Reaction sintered oxide-boride

Claim 2

A reaction sintered oxide-boride ceramic body consisting essentially of a fine-grained, homogeneous, intimate interdispersion of: (a) 10-90 mole percent of boride phase or phases having a maximum grain size substantially not greater than 15 μm and being boride of one or more of the elements of Groups 3b including lanthanide and actinide series elements, 4b, 5b and 6b, and (b) 10-90 mole percent of oxide phase or phases having a maximum grain size substantially not greater than 15 μm and being oxide of one or more of the elements of Groups 3a, 4a, 3b, 4b, 5b, 6b and 8; which body is prepared by the process comprising; (c) admixing particulate reactants of maximum particle size substantially not greater than 150 μm and being elements, compounds, intermetallic compounds, alloys or combination thereof in stoichiometric proportions to substantially form the boride and oxide phases, and (d) shaping and heating the admixture to form the reaction sintered body, the heating being done in nonreactive atmosphere and at temperature at which the reaction and sintering occurs between the reactants to substantially form the boride and oxide phases.

Claim 3

The body of claim 1 which is prepared by the shaping and heating being separate sequential steps.

Claim 4

The body of claim 1 which is prepared by the shaping and heating being substantially simultaneous steps of hot pressing.

Claim 5

The body of claim 1 wherein the maximum grain size of the boride and oxide phases is substantially not greater than 5 μm and the maximum particle size of the reactants is substantially not greater than 44 μm.

Claim 6

The body of claim 4 wherein the mean grain size of the boride and oxide phases is substantially not greater than 3.5 μm.

Claim 7

The body of claim 1 wherein the boride is of one or more elements of Groups 4b, 5b and 6b, and the oxide is predominantly Al 2 O 3 .

Claim 8

The body of claim 6 wherein the boride is of one or more elements of Group 4b.

Claim 9

The body of claim 1 having 25-90 mole percent of the boride phase or phases and 10-75 mole percent of the oxice phase or phases.

Claim 10

The body of claim 8 which is prepared by the shaping and heating being substantially simultaneous steps of hot pressing.

Claim 11

The body of claim 9 wherein the maximum grain size of the boride and oxide phases is substantially not greater than 5 μm and the maximum particle size of the reactants is substantially not greater than 44 μm.

Claim 12

The body of claim 10 wherein the boride is of one or more elements of Groups 4b, 5b and 6b, and the oxide is predominantly Al 2 O 3 .

Claim 13

The body of claim 11 wherein the main grain size of the boride and oxide phases is substantially not greater than 3.5 μm.

Claim 14

The body of claim 12 wherein the boride is of one or more elements of Group 4b.

Claim 15

The body of claim 13 wherein the maximum grain size of the boride and oxide phases is less than 2 μm.

Claim 16

The body of claim 14 wherein the boride is TiB 2 and the oxide is Al 2 O 3 .

Claim 17

The method of forming the body of claim 1 comprising: (a) admixing the particulate reactants, and (b) shaping and heating the admixture to form the reaction sintered body.

Claim 18

A reaction sintered oxide-boride ceramic body having a virtual absence of open porosity and consisting essentially of a fine-grained, homogeneous, intimate interdispersion of: (a) 10-90 mole percent of boride phase or phases having a maximum grain size substantially not greater than 15 μm and being boride of one or more of the elements of Groups 3b including lanthanide and actinide series elements, 4b, 5b and 6b, and (b) 10-90 mole percent of oxide phase or phases having a maximum grain size substantially not greater than 15 μm and being oxide of one or more of the elements of Groups 3a, 4a, 3b, 4b, 5b, 6b and 8; which body is prepared by the process comprising; (c) admixing particulate reactants of maximum particle size substantially not greater than 150 μm and being elements, compounds, intermetallic compounds, alloys or combination thereof in stoichiometric proportions to substantially form the boride and oxide phases, and (d) shaping and heating the admixture to form the reaction sintered body, the heating being done in nonreactive atmosphere and at temperature at which the reaction and sintering occurs between the reactants to substantially form the boride and oxide phases.

Claim 19

A reaction sintered oxide-boride ceramic body having a virtual absence of open porosity and consisting essentially of a fine-grained, homogeneous, intimate interdispersion of: (a) 10-90 mole percent of boride phase or phases having a maximum grain size substantially not greater than 15 μm and being boride of one or more of the elements of Groups 3b including lanthanide and actinide series elements, 4b, 5b and 6b, and (b) 10-90 mole percent of oxide phase or phases having a maximum grain size substantially not greater than 15 μm and being oxide of one or more of the elements of Groups 3a, 4a, 3b, 4b, 5b, 6b and 8; which body is prepared by the process comprising; (c) admixing particulate reactants of maximum particle size substantially not greater than 150 μm and being elements, compounds, intermetallic compounds, alloys or combination thereof in stoichiometric proportions to substantially form the boride and oxide phases, and (d) shaping and heating the admixture to form the reaction sintered body, the heating being done in nonreactive atmosphere and at temperature at which the reaction and sintering occurs between the reactants to substantially form the boride and oxide phases.

