Molding method using fast curing fiber reinforced, low viscosity thermosetting resin
Assignee: Union Carbide Corp
•
Filing: 1984-05-09
•
Granted: 1987-09-08
•
Expires: 2004-05-09
Abstract
Abstract A method of making a resin-impregnated molded fiber reinforced article including use of a thermosetting resin having a specified low viscosity and fast curing time with a specified fiber content for producing an article with improved strength.
Inventors
- 👤 Richard G. Angell, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 15:08
CPC Classifications
B; B29; B29C; B29C41/00; B29C41/02; B29C41/08; B29C43/00; B29C43/02; B29C43/20; B29C43/203; B29C70/00; B29C70/04; B29C70/28; B29C70/30; B29C70/34; B29C70/345; B29C70/40; B29C70/42; B29C70/46; B29C70/48; B29K; B29K2105/00; B29K2105/06; B29K2105/12; B29K2105/128
Claims Analysis
Total Claims: 31
Claim 1
Independent Claim
257 words
A process for rapidly fabricating fiber reinforced thermoset resin articles in which the fiber reinforcement comprises one or more fibers with a melting point or a glass transition temperature above about 130° C., which process comprises the steps of: (a) providing one or more of such fibers in the form of an interlocked mass in a heated matched metal die mold in an amount such that from about 15 to about 80 weight percent of the fabricated fiber reinforced thermoset resin article is comprised of such fibers; (b) providing in an accumulator zone a liquid body of a thermosettable organic material having a viscosity determined at 120° C., in the absence of curing agents therefor, of less than about 50 centipoise, and which is curable within three minutes upon heating to a thermoset resin composition, the viscosity of said liquid body being maintained essentially constant in the accumulator zone by keeping its temperature below that at which curing of said material is substantial; (c) closing the mold containing the interlocked mass of fibers; (d) continously injecting at least a portion of said thermosettable organic material under a substantially constant pressure of from about 2 to about 200 atmospheres from said accumulator zone into the closed mold to thereby fill the cavity in said mold; (e) curing said thermosettable organic material at such a temperature in said mold that said thermosettable organic material cures within about 3 minutes after being injected into the mold; and then (f) opening said mold and removing the cured thermoset molded article therefrom.
Claim 2
Dependent Claim
257 words
A process for rapidly fabricating fiber reinforced thermoset resin articles in which the fiber reinforcement comprises one or more fibers with a melting point or a glass transition temperature above about 130° C., which process comprises the steps of: (a) providing one or more of such fibers in the form of an interlocked mass in a heated matched metal die mold in an amount such that from about 15 to about 80 weight percent of the fabricated fiber reinforced thermoset resin article is comprised of such fibers; (b) providing in an accumulator zone a liquid body of a thermosettable organic material having a viscosity determined at 120° C., in the absence of curing agents therefor, of less than about 50 centipoise, and which is curable within three minutes upon heating to a thermoset resin composition, the viscosity of said liquid body being maintained essentially constant in the accumulator zone by keeping its temperature below that at which curing of said material is substantial; (c) closing the mold containing the interlocked mass of fibers; (d) continously injecting at least a portion of said thermosettable organic material under a substantially constant pressure of from about 2 to about 200 atmospheres from said accumulator zone into the closed mold to thereby fill the cavity in said mold; (e) curing said thermosettable organic material at such a temperature in said mold that said thermosettable organic material cures within about 3 minutes after being injected into the mold; and then (f) opening said mold and removing the cured thermoset molded article therefrom.
Claim 3
Dependent Claim
20 words
The process of claim 1, wherein the fibers have lengths of from about 1 to about 2 or more inches.
Claim 4
Dependent Claim
12 words
The process of claim 1, wherein the fiber is a continuous filament.
Claim 5
Dependent Claim
32 words
The process of claim 1, wherein an amount of fiber is used such that the interlocked mass of fibers comprises from about 35 to about 80 weight percent of the molded article.
