Process for preparing alloyed negative electrodes
Assignee: Hydro-Québec
•
Filing: 1985-04-04
•
Granted: 1987-09-01
•
Expires: 2005-04-04
Abstract
Abstract The disclosure describes a method for the preparation of metallic alloys containing an alkali or alkali-earth metal, such as lithium, and a host metal, such as aluminum. Initially, an active organic solution of the alkali or the alkali-earth metal is prepared, and a source of the alkali or alkali-earth metal which are both brought together with one another. On the other hand, a metallic structure containing the host metal is prepared, the metallic structure is brought together with the organic solution which is kept in touch with the source of metal until there is formed an alloy of the host metal and of the alkali or alkali-earth metal with the metallic structure, and the alloy possesses an activity which is determined by that of the organic solution. The organic solution then acts as transfer agent of the alkali or alkali-earth metal towards the host metallic structure. To prepare a negative electrode, the alloy is brought together with an electrolyte, such as a thin polymeric film. The disclosure also describes the electrodes as well as the electrochemical generators produced by using these electrodes. Considerably improved properties of cycling are obtained.
Inventors
- 👤 Michel Gauthier
- 👤 Denis Fauteux
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 04:10
CPC Classifications
H; H01; H01M; H01M4/00; H01M4/02; H01M4/13; H01M4/134; C; C23; C23C; C23C28/00; H01M10/00; H01M10/36; H01M4/36; H01M4/38; H01M4/40; H01M2004/026; H01M2004/027; H01M2300/00; H01M2300/0017; H01M2300/002; H01M2300/0022; H01M2300/0025; H01M2300/0048; H01M2300/0065; H01M2300/0082; H01M4/04; H01M4/049; H01M4/0495; H01M4/405; H01M4/64; H01M4/66; H01M4/661; H01M8/00; H01M8/04; H01M8/04007; H01M8/04067; H01M8/04074; Y; Y02; Y02E; Y02E60/00; Y02E60/10; Y02E60/30; Y02E60/50
Claims Analysis
Total Claims: 75
Claim 1
Independent Claim
150 words
Method for the preparation of metallic alloys containing an alkali or alkali-earth metal as well as a host metal, which comprises preparing an active organic solution of said alkali or alkali-earth metal in metallic form, as well as a source of said alkali or alkali-earth metal which are brought together, separately preparing a metallic structure containing said host metal and keeping said metallic structure separate from said source of alkali or alkali-earth metal, contacting together the metallic structure with the organic solution the latter being kept in contact with the source of metal until formation of a superficial alloy of said host metal and of the alkali or the alkali earth metal with the metallic structure, and the alloy has an activity which is determined by that of the organic solution, said organic solution then serving as transfer agent of the alkali or alkali-earth metal towards the host metallic structure.
Claim 2
Dependent Claim
150 words
Method for the preparation of metallic alloys containing an alkali or alkali-earth metal as well as a host metal, which comprises preparing an active organic solution of said alkali or alkali-earth metal in metallic form, as well as a source of said alkali or alkali-earth metal which are brought together, separately preparing a metallic structure containing said host metal and keeping said metallic structure separate from said source of alkali or alkali-earth metal, contacting together the metallic structure with the organic solution the latter being kept in contact with the source of metal until formation of a superficial alloy of said host metal and of the alkali or the alkali earth metal with the metallic structure, and the alloy has an activity which is determined by that of the organic solution, said organic solution then serving as transfer agent of the alkali or alkali-earth metal towards the host metallic structure.
Claim 3
Dependent Claim
14 words
Method according to claim 1, wherein the preparation is carried out at room temperature.
Claim 4
Dependent Claim
14 words
Method according to claim 1, wherein the alkali or alkali-earth metal comprises lithium Li°.
Claim 5
Dependent Claim
26 words
Method according to claim 1, wherein the organic solution contains metallic lithium, and is in free radical form as a result of containing said metallic lithium.
Claim 6
Dependent Claim
24 words
Method according to claim 1, wherein the host metal is capable of forming alloys, intermetallic compounds, or solid solutions with alkali or alkali-earth metal.
