Chromic acid anodizing of aluminium prior to adhesive bonding
Assignee: BAE Systems PLC
•
Filing: 1986-03-26
•
Granted: 1987-09-01
•
Expires: 2006-03-26
Abstract
Abstract A method of pre-treating articles of aluminium or aluminum alloy to form an environmentally stable adhesive receptive oxide layer, the method comprising anodizing said articles in a bath containing an aqueous solution of chromic acid at a minimum defined temperature/time/voltage cycle. By this method a particularly advantageous oxide surface layer is achieved in which the pore diameter of the outer, non-barrier layer is at least a factor of 10 larger than that achieved by prior art processes.
Inventors
- 👤 Peter Albericci
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 10:29
CPC Classifications
C; C25; C25D; C25D11/00; C25D11/02; C25D11/04; C25D11/06; C25D11/08
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
118 words
A method of preparing an adhesively bonded aluminium or aluminium alloy structure comprising: forming an environmentally stable adhesive receptive oxide layer on the surfaces of the articles to be adhesively bonded by anodising said articles in a bath containing an aqueous solution of chromic acid, the bath voltage being from at least 5 volts to about 30 volts, the concentration of chromic acid in solution lying in the range of 3% to 5% w/w, said solution being maintained at a temperature between at least 55° C. to about 62° C.; rinsing said articles to remove said solution, applying an adhesive to said surfaces to be adhesively bonded and bonding said articles together to form said adhesively bonded structure.
Claim 2
Independent Claim
118 words
A method of preparing an adhesively bonded aluminium or aluminium alloy structure comprising: forming an environmentally stable adhesive receptive oxide layer on the surfaces of the articles to be adhesively bonded by anodising said articles in a bath containing an aqueous solution of chromic acid, the bath voltage being from at least 5 volts to about 30 volts, the concentration of chromic acid in solution lying in the range of 3% to 5% w/w, said solution being maintained at a temperature between at least 55° C. to about 62° C.; rinsing said articles to remove said solution, applying an adhesive to said surfaces to be adhesively bonded and bonding said articles together to form said adhesively bonded structure.
Claim 3
Dependent Claim
51 words
A method according to claim 1 in which the anodic step is carried out for a time and at a voltage such that the resultant anodic layer has a thickness of about 3 microns, and the resultant porosity of the outer, non-barrier layer has a pore diameter of typically 0.2 microns.
Claim 4
Dependent Claim
44 words
A method according to claim 1 or claim 2 in which the anodic step is carried out using a step-wise voltage profile in which the bath voltage is maintained at 10 volts for 15 minutes and thereafter 20 volts for a further 15 minutes.
Claim 5
Dependent Claim
44 words
A method according to claim 1 or claim 2 in which the anodic step is carried out using a step-wise voltage profile in which the bath voltage is maintained at 10 volts for 10 minutes and thereafter 20 volts for a further 20 minutes.
Claim 6
Independent Claim
131 words
A method of preparing an adhesively bonded aluminium or aluminium alloy structure comprising: degreasing the articles to be bonded in a solvent vapour tank, forming an environmentally stable adhesive layer on the surfaces of the articles to be adhesively bonded by anodising said articles in a bath containing an aqueous solution of chromic acid in which the free chromic acid concentration is of the order of 35 g/L and total chromic acid 40 g/L, in which the bath temperature is substantially 61° and the bath voltage is maintained at 10 volts for 15 minutes and thereafter 20 volts for a further 15 minutes, rinsing said articles to remove said solution, applying an adhesive to said surfaces to be adhesively bonded and bonding said articles together to form said adhesively bonded structure.
Claim 7
Independent Claim
131 words
A method of preparing an adhesively bonded aluminium or aluminium alloy structure comprising: degreasing the articles to be bonded in a solvent vapour tank, forming an environmentally stable adhesive layer on the surfaces of the articles to be adhesively bonded by anodising said articles in a bath containing an aqueous solution of chromic acid in which the free chromic acid concentration is of the order of 35 g/L and total chromic acid 40 g/L, in which the bath temperature is substantially 61° and the bath voltage is maintained at 10 volts for 15 minutes and thereafter 20 volts for a further 15 minutes, rinsing said articles to remove said solution, applying an adhesive to said surfaces to be adhesively bonded and bonding said articles together to form said adhesively bonded structure.
Claim 8
Dependent Claim
35 words
A method according to claim 5 in which the resultant anodic layer has a thickness of substantially 3 microns and a porosity of the outer, non-barrier layer has a pore diameter of typically 0.2 microns.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-08-31 | 1991-03-02 | 1991-09-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-08-31 | 1995-03-02 | 1995-09-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-08-31 | 1999-03-02 | 1999-09-01 | $7700.00 | Window Closed / Lapsed |