Claim 6
Dependent Claim
25 words
The process of claim 1, wherein the thermosettable organic material comprises a backbone component selected from an unsaturated polyester, an epoxy, or a vinyl ester.
Claim 7
Dependent Claim
45 words
The process of claim 1, wherein the thermosettable organic material comprises a curable composition of (a) a half ester of an organic polyol, (b) maleic anhydride, and (c) an ethylenically unsaturated monomer which forms a liquid homogeneous mixture and is copolymerizable with (a) and (b).
Claim 8
Dependent Claim
38 words
The process of claim 1, wherein the thermosettable organic material comprises a curable composition of a poly(acrylate), an ethylenically unsaturated monomer and an elevated temperature free-radical curing catalyst capable of effecting the co-reaction of the poly(acrylate) and monomer.
Claim 9
Dependent Claim
25 words
The process of claim 1, wherein the thermosettable organic material comprises a curable composition of a maleic anhydride capped polyester, and an ethylenically unsaturated monomer.
Claim 10
Dependent Claim
26 words
The process of claim 1, wherein the thermosettable organic material has a viscosity of from about 5 to less than about 200 centipoise at 23° C.
Claim 11
Dependent Claim
27 words
The process of claim 1, wherein the mold temperature exceeds the initiation temperature of the thermosettable organic material by at least about 10 to about 20° C.
Claim 12
Dependent Claim
17 words
The process of claim 1, wherein air is evacuated from the mold cavity prior to step (d).
Claim 13
Dependent Claim
15 words
The process of claim 1, including curing the resin in less than about 2 minutes.
Claim 14
Dependent Claim
20 words
The process of claim 1, wherein after step (e) and prior to step (f), feeding additional material into the mold.
Claim 15
Dependent Claim
24 words
The process of claim 13, wherein the additional material is fed to the mold after enlarging the mold cavity to receive the additional material.
Claim 16
Dependent Claim
37 words
The process of claim 1, in which the pressure employed to inject the material into the mold according to step (d) is greater than the pressure required to fill the cavity of the mold with said material.
Claim 17
Dependent Claim
43 words
The process of claim 1, including maintaining the pressure of injecting the thermosettable material beyond the time required to initially fill the mold cavity and adding additional resin in order to fill the void created by the shrinkage of the initial resin charge.
Claim 18
Dependent Claim
17 words
The process of claim 1, wherein the fiber reinforcement is fiberglass, carbon fibers or aromatic polyamide fibers.
Claim 19
Dependent Claim
16 words
The process of claim 17, wherein the fibers have a length of at least 1/4 inch.
Claim 20
Dependent Claim
46 words
The process of claim 1, wherein a second accumulator zone is provided which contains therein a thermosettable composition different from said thermosettable organic material, and after step (e) and prior to step (f), at least a portion of said different composition is fed to the mold.
Claim 21
Dependent Claim
26 words
The process of claim 19, including filling said composition from the second accumulator zone to the mold after enlarging the mold cavity to receive said composition.
Claim 22
Dependent Claim
18 words
The process of claim 1, including spraying a combination of fiber and binder simultaneously onto the mold surface.
Claim 23
Dependent Claim
14 words
The process of claim 21, including compressing the bonded fiber on the mold surface.
Claim 24
Dependent Claim
17 words
The process of claim 21, wherein the bonded fiber is dried prior to injecting the organic material.
Claim 25
Dependent Claim
16 words
The process of claim 1, including forming the interlocked mass of fibers on the mold surface.
Claim 26
Dependent Claim
28 words
The process of claim 24, including forming regions of different density of the interlocked mass of fibers on the mold surface according to a predetermined pattern and amount.
Claim 27
Dependent Claim
20 words
The process of claim 1, including compressing the interlocked mass of fibers on the mold surface prior to step (c).
Claim 28
Dependent Claim
27 words
The process of claim 1, including forming the interlocked mass of fibers outside the mold and placing the mass of fibers in the mold in step (a).
