Method for manufacturing a reaction-sintered metal/ceramic composite body and metal/ceramic composite body
Assignee: Moltech Invent SA
•
Filing: 1986-05-19
•
Granted: 1987-08-25
•
Expires: 2006-05-19
Abstract
Abstract A method is disclosed for manufacturing a reaction sintered composite article which comprises at least one ceramic component. The method comprises preparing a particulate mixture of precursor powders leading to the formation of said composite material upon reaction sintering, pressing said particulate mixture to a self-sustaining body, heating said body up to a temperature below the temperature at which the reaction sintering is initiated, comminuting the heat treating body, selecting particles of a suitable grain size distribution, pressing said particles into shapes of desired size and configuration, and heating said shapes up to a temperature at which the reaction sintering is initiated. The reaction sintered body comprises borides, carbides, nitrides or silicides of a transition metal of the groups IVb, Vb or VIb of the periodic table (comprising titanium, hafnium, zirconium, vanadium, niobium, tantalum, chromium, molybdenum and tungsten), and a metal oxide. In the case that the composite material comprises Al2O3, TiB2 and facultatively Al, the precursor powder may comprise TiO2, B2O3 and Al. Composite bodies of sizes, shapes, varying compositions or other particular configurations which do not allow for the preparation of the final bodies in one operation are produced by preparing sub-sections of precursor shapes which are pressed in a first pressing operation, assembled to a shape of essentially the final configuration, again pressed and reaction sintered.
Inventors
- 👤 Michel Chevigne
- 👤 Dominique Darracq
- 👤 Jean-Pol Wiaux
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 18:48
CPC Classifications
C; C25; C25C; C25C3/00; C25C3/06; C25C3/08; C04; C04B; C04B35/00; C04B35/622; C04B35/64; C04B35/65; C04B35/651; C22; C22C; C22C1/00; C22C1/04; C22C1/05; C22C1/051; C22C29/00; C22C29/12
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
154 words
A method for manufacturing a reaction sintered composite article, comprising a mixture of at least two materials selected from a group consisting of borides, carbides, nitrides or silicides of a first metal being a transition metal of the groups IVb, Vb or VIb of the periodic table (consisting of titanium, hafnium, zirconium, vanadium, niobium, tantalum, chromium, molybdenum and tungsten), a second metal, and an oxide of said second metal, the method comprising providing a particulate precursor mixture leading to the formation of the said mixture of materials upon reaction sintering; pressing said precursor mixture to a self-sustaining body; presintering said body by heating it up to a temperature below the temperature at which the reaction sintering is initiated; comminuting the presintered body; selecting particles of a suitable grain size distribution; pressing said particles into shapes of desired size and configuration; heating said shapes up to a temperature at which the reaction sintering is initiated.
Claim 2
Independent Claim
154 words
A method for manufacturing a reaction sintered composite article, comprising a mixture of at least two materials selected from a group consisting of borides, carbides, nitrides or silicides of a first metal being a transition metal of the groups IVb, Vb or VIb of the periodic table (consisting of titanium, hafnium, zirconium, vanadium, niobium, tantalum, chromium, molybdenum and tungsten), a second metal, and an oxide of said second metal, the method comprising providing a particulate precursor mixture leading to the formation of the said mixture of materials upon reaction sintering; pressing said precursor mixture to a self-sustaining body; presintering said body by heating it up to a temperature below the temperature at which the reaction sintering is initiated; comminuting the presintered body; selecting particles of a suitable grain size distribution; pressing said particles into shapes of desired size and configuration; heating said shapes up to a temperature at which the reaction sintering is initiated.
Claim 3
Dependent Claim
105 words
The method of claim 1, wherein the composite article is prepared by: pressing precursor material in a first pressing operation, presintering said pressed precursor material by heating it up to a temperature below the temperature at which reaction sintering is initiated, comminuting the presintered material, selecting particles of a suitable grain size distribution, and pressing said selected particles into shapes of the size of said sub-sections of said article; assembling a plurality of said sub-sections to a precursor shape; pressing said precursor shape in a second pressing operation; and heating said pressed precursor shape up to a temperature at which the reaction sintering is initiated.
Claim 4
Dependent Claim
24 words
The method of claim 1, wherein the composite article comprises a metal selected from aluminum, magnesium, calcium and alkali and other alkaline earth metals.
Claim 5
Dependent Claim
16 words
The method of claim 3, wherein the composite article comprises titanium diboride, aluminum oxide and aluminum.
Claim 6
Dependent Claim
15 words
The method of claim 4, wherein the reaction sintering is carried out under liquid aluminum.
