Tapered trench process
Assignee: Texas Instruments Inc
•
Filing: 1986-03-19
•
Granted: 1987-09-01
•
Expires: 2006-03-19
Abstract
Abstract A plasma dry etch process for etching deep trenches in single crystal silicon material with controlled wall profile, for trench capacitors or trench isolation structures. HCl is used as an etchant under RIE conditions with a SiO 2 hard mask. The SiO 2 hard mask is forward sputtered during the course of the Si etch so as to slowly deposit SiO x (x<2) on the sidewalls of the silicon trench. Since the sidewall deposit shadows etching at the bottom of the trench near the sidewall, the effect of this gradual buildup is to produce a positively sloped trench sidewall without "grooving" the bottom of the trench, and without linewidth loss. This process avoids the prior art problems of mask undercut, which generates voids during subsequent refill processing, and grooving at the bottom of the trench, which is exceedingly deleterious to thin capacitor dielectric integrity.
Inventors
- 👤 Monte A. Douglas
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 05:38
CPC Classifications
H; H10; H10P; H10P50/00; H10P50/20; H10P50/24; H10P50/242; H10P50/244; H10P50/69; H10P50/691; H10P50/693; H10P50/694; Y; Y10; Y10S; Y10S148/00; Y10S148/05
Claims Analysis
Total Claims: 32
Claim 1
Independent Claim
52 words
A process for etching trenches in silicon, comprising the steps of: (a) providing a patterned mask over a silicon substrate; (b) plasma etching exposed portions of said silicon substrate under etch conditions such that the material of said mask is forward sputtered to induce deposition on sidewalls of said trench during etching.
Claim 2
Dependent Claim
52 words
A process for etching trenches in silicon, comprising the steps of: (a) providing a patterned mask over a silicon substrate; (b) plasma etching exposed portions of said silicon substrate under etch conditions such that the material of said mask is forward sputtered to induce deposition on sidewalls of said trench during etching.
Claim 3
Dependent Claim
96 words
A process for etching trenches in silicon, comprising the steps of: (a) providing a silicon substrate having thereon a patterned hard mask comprising silicon oxides and being defined to expose said silicon only in predetermined trench locations; (b) etching a trench, by means of a plasma source of silicon etchant ions, in said predetermined trench locations of said silicon substrate under conditions such that oxides of silicon are continually deposited on sidewalls of said trench during etching, wherein substantially all of the atomic oxygen in said oxides on said trench sidewalls derives from said hard mask.
Claim 4
Dependent Claim
96 words
A process for etching trenches in silicon, comprising the steps of: (a) providing a silicon substrate having thereon a patterned hard mask comprising silicon oxides and being defined to expose said silicon only in predetermined trench locations; (b) etching a trench, by means of a plasma source of silicon etchant ions, in said predetermined trench locations of said silicon substrate under conditions such that oxides of silicon are continually deposited on sidewalls of said trench during etching, wherein substantially all of the atomic oxygen in said oxides on said trench sidewalls derives from said hard mask.
Claim 5
Dependent Claim
44 words
The process of claim 1, wherein said mask consists essentially of silicon oxides, and wherein said trench etch comprises etching in a glow discharge formed in an etch gas containing one or more chlorine-bearing species, and said chlorine-bearing species consist predominantly of hydrogen chloride.
Claim 6
Dependent Claim
41 words
The process of claim 1, wherein said mask consists essentially of silicon oxides, and wherein said trench etch comprises plasma etching in an etch gas which provides a source of Cl+ ions in greater quantity than of Cl 2 + ions.
Claim 7
Dependent Claim
23 words
The process of claim 1, wherein said trench etch is performed at a total pressure in the range of 1 to 100 milliTorr.
Claim 8
Dependent Claim
28 words
The process of claim 1, wherein said openings in said mask have a sidewall angle, prior to said trench etch, in the range of 80 to 89 degrees.
Claim 9
Dependent Claim
23 words
The process of claim 1, wherein said trench etch is performed at a bias voltage in the range of 250 to 550 volts.
Claim 10
Dependent Claim
37 words
The process of claim 2, wherein said mask consists essentially of silicon oxides, and wherein said trench etch comprises plasma etching in an etch gas containing chlorine-bearing species, and said chlorine-bearing species consist predominantly of hydrogen chloride.
Claim 11
Dependent Claim
41 words
The process of claim 2, wherein said mask consists essentially of silicon oxides, and wherein said trench etch comprises plasma etching in an etch gas which provides a source of Cl+ ions in greater quantity than of Cl 2 + ions.
Claim 12
Dependent Claim
23 words
The process of claim 2, wherein said trench etch is performed at a total pressure in the range of 1 to 100 milliTorr.
Claim 13
Dependent Claim
28 words
The process of claim 2, wherein said openings in said mask have a sidewall angle, prior to said trench etch, in the range of 80 to 89 degrees.
Claim 14
Dependent Claim
23 words
The process of claim 2, wherein said trench etch is performed at a bias voltage in the range of 250 to 550 volts.