Claim 7
Dependent Claim
87 words
Method according to claim 1, wherein the organic solution comprises a mixture of liquids including at least one polar aprotic solvent which is compatible with the alkali or alkali metal and is capable of solvating ions of said alkali or alkali-earth metal, and conjugated double bond compound which can delocalize the electrons of said alkali or alkali metal and an organic diluent liquid which is compatible with the alkali or alkali-earth metal, said organic solution being capable of controlling the activity of said alkali or alkali-earth metal.
Claim 8
Dependent Claim
27 words
Method according to claim 6, wherein the organic solution is capable of controlling the activity of said alkali or alkali-earth metal at values lower than 600 mVvsLi°.
Claim 9
Dependent Claim
25 words
Method according to claim 6, wherein the polar aprotic solvent is selected from the group consisting of ether based solvents and substituted amino base solvents.
Claim 10
Dependent Claim
22 words
Method according to claim 8, wherein the polar aprotic solvent is selected from the group of THF, dioxolan, glymes and crown ethers.
Claim 11
Dependent Claim
27 words
Method according to claim 8, wherein the polar aprotic solvent is selected from the group consisting of N,N,N',N'-tetramethyl 1,2-ethane diamine, N,N,N',N'-tetramethyl 1,3-propane diamine and N,N,N",N"-pentamethyl diethylene triamine.
Claim 12
Dependent Claim
23 words
Method according to claim 6, wherein the conjugated double bond compound is selected from the group consisting of naphthalene, biphenyl, anthracene and benzophenone.
Claim 13
Dependent Claim
22 words
Method according to claim 6, wherein the organic diluent is selected from the group consisting of benzene, toluene, alkane and mixtures thereof.
Claim 14
Dependent Claim
37 words
Method according to claim 6, wherein the molar ratios of the components of the organic solution are the following: polar aprotic solvent: 10 -5 to <1 conjugated double bond compounds: <10 -5 to 0.2 organic diluent: <1.
Claim 15
Dependent Claim
28 words
Method according to claim 13, wherein the molar ratios are the following: polar aprotic solvent: 10 -3 to 0.2 aromatic compounds: 10 -4 to 0.1 organic diluent: <1.
Claim 16
Dependent Claim
44 words
Method according to claim 13, wherein when the organic solution comprises THF or N,N,N',N'-tetramethyl 1,2-ethane diamine, naphthalene or biphenyl and benzene, the molar ratio is the following: THF or N,N,N',N'-tetramethyl 1,2-ethane diamine: about 9×10 -2 biphenyl or naphthalene: about 7×10 -2 benzene: about 0.84.
Claim 17
Dependent Claim
34 words
Method according to claim 6, wherein the organic solution has a high content of inert diluent but contains little aromatic compounds and polar aportic solvents capable of solvating lithium ions and compatible with lithium.
Claim 18
Dependent Claim
11 words
Method according to claim 16, wherein the inert diluent comprises benzene.
Claim 19
Dependent Claim
13 words
Method according to claim 1, wherein the organic solution contains naphthalene or biphenyl.
Claim 20
Dependent Claim
15 words
Method according to claim 1, wherein the organic solution contains THF and N,N,N',N'-tetramethyl 1,2-ethane diamine.
Claim 21
Dependent Claim
26 words
Method according to claim 1, wherein the host metal is selected from the group consisting of aluminum, magnesium, silicon, zinc, boron, mercury, silver and alloys thereof.
Claim 22
Dependent Claim
11 words
Method according to claim 20, wherein the host metal comprises aluminum.
Claim 23
Dependent Claim
49 words
Method according to claim 1, wherein the organic solution comprises benzene and contains naphthalene or biphenyl, N,N,N',N'-tetramethyl-1,2 ethane diamine or THF, and is saturated with lithium, said solution being in free radical form as a result of containing metallic lithium, said solution containing an excess of said metallic lithium.