Claim 20

A reaction sintered oxide-boride ceramic body having not greater than 5% open porosity and consisting essentially of a fine-grained, homogeneous, intimate interdispersion of: (a) 10-90 mole percent of boride phase or phases having a maximum grain size substantially not greater than 15 μm and being boride of one or more of the elements of Groups 3b including lanthanide and actinide series elements, 4b, 5b and 6b, and (b) 10-90 mole percent of oxide phase or phases having a maximum grain size substantially not greater than 15 μm and being oxide of one or more of the elements of Groups 3a, 4a, 3b, 4b, 5b, 6b and 8; which body is prepared by the process comprising; (c) admixing particulate reactants of maximum particle size substantially not greater than 150 μm and being elements, compounds, intermetallic compounds, alloys or combination thereof in stoichiometric proportions to substantially form the boride and oxide phases, and (d) shaping and heating the admixture to form the reaction sintered body, the heating being done in nonreactive atmosphere and at temperature at which the reaction and sintering occurs between the reactants to substantially form the boride and oxide phases.

Claim 21

A reaction sintered oxide-boride ceramic body having not greater than 5% open porosity and consisting essentially of a fine-grained, homogeneous, intimate interdispersion of: (a) 10-90 mole percent of boride phase or phases having a maximum grain size substantially not greater than 15 μm and being boride of one or more of the elements of Groups 3b including lanthanide and actinide series elements, 4b, 5b and 6b, and (b) 10-90 mole percent of oxide phase or phases having a maximum grain size substantially not greater than 15 μm and being oxide of one or more of the elements of Groups 3a, 4a, 3b, 4b, 5b, 6b and 8; which body is prepared by the process comprising; (c) admixing particulate reactants of maximum particle size substantially not greater than 150 μm and being elements, compounds, intermetallic compounds, alloys or combination thereof in stoichiometric proportions to substantially form the boride and oxide phases, and (d) shaping and heating the admixture to form the reaction sintered body, the heating being done in nonreactive atmosphere and at temperature at which the reaction and sintering occurs between the reactants to substantially form the boride and oxide phases.

Claim 22

A reaction sintered oxide-boride ceramic body having less than about 3% open porosity and consisting essentially of a fine-grained, homogeneous, intimate interdispersion of: (a) 10-90 mole percent of boride phase or phases having a maximum grain size substantially not greater than 15 μm and being boride of one or more of the elements of Groups 3b including lanthanide and actinide series elements, 4b, 5b and 6b, and (b) 10-90 mole percent of oxide phase or phases having a maximum grain size substantially not greater than 15 μm and being oxide of one or more of the elements of Groups 3a, 4a, 3b, 4b, 5b, 6b and 8; which body is prepared by the process comprising; (c) admixing particulate reactants of maximum particle size substantially not greater than 150 μm and being elements, compounds, intermetallic compounds, alloys or combination thereof in stoichiometric proportions to substantially form the boride and oxide phases, and (d) shaping and heating the admixture to form the reaction sintered body, the heating being done in nonreactive atmosphere and at temperature at which the reaction and sintering occurs between the reactants to substantially form the boride and oxide phases.

Claim 23

A reaction sintered oxide-boride ceramic body having less than about 3% open porosity and consisting essentially of a fine-grained, homogeneous, intimate interdispersion of: (a) 10-90 mole percent of boride phase or phases having a maximum grain size substantially not greater than 15 μm and being boride of one or more of the elements of Groups 3b including lanthanide and actinide series elements, 4b, 5b and 6b, and (b) 10-90 mole percent of oxide phase or phases having a maximum grain size substantially not greater than 15 μm and being oxide of one or more of the elements of Groups 3a, 4a, 3b, 4b, 5b, 6b and 8; which body is prepared by the process comprising; (c) admixing particulate reactants of maximum particle size substantially not greater than 150 μm and being elements, compounds, intermetallic compounds, alloys or combination thereof in stoichiometric proportions to substantially form the boride and oxide phases, and (d) shaping and heating the admixture to form the reaction sintered body, the heating being done in nonreactive atmosphere and at temperature at which the reaction and sintering occurs between the reactants to substantially form the boride and oxide phases.

Claim 24

The body of claim 17 further having Rockwell A hardness of greater than 90.

Claim 25

The body of claim 18 further having Rockwell A hardness of greater than 90.

Claim 26

The body of claim 19 further having Rockwell A hardness of greater than 90.

Claim 27

A cutting tool tip formed of the body of claim 1.

Claim 28

A cutting tool tip formed of the body of claim 17.