Claim 15
Dependent Claim
33 words
The process of claim 2, wherein said trench etching plasma includes a small fraction of an oxide-etching species, said small fraction being preselected to adjust the rate of deposition of said sidewall oxides.
Claim 16
Dependent Claim
26 words
The process of claim 2, wherein said plasma etching is performed at a volumetric power density in the range of 5 to 10 Watts per liter.
Claim 17
Dependent Claim
19 words
The process of claim 2, wherein said trench etch comprises plasma etching in an etch gas comprising hydrogen chloride.
Claim 18
Dependent Claim
19 words
The process of claim 1, wherein said trench etch comprises plasma etching in an etch gas comprising hydrogen chloride.
Claim 19
Dependent Claim
95 words
A process for etching trenches in silicon, comprising the steps of: (a) providing a patterned mask over a silicon substrate; (b) etching exposed portions of said silicon substrate in proximity to a glow discharge under etch conditions such that the material of said mask is forward sputtered to induce deposition on sidewalls of said trench during etching, said conditions being adjusted during etching so that said deposition on said sidewalls of said trench is enhanced during the first 20% of depth of said trench and also during the last 20% of depth of said trench.
Claim 20
Dependent Claim
95 words
A process for etching trenches in silicon, comprising the steps of: (a) providing a patterned mask over a silicon substrate; (b) etching exposed portions of said silicon substrate in proximity to a glow discharge under etch conditions such that the material of said mask is forward sputtered to induce deposition on sidewalls of said trench during etching, said conditions being adjusted during etching so that said deposition on said sidewalls of said trench is enhanced during the first 20% of depth of said trench and also during the last 20% of depth of said trench.
Claim 21
Dependent Claim
149 words
A process for etching trenches in silicon, comprising the steps of: (a) providing a silicon substrate having thereon a patterned hard mask comprising silicon oxides and being defined to expose said silicon only in predetermined trench locations; (b) etching a trench, i. by means of a plasma source of silicon etchant ions, ii. in said predetermined trench locations of said silicon substrate iii. under conditions such that a material including a substantial fraction of oxides of silicon is continually deposited on sidewalls of said trench during etching, iv. said conditions being adjusted during etching so that said deposition on said sidewalls of said trench is enhanced during the first 20% of depth of said trench and also during the last 20% of depth of said trench; v. wherein substantially all of the atomic oxygen in said material deposited on said sidewalls of said trench derives from said hard mask.
Claim 22
Dependent Claim
149 words
A process for etching trenches in silicon, comprising the steps of: (a) providing a silicon substrate having thereon a patterned hard mask comprising silicon oxides and being defined to expose said silicon only in predetermined trench locations; (b) etching a trench, i. by means of a plasma source of silicon etchant ions, ii. in said predetermined trench locations of said silicon substrate iii. under conditions such that a material including a substantial fraction of oxides of silicon is continually deposited on sidewalls of said trench during etching, iv. said conditions being adjusted during etching so that said deposition on said sidewalls of said trench is enhanced during the first 20% of depth of said trench and also during the last 20% of depth of said trench; v. wherein substantially all of the atomic oxygen in said material deposited on said sidewalls of said trench derives from said hard mask.
Claim 23
Dependent Claim
21 words
The process of claim 18, wherein said etching is initialized using an etchant composition which is not highly selective to oxide.
Claim 24
Dependent Claim
21 words
The process of claim 17, wherein said etching is initialized using an etchant composition which is not highly selective to oxide.
Claim 25
Dependent Claim
37 words
The process of claim 18, wherein a source of silicon-bearing radicals is introduced to increase sidewall deposition during at least the first 20% of depth of said trench and the last 20% of depth of said trench.
Claim 26
Dependent Claim
19 words
The process of the 21 claim, wherein said source of silicon-bearing radicals consists essentially of a halated silane compound.
Claim 27
Dependent Claim
14 words
The process of the 22 claim, wherein said halated silane compound comprises a chlorosilane.
Claim 28
Dependent Claim
17 words
The process of the 22 claim, wherein said halated silane compound consists essentially of SiCl 4 .
Claim 29
Dependent Claim
37 words
The process of claim 17, wherein a source of silicon-bearing radicals is introduced to increase sidewall deposition during at least the first 20% of depth of said trench and the last 20% of depth of said trench.
Claim 30
Dependent Claim
19 words
The process of the 25 claim, wherein said source of silicon-bearing radicals consists essentially of a halated silane compound.
Claim 31
Dependent Claim
14 words
The process of the 26 claim, wherein said halated silane compound comprises a chlorosilane.
Claim 32
Dependent Claim
17 words
The process of the 27 claim, wherein said halated silane compound consists essentially of SiCl 4 .
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-08-31 | 1991-03-02 | 1991-09-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-08-31 | 1995-03-02 | 1995-09-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-08-31 | 1999-03-02 | 1999-09-01 | $7700.00 | Window Closed / Lapsed |