Claim 24
Dependent Claim
58 words
Method according to claim 1, wherein the organic solution comprises benzene, and contains naphthalene or biphenyl, N,N,N',N'-tetramethyl-1,2 ethane diamine or THF, and is saturated with lithium, said solution being in free radical form as a result of containing metallic lithium, said solution containing a limited quantity of metallic lithium so as to control the proportion of alloy formed.
Claim 25
Dependent Claim
166 words
Method for the preparation of alloyed metallic electrodes containing an alkali or alkali-earth metal as well as a host metal the whole being in contact with an electrolyte, which comprises preparing an active organic solution of said alkali or alkali-earth metal in metallic form, as well as a source of said alkali or alkali-earth metal which are brought together, separately preparing a metallic structure containing said host metal and keeping said metallic structure separate from said source of alkali or alkali-earth metal, contacting together the metallic structure with the organic solution, the latter being kept in contact with the source of metal until formation of a superficial alloy of said host metal and of the alkali or the alkali-earth metal with the metallic structure, and the alloy has an activity which is determined by that of the organic solution, said organic solution then acts as transfer agent of the alkali or alkali-earth metal towards the host metallic structure, the resulting alloy being contacted with an electrolyte.
Claim 26
Dependent Claim
166 words
Method for the preparation of alloyed metallic electrodes containing an alkali or alkali-earth metal as well as a host metal the whole being in contact with an electrolyte, which comprises preparing an active organic solution of said alkali or alkali-earth metal in metallic form, as well as a source of said alkali or alkali-earth metal which are brought together, separately preparing a metallic structure containing said host metal and keeping said metallic structure separate from said source of alkali or alkali-earth metal, contacting together the metallic structure with the organic solution, the latter being kept in contact with the source of metal until formation of a superficial alloy of said host metal and of the alkali or the alkali-earth metal with the metallic structure, and the alloy has an activity which is determined by that of the organic solution, said organic solution then acts as transfer agent of the alkali or alkali-earth metal towards the host metallic structure, the resulting alloy being contacted with an electrolyte.
Claim 27
Dependent Claim
14 words
Method according to claim 24, wherein the alloy is contacted with a polymeric electrolyte.
Claim 28
Dependent Claim
11 words
Method according to claim 25, wherein the polymeric electrolyte comprises polyethers.
Claim 29
Dependent Claim
36 words
Method according to claim 25, wherein the contact of the alloy and of the polymeric electrolyte is carried out so as to define in said electrode zones where the alloy is not penetrated by the polymer.
Claim 30
Dependent Claim
19 words
Method according to claims 24, 25 or 26, wherein the electrolyte is contacted with the alloy, in molten form.
Claim 31
Dependent Claim
25 words
Method according to claims 25 or 26, wherein the electrolyte is contacted with the alloy in a solution, said solution being compatible with said alloy.
Claim 32
Dependent Claim
48 words
Method according to claim 24, wherein the metallic electrode obtained has a predetermined shape, and that for this purpose, the initial metallic structure is prepared so as to be a precursor of the final shape of said electrode, said shape being adaptable to produce electrodes as thin film.
Claim 33
Dependent Claim
14 words
Method according to claim 24, wherein the alkali or alkali-earth metal comprises lithium Li°.
Claim 34
Dependent Claim
29 words
Method according to claim 31, wherein the organic solution is based on naphthalene in which the activity of the metallic lithium is between about +200 and about +400 mVsLi°.
Claim 35
Dependent Claim
29 words
Method according to claim 31, wherein the organic solution is based on biphenyl in which the activity of the metallic lithium is between about +200 and about +80 mVvsLi°.
Claim 36
Dependent Claim
26 words
Method according to claim 24, wherein the organic solution contains metallic lithium, and is in free radical form as a result of containing said metallic lithium.
Claim 37
Dependent Claim
20 words
Method according to claim 34, wherein the organic solution containing metallic lithium is in contact with the source of lithium.
Claim 38
Dependent Claim
24 words
Method according to claim 24, wherein the host metal is capable of forming alloys, intermetallic compounds or solid solutions with alkali or alkali-earth metals.
