Process for the manufacture of molded objects
Assignee: Evonik Operations GmbH
•
Filing: 1985-12-26
•
Granted: 1987-09-08
•
Expires: 2005-12-26
Abstract
Abstract Process for manufacturing of molded objects by hot-pressing lignocellulose-containing materials with polyisocyanates as binders while using an agent to release the molded article from the surface of the metal press used. A mixture of the organosilicon compounds is applied onto the surface of the cauls or molds which faces the material to be pressed, and cured at a temperature from 100° to 200° C., preferably in the presence of known curing catalysts. The mixture of organosilicon compounds comprising (a) 20 to 65 weight percent of a silicone resin of the general formula ##EQU1## in which R 1 is a low molecular weight alkyl radical with 1 to 4 carbon atoms, a has a value of 1 to 1.7, b has a value of 0.3 to 1.0; (b) 30 to 65 weight percent of an α,ω-methylsiloxanediol with an average molecular weight of 1,000 to 20,000; (c) 5 to 15 weight percent of a silicate ester of the general formula ##EQU2## in which R 2 is a low molecular weight hydrocarbon radical with 2 to 4 carbon atoms, c has a value of 2.1 to 4.0; wherein the sum of components (a), (b) and (c) amounts to 100. The release properties can be further improved if more closely defined polysiloxane block copolymers are used as internal release agents.
Inventors
- 👤 Hans-Joachim Kollmeier
- 👤 Helmut Lammerting
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 18:17
CPC Classifications
B; B29; B29C; B29C33/00; B29C33/56; B29C33/60; B29C33/62; B29C33/64; B29K; B29K2503/00
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
207 words
In a process for the manufacture of molded objects wherein lignocellulose-containing materials with polyisocyanates as a binder are subjected to hot pressing in a caul or mold and wherein an agent is applied to the surface of the caul or mold to facilitate release of the molded article from the press, the improvement which comprises using as the release agent a mixture comprising (a) 20 to 65 weight percent of a silicone resin of the general formula ##EQU5## in which R 1 is a low molecular weight alkyl radical with 1 to 4 carbon atoms, a has a value of 1 to 1.7, b has a value of 0.3 to 1.0; (b) 30 to 65 weight percent of an α,ω-methylsiloxanediol with an average molecular weight of 1,000 to 20,000; (c) 5 to 15 weight percent of a silicate ester of the general formula ##EQU6## in which R 2 is a low molecular weight hydrocarbon radical with 2 to 4 carbon atoms, c has a value of 2.1 to 4.0; wherein the sum of components (a), (b), and (c) amounts to 100, and after applying the mixture to the surface of the caul or mold, subjecting the mixture to curing at temperatures from 100° C. to 200° C.
Claim 2
Dependent Claim
207 words
In a process for the manufacture of molded objects wherein lignocellulose-containing materials with polyisocyanates as a binder are subjected to hot pressing in a caul or mold and wherein an agent is applied to the surface of the caul or mold to facilitate release of the molded article from the press, the improvement which comprises using as the release agent a mixture comprising (a) 20 to 65 weight percent of a silicone resin of the general formula ##EQU5## in which R 1 is a low molecular weight alkyl radical with 1 to 4 carbon atoms, a has a value of 1 to 1.7, b has a value of 0.3 to 1.0; (b) 30 to 65 weight percent of an α,ω-methylsiloxanediol with an average molecular weight of 1,000 to 20,000; (c) 5 to 15 weight percent of a silicate ester of the general formula ##EQU6## in which R 2 is a low molecular weight hydrocarbon radical with 2 to 4 carbon atoms, c has a value of 2.1 to 4.0; wherein the sum of components (a), (b), and (c) amounts to 100, and after applying the mixture to the surface of the caul or mold, subjecting the mixture to curing at temperatures from 100° C. to 200° C.
Claim 3
Dependent Claim
18 words
The process of claim 1 wherein the curing is carried out in the presence of a curing catalyst.
Claim 4
Dependent Claim
38 words
The process of claim 1 wherein the lignocellulose-containing material is admixed with an internal release agent prior to pressing, the amount of the internal release agent being from 1 to 5 percent by weight based on the isocyanate.
Claim 5
Dependent Claim
44 words
The process of claim 3, wherein the internal release agent is an organopolysiloxane having the general formula ##STR17## in which R 4 is a methyl radical or the R 3 radical, n=10 to 300, m=1 to 20, and R 3 is a polar radical.
Claim 6
Dependent Claim
96 words
The process of claim 4 wherein R 3 represents the group ##STR18## in which R 5 is a bivalent hydrocarbon radical with 2 to 4 carbon atoms, R 6 is a hydrogen, acyl, carbamate or alkyl radical with 1 to 4 carbon atoms, n=10 to 200, m=1 to 10, and x and y are selected such that the average molecular weight of the polyoxyalkylene block is 200 to 2,000 and this block has up to 50 weight percent of oxyethylene groups, the terminal oxyalkylene group being an oxypropylene group when R 6 is a hydrogen atom.
Claim 7
Dependent Claim
48 words
The process of claim 4 wherein R 3 represents the group ##STR19## in which R 5 is a bivalent hydrocarbon radical with 2 to 4 carbon atoms, R 7 and R 8 are univalent hydrocarbon radicals, alkyloxyalkyl radicals or a common component of a morpholine or piperazine ring.
Claim 8
Dependent Claim
43 words
The process of claim 4 wherein R 3 represents the group ##STR20## in which R 5 is a bivalent hydrocarbon radical with 2 to 4 carbon atoms, R 9 is an alkyl radical with 1 to 4 carbon atoms, and z=1 to 10.
Claim 9
Dependent Claim
27 words
The process of claim 1, 2, or 3 wherein R 1 is selected from the group consisting of ethyl, methyl, propyl, butyl, branched propyl and branched butyl.
Claim 10
Dependent Claim
14 words
The process of claim 1, 2, or 3 wherein a is 1 to 1.5.
Claim 11
Dependent Claim
14 words
The process of claim 1, 2, or 3 wherein b is 0.5 to 0.8.
Claim 12
Dependent Claim
20 words
The process of claim 1, 2, or 3 wherein the molecular weight of component (b) is from 3,000 to 10,000.
Claim 13
Dependent Claim
24 words
The process of claim 1, 2, or 3 wherein R 2 is selected from the group consisting of ethyl, propyl, branched propyl and butyl.
Claim 14
Dependent Claim
11 words
The process of claim 1 wherein the silicate ester is polymeric.
References Cited (Backward Citations)
US3565838A
Cited
US3941856A
Cited
US4033912A
Cited
US4110397A
Cited
GB2081637A
Cited
US4504313A
Cited
US4498929A
Cited
US4546154A
Cited
US4528154A
Cited
US4534928A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-09-07 | 1991-03-09 | 1991-09-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-09-07 | 1995-03-09 | 1995-09-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-09-07 | 1999-03-09 | 1999-09-08 | $7700.00 | Window Closed / Lapsed |