Silicon nitride/silicon carbide composition and articles thereof
Assignee: Stemcor Corp
•
Filing: 1985-07-23
•
Granted: 1987-09-01
•
Expires: 2005-07-23
Abstract
Abstract Corrosion and thermal shock resistant high silicon nitride content silicon nitride-bonded silicon carbide article, e.g., nozzle for transfer of molten metal, is prepared by combining finely divided silicon metal, silicon carbide grain with processing aids, forming the mixture into an article, and firing the article in nitrogen. Even higher silicon nitride content is obtained by crushing the article to obtain a precursor grog material, combining this grog with more finely divided silicon metal and processing aids, forming the mixture into an article and firing in nitrogen. Silicon nitride content of up to about 70 weight percent may be obtained with single mixing and firing; up to about 98 weight percent with use of nitrided precusor grog, remixing and firing. With reiteration, a silicon nitride content of essentially 100 weight percent can be approached.
Inventors
- 👤 Carl H. Bates
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 15:22
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/515; C04B35/58; C04B35/584; C04B35/591; C04B35/56; C04B35/565
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
175 words
A process for the preparation of an article of silicon nitride - bonded silicon carbide comprising: a. forming an admixture of finely divided silicon metal, and SiC grain, shaping said admixture into discrete pellets, drying said pellets, firing said dried pellets in a nitrogenous non-oxidative atmosphere at a temperature and for a period sufficient to convert substantially all of said silicon metal to Si 3 N 4 , thereby resulting in formation of Si 3 N 4 -bonded SiC precursor material pellets having a Si 3 N 4 content of at least 50 weight percent; b. crushing said precursor material pellets; c. mixing from 30 to 75 weight percent of said crushed precursor material with from 16 to 60 weight percent finely divided silicon metal to form a green composition; d. shaping said green composition and drying said shaped green composition; and e. firing said dried green composition in a nitrogenous non-oxidative atmosphere at a temperature and for a period sufficient to convert substantially all of said silicon metal to Si 3 N 4 .
Claim 2
Dependent Claim
175 words
A process for the preparation of an article of silicon nitride - bonded silicon carbide comprising: a. forming an admixture of finely divided silicon metal, and SiC grain, shaping said admixture into discrete pellets, drying said pellets, firing said dried pellets in a nitrogenous non-oxidative atmosphere at a temperature and for a period sufficient to convert substantially all of said silicon metal to Si 3 N 4 , thereby resulting in formation of Si 3 N 4 -bonded SiC precursor material pellets having a Si 3 N 4 content of at least 50 weight percent; b. crushing said precursor material pellets; c. mixing from 30 to 75 weight percent of said crushed precursor material with from 16 to 60 weight percent finely divided silicon metal to form a green composition; d. shaping said green composition and drying said shaped green composition; and e. firing said dried green composition in a nitrogenous non-oxidative atmosphere at a temperature and for a period sufficient to convert substantially all of said silicon metal to Si 3 N 4 .
Claim 3
Dependent Claim
27 words
The process of claim 1 wherein firing of the precursor material pellets occur at about atmospheric pressure at a temperature of between 1300° C. and 1450° C.
Claim 4
Dependent Claim
27 words
The process of claim 2 wherein reaction sintering of said dried green composition occurs at about atmospheric pressure at a temperature between 1300° C. and 1450° C.
Claim 5
Dependent Claim
31 words
The process of claim 1 wherein the silicon metal powder has a particle size of about 200 mesh; and the green pellets have a density of 1.7 g/cc to 1.9 g/cc.
Claim 6
Dependent Claim
35 words
The process of claim 1 wherein about 2 weight percent calcium aluminate cement and about 1 weight percent dextrin and sufficient water are added in step (a) and/or step (c) to form a plastic mixture.
Claim 7
Dependent Claim
47 words
The process of claim 1 wherein the green composition further includes up to 4 weight percent of calcium aluminate cement, up to 6 weight percent of Tennessee ball clay, from 1 to 6 weight percent of fumed silica powder and from 0.5 to 2 weight percent dextrin.
Claim 8
Dependent Claim
37 words
The process of claim 1 further comprising adding sufficient water to step (c) to result in formation of a castable liquid material and casting said castable liquid material into a mold into the configuration of a nozzle.
Claim 9
Dependent Claim
39 words
The process of claim 1 further comprising: f. crushing the material of step (e) after firing; and g. repeating steps (b) through (e) but with substitution of the material of step (f) for the precursor material of step (a).
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-08-31 | 1991-03-02 | 1991-09-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-08-31 | 1995-03-02 | 1995-09-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-08-31 | 1999-03-02 | 1999-09-01 | $7700.00 | Window Closed / Lapsed |