Halogenated ethylene-carbon monoxide interpolymers
Assignee: Dow Chemical Co
•
Filing: 1986-04-30
•
Granted: 1987-08-18
•
Expires: 2006-04-30
Abstract
Abstract Halogenated interpolymers of ethylene and carbon monoxide. The halogenated interpolymer is prepared by (a) preparing a mixture of a liquid medium and a backbone polymer having interpolymerized therein ethylene and carbon monoxide, (b) contacting the backbone polymer in the mixture with halogen at conditions effective to react the halogen only with carbon atoms in the alpha position with respect to the carbonyl groups in the backbone polymer, and (c) recovering the halogenated polymer of step (b). The halogenated interpolymer is useful in molding films and articles therefrom and as a plasticizer in polyvinyl chloride resins. In a preferred embodiment, the backbone polymer has a carbon monoxide content of about 8-20 wt. percent and the halogenated interpolymer has a halide content of about 10-24 wt. percent.
Inventors
- 👤 Mary L. N. White
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 05:52
CPC Classifications
C; C08; C08G; C08G67/00; C08G67/02
Claims Analysis
Total Claims: 42
Claim 1
Independent Claim
30 words
A halogenated ethylene-carbon monoxide interpolymer, consisting essentially of: a backbone of interpolymerized ethylene and carbon monoxide; and halogen substituted substantially only at carbon atoms adjacent carbonyl groups in said backbone.
Claim 2
Dependent Claim
30 words
A halogenated ethylene-carbon monoxide interpolymer, consisting essentially of: a backbone of interpolymerized ethylene and carbon monoxide; and halogen substituted substantially only at carbon atoms adjacent carbonyl groups in said backbone.
Claim 3
Dependent Claim
36 words
The halogenated interpolymer of claim 1, wherein said backbone polymer consists essentially of from about 55 to about 99 percent interpolymerized ethylene and at least about 1 percent interpolymerized carbon monoxide, by weight of said backbone.
Claim 4
Dependent Claim
49 words
The halogenated interpolymer of claim 1, wherein said backbone further consists essentially of additional interpolymerized monomer selected from the group consisting of: α-olefins having from 3 to 12 carbon atoms, α,β-ethylenically unsaturated carboxylic acids and alkyl esters, amides and nitriles thereof, alkenyl esters of carboxylic acids, and combinations thereof.
Claim 5
Dependent Claim
28 words
The halogenated inte claim 1, wherein the halogenated interpolymer consists essentially of from about 3 to about 40 percent of said halogen by weight of the halogenated interpolymer.
Claim 6
Dependent Claim
18 words
The halogenated interpolymer of claim 1, wherein said halogenated interpolymer is substantially soluble in dioxane, tetrahydrofuran, or 1,1,1-trichloroethane.
Claim 7
Dependent Claim
73 words
A halogenated ethylene-carbon monoxide interpolymer, consisting essentially of: a backbone of from about 55 to about 99 percent interpolymerized ethylene and at least about 1 percent interpolymerized carbon monoxide, by weight of said backbone; and from about 3 to about 40 percent by weight of the halogenated interpolymer, of halogen substituted substantially only at carbon atoms adjacent carbonyl groups in said backbone, said halogenated interpolymer being substantially soluble in dioxane, tetrahydrofuran or 1,1,1-trichloroethane.
Claim 8
Dependent Claim
73 words
A halogenated ethylene-carbon monoxide interpolymer, consisting essentially of: a backbone of from about 55 to about 99 percent interpolymerized ethylene and at least about 1 percent interpolymerized carbon monoxide, by weight of said backbone; and from about 3 to about 40 percent by weight of the halogenated interpolymer, of halogen substituted substantially only at carbon atoms adjacent carbonyl groups in said backbone, said halogenated interpolymer being substantially soluble in dioxane, tetrahydrofuran or 1,1,1-trichloroethane.
Claim 9
Dependent Claim
49 words
The halogenated interpolymer of claim 6, wherein said backbone further consists essentially of additional interpolymerized monomer selected from the group consisting of: α-olefins having 3 to 12 carbon atoms, α, β-ethylenically unsaturated carboxylic acids and alkyl esters, amides and nitriles thereof, alkenyl esters of carboxylic acids, and combinations thereof.
Claim 10
Dependent Claim
36 words
The halogenated interpolymer of claim 6, wherein said backbone consists essentially of from about 65 to about 97 percent by weight interpolymerized ethylene and from about 3 to about 35 percent by weight interpolymerized carbon monoxide.
Claim 11
Dependent Claim
11 words
The halogenated interpolymer of claim 6, wherein said halogen is chlorine.
