said titanium compound being in the range of between 0.3 and 0.8, said titanium compound comprising TiX and Ti 2 X wherein X is one of carbon and nitrogen or at least two of carbon, nitrogen and oxygen, said TiX having a cubic structure, said Ti 2 X having a tetragonal structure and said titanium compound having an average thickness of 1 to 10 μm.
Claim 2
Dependent Claim
148 words
A surface-coated wear-resistant member of cermet comprising: (a) a substrate of cermet; and (b) a hard coating vapor-deposited on a surface of said substrate, said coating composed of at least one titanium compound selected from the group consisting of titanium carbide, titanium nitride, carbo-nitride of titanium, oxy-carbide of titanium, oxy-nitride of titanium and oxy-carbo-nitride of titanium, the atomic ratio of one of carbon, nitrogen, carbon plus nitrogen, carbon plus oxygen, nitrogen plus oxygen and carbon plus nitrogen plus oxygen to titanium (Ti) in said titanium compound being in the range of between 0.3 and 0.8, said titanium compound comprising TiX and Ti 2 X wherein X is one of carbon and nitrogen or at least two of carbon, nitrogen and oxygen, said TiX having a cubic structure, said Ti 2 X having a tetragonal structure and said titanium compound having an average thickness of 1 to 10 μm.
Claim 3
Dependent Claim
164 words
A surface-coated wear-resistant member of cermet comprising: (a) a substrate of cermet; and (b) a hard coating vapor-deposited on a surface of the substrate, said coating being composed of titanium metal and at least one titanium compound selected from the group consisting of titanium carbide, titanium nitride, carbonitride of titanium, oxycarbide of titanium, oxy-nitride of titanium and oxy-carbo-nitride of titanium, oxy-nitride of titanium and oxycarbo-nitride of titanium, the atomic ratio of one of carbon, nitrogen, carbon plus nitrogen, carbon plus oxygen, nitrogen plus oxygen nitrogen plus oxygen and carbon plus nitrogen plus oxygen to titanium (Ti) in said titanium compound being in the range of between 0.3 and 0.8, said titanium compound comprising titanium metal, TiX and Ti 2 X wherein X is one of carbon and nitrogen or at least two of carbon, nitrogen and oxygen, said TiX having a cubic structure, said Ti 2 X having a tetragon structure and said titanium compound having an average thickness of 1 to 10 μm.
Claim 4
Dependent Claim
164 words
A surface-coated wear-resistant member of cermet comprising: (a) a substrate of cermet; and (b) a hard coating vapor-deposited on a surface of the substrate, said coating being composed of titanium metal and at least one titanium compound selected from the group consisting of titanium carbide, titanium nitride, carbonitride of titanium, oxycarbide of titanium, oxy-nitride of titanium and oxy-carbo-nitride of titanium, oxy-nitride of titanium and oxycarbo-nitride of titanium, the atomic ratio of one of carbon, nitrogen, carbon plus nitrogen, carbon plus oxygen, nitrogen plus oxygen nitrogen plus oxygen and carbon plus nitrogen plus oxygen to titanium (Ti) in said titanium compound being in the range of between 0.3 and 0.8, said titanium compound comprising titanium metal, TiX and Ti 2 X wherein X is one of carbon and nitrogen or at least two of carbon, nitrogen and oxygen, said TiX having a cubic structure, said Ti 2 X having a tetragon structure and said titanium compound having an average thickness of 1 to 10 μm.
Claim 5
Dependent Claim
28 words
A surface-coated wear-resistant member cermet according to claim 1 or claim 2, in which said coating further comprises a vapor-deposited outermost layer of Al 2 O 3 .
Claim 6
Dependent Claim
162 words
A process for producing a surrface-coated wear-resistant member of cermet, which comprises the steps of: (a) providing a substrate of cermet; and (b) forming a coating on a surface of said substrate, said coating formed by vapor-depositing alternately at least one layer of titanium (Ti) metal and at least one titaniium compound one upon another, said titanium compound being one of titanium carbide, titanium nitride, carbo-nitride of titanium, oxy-carbide of titanium, the atomic ratio of one of carbon, nitrogen, carbon plus nitrogen, carbon plus oxygen, nitrogen plus oxygen and carbon plus nitrogen plus oxygen to titanium (Ti) in said titanium compound being in the range of between 0.3 and 0.8, said titanium compound comprising TiX and Ti 2 X wherein X is one of carbon and nitrogen or at least two of carbon, nitrogen and oxygen, said TiX having a cubic structure, said Ti 2 X having a tetragonal structure, and titanium compound having an average thickness of 1 to 10 μm.