Claim 39
Dependent Claim
81 words
Method according to claim 24, wherein the organic solution comprises a mixture of liquids including at least one polar aprotic solvent which is compatible with the alkali or alkali-earth metal and has a solvating effect on the ions of said alkali or alkali-earth metal, and conjugated double bond compound which can delocalize the electrons of said alkali or alkali-earth metal and a compatible liquid organic diluent, said organic solution being capable of controlling the activity of said alkali or alkali-earth metal.
Claim 40
Dependent Claim
27 words
Method according to claim 37, wherein the organic solution is capable of controlling the activity of said alkali or alkali-earth metal to values lower than 600 mVvsLi°.
Claim 41
Dependent Claim
25 words
Method according to claim 37, wherein the polar aprotic solvent is selected in the group consisting of ether base solvents and substituted amine base solvents.
Claim 42
Dependent Claim
23 words
Method according to claim 39, wherein the polar aprotic solvent is selected from the group consisting of THF, dioxolan, glymes and crown ethers.
Claim 43
Dependent Claim
27 words
Method according to claim 39, wherein the polar aprotic solvent is selected from the group consisting of N,N,N',N'-tetramethyl 1,2-ethane diamine, N,N,N',N'-tetramethyl 1,3-propane diamine, and N,N,N",N"-pentamethyl diethylene triamine.
Claim 44
Dependent Claim
21 words
Method according to claim 37, wherein the conjugated double bond compound is selected from the group consisting of naphthalene and biphenyl.
Claim 45
Dependent Claim
23 words
Method according to claim 37, wherein the compatible organic diluent is selected from the group consisting of benzene, toluene, alkane and mixtures thereof.
Claim 46
Dependent Claim
37 words
Method according to claim 37, wherein the molar ratios of the components of the organic solution are the following: polar aprotic solvent: 10 -5 to <1 conjugated double bond compounds: <10 -5 to 0.2 organic diluent: <1.
Claim 47
Dependent Claim
28 words
Method according to claim 44, wherein the molar ratios are the following: polar aprotic solvent: 10 -3 to 0.2 aromatic compounds: 10 -4 to 0.1 organic diluent: <1.
Claim 48
Dependent Claim
44 words
Method according to claim 44, wherein when the organic solution comprises THF or N,N,N',N'-tetramethyl 1,2-ethane diamine, naphthalene or biphenyl and benzene, the molar ratio is the following: THF or N,N,N',N'-tetramethyl 1,2-ethane diamine: about 9×10 -2 biphenyl or naphthalene: about 7×10 -2 benzene: about 0.84.
Claim 49
Dependent Claim
13 words
Method according to claim 24, wherein the organic solution contains napththalene or biphenyl.
Claim 50
Dependent Claim
15 words
Method according to claim 24, wherein the organic solution contains THF and N,N,N',N'-tetramethyl 1,2-1,2-ethane diamine.
Claim 51
Dependent Claim
50 words
Method according to claim 24, wherein the organic solution has a high content of inert diluent and contains little aromatic compounds and polar aprotic solvents which have a solvating effect on the lithium ion and are compatible with lithium, thereby enabling to obtain electrodes which are not very electrochemically passivated.
Claim 52
Dependent Claim
11 words
Method according to claim 49, wherein the inert diluent comprises benzene.
Claim 53
Dependent Claim
26 words
Method according to claim 24, wherein the host metal is selected from the group consisting of aluminum, magnesium, silicon, zinc, boron, mercury, silver and alloys thereof.
Claim 54
Dependent Claim
11 words
Method according to claim 51, wherein the host metal comprises aluminum.
Claim 55
Dependent Claim
21 words
Method according to claim 52, wherein the organic solution comprises lithium and is in contact with a a source of lithium.
Claim 56
Dependent Claim
16 words
Method according to claim 53, wherein after shaping the host structure, the latter undergoes superficial treatment.
Claim 57
Dependent Claim
35 words
Method according to claim 54, wherein the superficial treatments are carried out by forming solid solutions of lithium in aluminum Li.sub.ε Al where ε corresponds to a few percentages of Li with respect to aluminum.
