Process of preparing nonfibrous, piezoelectric polymer sheet of improved activity
Assignee: Arkema Inc
•
Filing: 1985-07-01
•
Granted: 1987-09-08
•
Expires: 2005-07-01
Abstract
Abstract A nonfibrous, unoriented sheet of a copolymer resin of about 65 to 85 mol percent of vinylidene fluoride and from 15 to about 35 mol percent of at least one other copolymerizable substituted monoolefinic monomer, said sheet having improved and uniform piezoelectric properties for hydrophonic use, and the process for preparing said sheet with improved piezoelectric and dielectric breakdown strength properties wherein it is heated for at least about 20 minutes within the temperature range of above the crystalline melting temperature and below a defined temperature, cooled to below the Curie temperature and then electrically poled, are disclosed herein.
Inventors
- 👤 Philip E. Bloomfield
- 👤 Seymour Preis
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 21:02
CPC Classifications
H; H10; H10N; H10N30/00; H10N30/01; H10N30/04; H10N30/045; H10N30/09; H10N30/098; H10N30/80; H10N30/85; H10N30/857
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
127 words
A process for preparing a sheet having improved piezoelectric properties when electrically poled comprising heating a nonfibrous, unoriented copolymer resin sheet of at least about 25 micrometers thick and comprising about 65 to 85 mol % of vinylidene fluoride and from 15 to about 35 mol % of at least one other copolymerizable, substituted, monolefinic monomer having from 2 to 4 carbon atoms in the olefinic chain to a temperature within a range of above the crystalline melting temperature (T m ) and below the dielectric strength degradation temperature (T d ) of said sheet for a time period of at least 20 minutes whereby said sheet has improved dielectric strength and, after poling, has a hydrostatic coefficient (g h ) of magnitude at least 0.100 V·m/N.
Claim 2
Dependent Claim
127 words
A process for preparing a sheet having improved piezoelectric properties when electrically poled comprising heating a nonfibrous, unoriented copolymer resin sheet of at least about 25 micrometers thick and comprising about 65 to 85 mol % of vinylidene fluoride and from 15 to about 35 mol % of at least one other copolymerizable, substituted, monolefinic monomer having from 2 to 4 carbon atoms in the olefinic chain to a temperature within a range of above the crystalline melting temperature (T m ) and below the dielectric strength degradation temperature (T d ) of said sheet for a time period of at least 20 minutes whereby said sheet has improved dielectric strength and, after poling, has a hydrostatic coefficient (g h ) of magnitude at least 0.100 V·m/N.
Claim 3
Dependent Claim
39 words
The process of claim 1 including the step of cooling said sheet to below the Curie temperature (↓T c ) of the resin from which the sheet is formed and while cooling, or after cooling, electrically poling said sheet.
Claim 4
Dependent Claim
31 words
The process of claim 2 wherein the sheet comprises about 70 to 82 mol percent of vinylidene fluoride and about 18 to 30 mol percent of a copolymerizable fluorine substituted ethylene.
Claim 5
Dependent Claim
34 words
The process of claim 2 wherein the sheet is heated to a temperature within the range of 145° to 200° C. for a time period ranging from about 30 minutes to about 2 hours.
Claim 6
Dependent Claim
13 words
The process of claim 4 wherein the copolymerizable fluorine substituted ethylene is trifluoroethylene.
Claim 7
Dependent Claim
13 words
The process of claim 4 wherein the copolymerizable fluorine substituted ethylene is tetrafluoroethylene.
References Cited (Backward Citations)
US3197538A
Cited
US3707592A
Cited
US3991451A
Cited
US3833503A
Cited
US3878274A
Cited
US4127681A
Cited
US4268653A
Cited
US4578442A
Cited
US4349502A
Cited
JPS57123603A
Cited
US4393093A
Cited
US4434114A
Cited
GB2121810A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-09-07 | 1991-03-09 | 1991-09-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-09-07 | 1995-03-09 | 1995-09-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-09-07 | 1999-03-09 | 1999-09-08 | $7700.00 | Window Closed / Lapsed |