Claim 7
Dependent Claim
14 words
The method of claim 4, wherein the sintering is carried out under inert atmosphere.
Claim 8
Dependent Claim
18 words
The method of claim 4, wherein the selected particles have a grain size of smaller than 28 micrometer.
Claim 9
Dependent Claim
107 words
The method of claim 4, wherein the precursor mixture comprises an oxide, or a nitride or a hydride of at least one transition metal of the groups IVb, Vb or VIb of the Periodic Table (consisting of titanium, hafnium, zirconium, vanadium, niobium, tantalum, chromium, molybdenum and tungsten); a second metal in metallic state and/or a boride, nitride, carbide or silicide of said second metal or a boron-, nitrogen-, carbon or silicon-containing compound of a non-metallic element, the reaction-sintered article comprising a boride, nitride, carbide or silicide of said transition metal(s), said second metal in metallic state and/or an oxide, nitride, carbide or silicide of said second metal.
Claim 10
Dependent Claim
18 words
The method of claim 8, wherein the precursor mixture comprises powders of titanium dioxide, boron oxide, and aluminum.
Claim 11
Dependent Claim
17 words
The method of claim 9, wherein the precursor mixture further comprises a powder of TiB 2 .
Claim 12
Dependent Claim
20 words
The method of claim 8, wherein the presintering is carried out at a temperature between 300° C. and 800° C.
Claim 13
Dependent Claim
26 words
The method of claim 11, wherein the temperature is between 400° C. and 500° C., at which said B 2 O 3 is in softened state.
Claim 14
Dependent Claim
83 words
A reaction sintered composite article comprising a mixture of at least two materials selected from borides, carbides, nitrides or silicides of a first metal being a transition metal of the groups IVb, Vb or VIb of the periodic table (consisting of titanium, hafnium, zircinium, vanadium, niobium, tantalum, chromium, molybdenum and tungsten), a second metal, and an oxide of said second metal, wherein the microstructure of said article has a uniform distribution of single, non-agglomerated grains of the reaction products of the sinter reaction.
Claim 15
Dependent Claim
83 words
A reaction sintered composite article comprising a mixture of at least two materials selected from borides, carbides, nitrides or silicides of a first metal being a transition metal of the groups IVb, Vb or VIb of the periodic table (consisting of titanium, hafnium, zircinium, vanadium, niobium, tantalum, chromium, molybdenum and tungsten), a second metal, and an oxide of said second metal, wherein the microstructure of said article has a uniform distribution of single, non-agglomerated grains of the reaction products of the sinter reaction.
Claim 16
Dependent Claim
95 words
The article of claim 13, wherein the micro-structure has been obtained by providing a particulate precursor mixture leading to the formation of the said mixture of materials upon reaction sintering; pressing said precursor mixture into a self-sustaining body; presintering said body by heating it up to a temperature below the temperature at which the reaction sintering is initiated; comminuting the presintered body; selecting particles of a suitable grain size distribution; pressing said particles to shapes of desired size and configuration; and heating said shapes up to a temperature at which the reaction sintering is initiated.
Claim 17
Dependent Claim
96 words
The article of claim 13, prepared by pressing precursor material in a first pressing operation, presintering said pressed precursor material by heating it up to a temperature below the temperature at which the reaction sintering is initiated, comminuting the presintered material, selecting particles of a suitable grain size distribution, and pressing said selected particles into shapes of the size of sub-sections of said body, assembling said sub-sections to said precursor shape, pressing said precursor shape in a second pressing operation, and heating said pressed precursor shape up to a temperature at which reaction sintering is initiated.
Claim 18
Dependent Claim
16 words
The article of claim 13, wherein the composite material comprises titanium diboride, aluminum oxide and aluminum.
Claim 19
Dependent Claim
25 words
The article of claim 13, wherein the composite material comprises a component in an aluminum electrowinning cell, which component is normally exposed to molten aluminum.
Claim 20
Dependent Claim
25 words
The article of claim 14, wherein the composite material comprises a component in an aluminum electrowinning cell, which component is normally exposed to molten aluminum.
References Cited (Backward Citations)
US1981719A
Cited
US2033513A
Cited
US3031300A
Cited
US3360348A
Cited
US3783494A
Cited
US4514268A
Cited
US4534835A
Cited
US4540475A
Cited
US4605634A
Cited
US4605633A
Cited
US4585618A
Cited
US4610726A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-08-24 | 1991-02-23 | 1991-08-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-08-24 | 1995-02-23 | 1995-08-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-08-24 | 1999-02-23 | 1999-08-25 | $7700.00 | Window Closed / Lapsed |