Claim 58
Dependent Claim
24 words
Method according to claim 24, wherein the metallic structure containing said host metal comprises a metallic sheet having a plane layer of host metal.
Claim 59
Dependent Claim
20 words
Method according to claim 56, wherein the metallic sheet is selected from the group consisting of copper, molybdenum and nickel.
Claim 60
Dependent Claim
14 words
Method according to claim 57, wherein the plane layer of host metal comprises aluminum.
Claim 61
Dependent Claim
35 words
Method according to claims 56, 57 or 58, wherein the thickness of the metallic sheet varies between about 1μ and 25μ, while the thickness of the layer of host metal varies between 5μ and 50μ.
Claim 62
Dependent Claim
33 words
Method according to claims 56, 57 or 58, wherein the thickness of the metallic sheet varies between about 1μ and 25μ, while the thickness of the layer of host metal is about 25μ.
Claim 63
Dependent Claim
28 words
Method according to claim 24, wherein the metallic structure containing said host metal comprises a metallic sheet having a layer of host metal which presents a dendritic surface.
Claim 64
Dependent Claim
20 words
Method according to claim 61, wherein the metallic sheet is selected from the group consisting of copper, molybdenum and nickel.
Claim 65
Dependent Claim
15 words
Method according to claim 62, wherein the dendritic surface of the host metal comprises aluminum.
Claim 66
Dependent Claim
25 words
Method according to claims 61, 62 or 63, wherein the total thickness of the dendritic layer of host metal varies between about 5μ and 50μ.
Claim 67
Dependent Claim
23 words
Method according to claim 24, wherein the metallic structure containing said host metal is essentially made of a sheet of said host metal.
Claim 68
Dependent Claim
14 words
Method according to claim 65, wherein the metallic structure comprises a sheet of aluminum.
Claim 69
Dependent Claim
51 words
Method according to claim 66, wherein the sheet of aluminum has a thickness which varies between about 5μ and 500μ, and the reaction is allowed to proceed until the sheet has one or two alloyed faces and non-reacted zone, and maintaining coexistence between the alloy formed and the non-reacted host structure.
Claim 70
Dependent Claim
19 words
Method according to claim 67, wherein the aluminum sheet has a thickness which varies between about 50μ and 300μ.
Claim 71
Dependent Claim
42 words
Method according to claim 24, wherein the host structure comprises a mixture of spheres, fibers or flakes of said host metal which are contacted with the organic solution to give spheres, fibers or flakes of alloys which are treated with the electrolyte.
Claim 72
Dependent Claim
34 words
Method according to claim 69, wherein the spheres, fibers or flakes of host metal are not larger than 50μ along of one of their dimensions and films of alloy are formed on these particles.
Claim 73
Dependent Claim
60 words
Method according to claim 69, wherein the host structure comprises particles of Al, Mg, Si, Zn in the form of spheres, flakes or fibers of predetermined granulometry selected so as to form alloys of lithium responding to stoichiometries in the vicinity of LiAl, Li 0 .9 Mg, Li 3 .5 Si, LiZn from a free radical solution of this metal.
Claim 74
Dependent Claim
51 words
Method according to claim 24, wherein the organic solution is based on benzene and contains naphthalene or biphenyl, and N,N,N',N'-tetramethyl 1,2-ethane diamine or THF, and is saturated with lithium said solution being in free radical form as a result of containing metallic lithium, said solution containing an excess of metallic lithium.
Claim 75
Dependent Claim
52 words
Method according to claim 72, wherein the organic solution is based on benzene and contains naphthalene or biphenyl, and N,N,N',N'-tetramethyl 1,2-ethane diamine or THF, and is saturated with lithium, said solution being in free radical form as a result of containing metallic lithium, said solution containing a limited quantity of said lithium.
References Cited (Backward Citations)
US4002492A
Cited
US4056885A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-08-31 | 1991-03-02 | 1991-09-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-08-31 | 1995-03-02 | 1995-09-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-08-31 | 1999-03-02 | 1999-09-01 | $7700.00 | Window Closed / Lapsed |