Claim 7
Dependent Claim
162 words
A process for producing a surrface-coated wear-resistant member of cermet, which comprises the steps of: (a) providing a substrate of cermet; and (b) forming a coating on a surface of said substrate, said coating formed by vapor-depositing alternately at least one layer of titanium (Ti) metal and at least one titaniium compound one upon another, said titanium compound being one of titanium carbide, titanium nitride, carbo-nitride of titanium, oxy-carbide of titanium, the atomic ratio of one of carbon, nitrogen, carbon plus nitrogen, carbon plus oxygen, nitrogen plus oxygen and carbon plus nitrogen plus oxygen to titanium (Ti) in said titanium compound being in the range of between 0.3 and 0.8, said titanium compound comprising TiX and Ti 2 X wherein X is one of carbon and nitrogen or at least two of carbon, nitrogen and oxygen, said TiX having a cubic structure, said Ti 2 X having a tetragonal structure, and titanium compound having an average thickness of 1 to 10 μm.
Claim 8
Dependent Claim
171 words
A process for producing a surface-coated wear-resistant member of cermet, which comprises the steps of: (a) providing a substrate of cermet; and (b) forming a coating on a surface of said substrate, said coating formed by vapor-depositing alternately at least one layer of titanium metal and at least one titanium compound one upon another, said titanium compound being one of titanium carbide, titanium nitride, carbo-nitride of titanium, oxy-carbide of titanium, oxy-nitride of titanium and oxy-carbo-nitride of titanium, an atomic ratio of one of carbon, nitrogen, carbon plus nitrogen, carbon plus oxygen, nitrogen plus oxygen and carbon plus nitrogen plus oxygen to titanium (Ti) in said titanium compound being in the range of between 0.3 and 0.8, said titanium compound comprising titanium metal, TiX and Ti 2 X wherein X is one of carbon and nitrogen or at least two of carbon, nitrogen and oxygen, said TiX having a cubic structure, said Ti 2 X having a tetragonal structure, and said titanium compound having an average thickness of 1 to 10 μm.
Claim 9
Dependent Claim
171 words
A process for producing a surface-coated wear-resistant member of cermet, which comprises the steps of: (a) providing a substrate of cermet; and (b) forming a coating on a surface of said substrate, said coating formed by vapor-depositing alternately at least one layer of titanium metal and at least one titanium compound one upon another, said titanium compound being one of titanium carbide, titanium nitride, carbo-nitride of titanium, oxy-carbide of titanium, oxy-nitride of titanium and oxy-carbo-nitride of titanium, an atomic ratio of one of carbon, nitrogen, carbon plus nitrogen, carbon plus oxygen, nitrogen plus oxygen and carbon plus nitrogen plus oxygen to titanium (Ti) in said titanium compound being in the range of between 0.3 and 0.8, said titanium compound comprising titanium metal, TiX and Ti 2 X wherein X is one of carbon and nitrogen or at least two of carbon, nitrogen and oxygen, said TiX having a cubic structure, said Ti 2 X having a tetragonal structure, and said titanium compound having an average thickness of 1 to 10 μm.
Claim 10
Dependent Claim
25 words
A process according to claim 4 or claim 5, in which said coating further comprises a vapor-deposited outermost layer of Al 2 O 3 .
Claim 11
Dependent Claim
29 words
A process according to claim 4 or claim 5, in which the vapor-deposition of each layer is carried out at temperatures of between about 600° C. and 1,000° C.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-09-14 | 1991-03-16 | 1991-09-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-09-14 | 1995-03-16 | 1995-09-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-09-14 | 1999-03-16 | 1999-09-15 | $7700.00 | Window Closed / Lapsed |