Method of preparing lithium-aluminum alloy electrodes
Assignee: ExxonMobil Technology and Engineering Co
•
Filing: 1976-12-15
•
Granted: 1977-11-08
•
Expires: 1996-12-15
Abstract
Abstract A lithium-aluminum alloy electrode having from about 10% to 95% by weight of lithium is formed by contacting a preformed lithium-aluminum laminate with a solution of a lithium salt in an organic solvent. Preferably the laminate is supported on a wire mesh support structure.
Inventors
- 👤 Bhaskara M. L. Rao
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 15:31
CPC Classifications
H; H01; H01M; H01M4/00; H01M4/02; H01M4/13; H01M4/36; H01M4/38; H01M4/40; H01M4/64; H01M4/70; H01M4/72; H01M4/74; H01M4/742; H01M2004/026; H01M2004/027; H01M2300/00; H01M2300/0017; H01M2300/0025; H01M4/04; H01M4/049; H01M4/0492; H01M4/405; H01M4/46; H01M4/463; Y; Y02; Y02E; Y02E60/00; Y02E60/10; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/49108
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
54 words
A method of making a lithium-aluminum alloy electrode comprising: a. forming a laminate having at least one ply of aluminum sheet material and one ply of lithium sheet material; b. contacting the laminate with a solution of a lithium salt dissolved in an organic solvent for a time sufficient for alloy formation to occur.
Claim 2
Independent Claim
54 words
A method of making a lithium-aluminum alloy electrode comprising: a. forming a laminate having at least one ply of aluminum sheet material and one ply of lithium sheet material; b. contacting the laminate with a solution of a lithium salt dissolved in an organic solvent for a time sufficient for alloy formation to occur.
Claim 3
Dependent Claim
18 words
The method of claim 1 wherein said laminate has two plies of aluminum enclosing one ply of lithium.
Claim 4
Dependent Claim
16 words
The method of claim 2 wherein the laminate is supported on a metal mesh support structure.
Claim 5
Dependent Claim
23 words
The method of claim 3 wherein the weight ratio of aluminum to lithium is in the range of 10% to 95% by weight.
Claim 6
Dependent Claim
23 words
The method of claim 4 wherein the weight ratio of aluminum to lithium is in the range of 20% to 80% by weight.
Claim 7
Dependent Claim
27 words
The method of claim 4 wherein the concentration of lithium salt dissolved in an organic solvent is in the range of from about 1 to 3 molar.
Claim 8
Dependent Claim
17 words
The method of claim 6 wherein the solution of the salt is lithium perchlorate dissolved in dioxolane.
Claim 9
Dependent Claim
24 words
The method of claim 7 wherein the concentration of lithium perchlorate in dioxolane is in the range of from about 2.5 to 3 molar.
Claim 10
Independent Claim
94 words
The method of forming a lithium-aluminum alloy electrode comprising: pressing a sheet of lithium metal onto a metal mesh support structure; pressing aluminum sheet material on each major surface of said lithium pressed on said wire mesh, thereby forming a laminated structure, said aluminum sheet material being perforated, the weight ratio of aluminum sheet material to lithium sheet material being in the range of from about 10% to about 95% by weight; contacting said laminated structure with a nonaqueous organic solution of a lithium salt for a time sufficient for alloy formation to occur.
Claim 11
Independent Claim
94 words
The method of forming a lithium-aluminum alloy electrode comprising: pressing a sheet of lithium metal onto a metal mesh support structure; pressing aluminum sheet material on each major surface of said lithium pressed on said wire mesh, thereby forming a laminated structure, said aluminum sheet material being perforated, the weight ratio of aluminum sheet material to lithium sheet material being in the range of from about 10% to about 95% by weight; contacting said laminated structure with a nonaqueous organic solution of a lithium salt for a time sufficient for alloy formation to occur.
Claim 12
Dependent Claim
27 words
The method of claim 9 wherein the weight ratio of aluminum to lithium sheet material is in the range from about 20% to about 80% by weight.
Claim 13
Dependent Claim
24 words
The method of claim 10 wherein the perforations in said aluminum sheet comprise greater than 35% of the total area of said aluminum sheet.
Claim 14
Dependent Claim
19 words
The method of claim 11 wherein the concentration of lithium salt solution is between about 1.0 and 3.0 molar.
Claim 15
Dependent Claim
20 words
The method of claim 12 wherein the lithium salt is lithium perchlorate and wherein the nonaqueous organic solvent is dioxolane.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-11-07 | 1981-05-09 | 1981-11-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-11-07 | 1985-05-09 | 1985-11-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-11-07 | 1989-05-09 | 1989-11-08 | $7700.00 | Window Closed / Lapsed |