Claim 12
Dependent Claim
75 words
A halogenated ethylene-carbon monoxide interpolymer, consisting essentially of: a backbone of from about 65 to about 97 percent interpolymerized ethylene, and from about 3 to about 35 percent interpolymerized carbon monoxide, by weight of said backbone; and from about 3 to about 40 percent by weight of the halogenated interpolymer of chlorine substituted substantially only at carbon atoms adjacent carbonyl groups in said backbone, said halogenated interpolymer being substantially soluble in dioxane, tetrahydrofuran or 1,1,1-trichloroethane.
Claim 13
Dependent Claim
75 words
A halogenated ethylene-carbon monoxide interpolymer, consisting essentially of: a backbone of from about 65 to about 97 percent interpolymerized ethylene, and from about 3 to about 35 percent interpolymerized carbon monoxide, by weight of said backbone; and from about 3 to about 40 percent by weight of the halogenated interpolymer of chlorine substituted substantially only at carbon atoms adjacent carbonyl groups in said backbone, said halogenated interpolymer being substantially soluble in dioxane, tetrahydrofuran or 1,1,1-trichloroethane.
Claim 14
Dependent Claim
36 words
The halogenated interpolymer of claim 10, wherein said backbone consists essentially of from about 80 to about 92 percent by weight interpolymerized ethylene and from about 8 to about 20 percent by weight interpolymerized carbon monoxide.
Claim 15
Dependent Claim
61 words
The halogenated interpolymer of claim 10, wherein said backbone further consists essentially of from about 0 to about 27 percent by weight of said backbone of additional interpolymerized monomer selected from the group consisting of: α-olefin having 3 to 12 carbon atoms, α,β-ethylenically unsaturated carboxylic acids and alkyl esters, amides and nitriles thereof, alkenyl esters of carboxylic acids, and combinations thereof.
Claim 16
Dependent Claim
25 words
The halogenated interolymer of claim 10, wherein the halogenated interpolymer consists essentially of from about 10 to about 24 percent by weight of said chlorine.
Claim 17
Dependent Claim
102 words
A halogenated ethylene-carbon monoxide interpolymer prepared by a process comprising the steps of: (a) preparing a mixture which includes: (i) a backbone polymer having interpolymerized therein ethylene and carbon monoxide; (ii) an ionic halogenation catalyst selected from the group consisting of: Lewis acids and Lewis bases; and (iii) a liquid medium, said catalyst and halogen being at least partially soluble in said liquid medium and substantially nonreactive therewith; (b) contacting said backbone polymer in said mixture with halogen in substantial absence of halogen free radicals to react said halogen with said backbone polymer; and (c) recovering said halogenated polymer from step (b).
Claim 18
Dependent Claim
102 words
A halogenated ethylene-carbon monoxide interpolymer prepared by a process comprising the steps of: (a) preparing a mixture which includes: (i) a backbone polymer having interpolymerized therein ethylene and carbon monoxide; (ii) an ionic halogenation catalyst selected from the group consisting of: Lewis acids and Lewis bases; and (iii) a liquid medium, said catalyst and halogen being at least partially soluble in said liquid medium and substantially nonreactive therewith; (b) contacting said backbone polymer in said mixture with halogen in substantial absence of halogen free radicals to react said halogen with said backbone polymer; and (c) recovering said halogenated polymer from step (b).
Claim 19
Dependent Claim
35 words
The halogenated interpolymer of claim 14, wherein said backbone polymer comprises, by weight of said backbone polymer, from about 55 to about 99 percent interpolymerized ethylene and at least about 1 percent interpolymerized carbon monoxide.
Claim 20
Dependent Claim
48 words
The halogenated interpolymer of claim 14, wherein said backbone polymer further comprises additional interpolymerized monomer selected from the group consisting of: α-olefins having from 3 to 12 carbon atoms, α,β-ethylenically unsaturated carboxylic acids and alkyl esters, amides, and nitriles thereof, alkenyl esters of carboxylic acids, and combinations thereof.
Claim 21
Dependent Claim
59 words
The halogenated interpolymer of claim 14, wherein said halogenation catalyst is initially present in said mixture in an amount of from about 0.1 to about 1 percent by weight of said backbone polymer and said catalyst is selected from the group consisting of: hydrogen halides, aluminum trihalides, boron trihalides, phosphorus trihalides, phosphorus oxyhalides, aromatic sulfonic acids, and combinations thereof.
Claim 22
Dependent Claim
11 words
The halogenated interpolymer of claim 14, wherein said halogen is chlorine.