Claim 29
Dependent Claim
24 words
The process of claims 1, 24, or 27, including bonding the interlocked mass of fibers by a thermoplastic resin, starch or a thermosettable resin.
Claim 30
Dependent Claim
254 words
A process for rapidly fabricating fiber reinforced thermoset resin articles in which the fiber reinforcement comprises one or more fibers with a melting point or a glass transition temperature above about 130° C., which process comprises the steps of: (a) providing one or more of such fibers in the form of an interlocked mass in a heated matched metal die mold in an amount such that from about 15 to about 80 weight percent of the fabricated fiber reinforced thermoset resin article is comprised of such fibers; (b) providing in an accumulator zone a liquid body of a thermosettable organic material having a viscosity determined at 120° C., in the absence of curing agents therefor, of less than about 50 centipoise, and which is curable upon heating to a thermoset resin composition, the viscosity of said liquid body being maintained essentially constant in the accumulator zone by keeping its temperature below that at which curing of said material is substantial; (c) closing the mold containing the interlocked mass of fibers; (d) continuously injecting at least a portion of said thermosettable organic material under a substantially constant pressure of from about 10 to about 200 atmospheres from said accumulator zone into the closed mold to thereby fill the cavity in said mold; (e) curing said thermosettable organic material at such a temperature in said mold that said thermosettable organic material cures within about 3 minutes after being injected into the mold; and then (f) opening said mold and removing the cured thermoset molded article therefrom.
Claim 31
Dependent Claim
254 words
A process for rapidly fabricating fiber reinforced thermoset resin articles in which the fiber reinforcement comprises one or more fibers with a melting point or a glass transition temperature above about 130° C., which process comprises the steps of: (a) providing one or more of such fibers in the form of an interlocked mass in a heated matched metal die mold in an amount such that from about 15 to about 80 weight percent of the fabricated fiber reinforced thermoset resin article is comprised of such fibers; (b) providing in an accumulator zone a liquid body of a thermosettable organic material having a viscosity determined at 120° C., in the absence of curing agents therefor, of less than about 50 centipoise, and which is curable upon heating to a thermoset resin composition, the viscosity of said liquid body being maintained essentially constant in the accumulator zone by keeping its temperature below that at which curing of said material is substantial; (c) closing the mold containing the interlocked mass of fibers; (d) continuously injecting at least a portion of said thermosettable organic material under a substantially constant pressure of from about 10 to about 200 atmospheres from said accumulator zone into the closed mold to thereby fill the cavity in said mold; (e) curing said thermosettable organic material at such a temperature in said mold that said thermosettable organic material cures within about 3 minutes after being injected into the mold; and then (f) opening said mold and removing the cured thermoset molded article therefrom.
References Cited (Backward Citations)
DE1404387A1
Cited
US3137750A
Cited
US3192297A
Cited
US3222421A
Cited
US3442998A
Cited
US3608150A
Cited
DE2121209A1
Cited
DE2135181A1
Cited
US3748075A
Cited
US3899277A
Cited
US3903343A
Cited
US3819312A
Cited
US4011651A
Cited
US3975479A
Cited
US4149838A
Cited
US4104353A
Cited
US4081578A
Cited
US4091061A
Cited
DE2529214A1
Cited
US4219598A
Cited
DE2548751A1
Cited
US4051290A
Cited
US4205031A
Cited
US4121646A
Cited
US4076788A
Cited
US4085810A
Cited
US4123493A
Cited
US4153490A
Cited
US4235833A
Cited
GB2015915A
Cited
US4199388A
Cited
US4207282A
Cited
US4238437A
Cited
US4234633A
Cited
US4245006A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-09-07 | 1991-03-09 | 1991-09-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-09-07 | 1995-03-09 | 1995-09-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-09-07 | 1999-03-09 | 1999-09-08 | $7700.00 | Window Closed / Lapsed |