Claim 23
Dependent Claim
84 words
The halogenated interpolymer of claim 14, wherein said liquid medium is present in an amount sufficient to provide a concentration of said backbone polymer of from about 1 to about 25 g per 100 ml of said mixture prior to said halogenation, and said halogen contact with said backbone polymer in said mixture is at a halogen rate of from about 0.1 to about 10 g per minute per 1000 g of said mixture for a period of time less than about 60 minutes.
Claim 24
Dependent Claim
30 words
The halogenated interpolymer of claim 14, wherein said preparation process further comprises the step of: (d) exposing said recovered halogenated polymer to conditions effective to substantially cross-link said halogenated polymer.
Claim 25
Dependent Claim
113 words
A plasticized polvinyl halide composition, comprising: (a) a polyvinyl halide resin; and (b) blended therewith, from about 3 to about 2000 parts by weight of a halogenated ethylene-carbon monoxide interpolymer per 100 parts by weight of said polyvinyl halide resin, said halogenated interpolymer consisting essentially of: (i) a backbone of from about 55 to about 99 percent interpolymerized ethylene and at least about 1 percent interpolymerized carbon monoxide, by weight of said backbone; and (ii) from about 3 to about 40 percent by weight of said halogenated interpolymer, of halogen substituted substantially only at carbon atoms adjacent carbonyl groups in said backbone, said halogenated interpolymer being substantially soluble in dioxane, tetrahydrofuran or 1,1,1-trichloroethane.
Claim 26
Dependent Claim
113 words
A plasticized polvinyl halide composition, comprising: (a) a polyvinyl halide resin; and (b) blended therewith, from about 3 to about 2000 parts by weight of a halogenated ethylene-carbon monoxide interpolymer per 100 parts by weight of said polyvinyl halide resin, said halogenated interpolymer consisting essentially of: (i) a backbone of from about 55 to about 99 percent interpolymerized ethylene and at least about 1 percent interpolymerized carbon monoxide, by weight of said backbone; and (ii) from about 3 to about 40 percent by weight of said halogenated interpolymer, of halogen substituted substantially only at carbon atoms adjacent carbonyl groups in said backbone, said halogenated interpolymer being substantially soluble in dioxane, tetrahydrofuran or 1,1,1-trichloroethane.
Claim 27
Dependent Claim
15 words
The composition of claim 21, wherein said polyvinyl halide resin includes a polyvinyl chloride resin.
Claim 28
Dependent Claim
16 words
The composition of claim 22, wherein said halogenated ethylene-carbon monoxide interpolymer is chlorinated ethylene-carbon monoxide interpolymer.
Claim 29
Dependent Claim
34 words
The composition of claim 21, wherein said composition comprises from about 3 to about 2000 parts by weight of said halogenated ethylene-carbon monoxide interpolymer per 100 parts by weight of said polyvinyl halide resin.
Claim 30
Dependent Claim
32 words
The composition of claim 23, wherein said composition comprises from about 3 to about 18 parts by weight of said chlorinated interpolymer per 100 parts by weight of said polyvinyl chloride resin.
Claim 31
Dependent Claim
32 words
The composition of claim 23, wherein said composition comprises from about 18 to about 65 parts by weight of said chlorinated interpolymer per 100 parts by weight of said polyvinyl chloride resin.
Claim 32
Dependent Claim
32 words
The composition of claim 23, wherein said composition comprises from about 40 to about 2000 parts by weight of said chlorinated interpolymer per 100 parts by weight of said polyvinyl chloride resin.
Claim 33
Dependent Claim
47 words
The composition of claim 21, wherein said backbone further consists essentially of additional interpolymerized monomer selected from the group consisting of: α-olefins having 3 to 12 carbon atoms, α,β-ethylenically unsaturated carboxylic acids and alkyl esters, amides and nitriles thereof, alkenyl esters of carboxylic acids, and combinations thereof.
Claim 34
Dependent Claim
35 words
The composition of claim 21, wherein said backbone consists essentially of from about 65 to about 97 percent by weight interpolymerized ethylene and from about 3 to about 35 percent by weight interpolymerized carbon monoxide.
Claim 35
Dependent Claim
115 words
A plasticized polyvinyl halide composition, comprising: (a) a polyvinyl chloride resin; and (b) blended therewith, from about 3 to about 2000 parts by weight of a chlorinated ethylene-carbon monoxide interpolymer per 100 parts by weight of said polyvinyl chloride resin, said chlorinated interpolymer consisting essentially of: (i) a backbone of from about 65 to about 97 percent interpolymerized ethylene, and from about 3 to about 35 percent interpolymerized carbon monoxide, by weight of said backbone; and (ii) from about 3 to about 40 percent by weight of said chlorinated interpolymer of chlorine substituted substantially only at carbon atoms adjacent carbonyl groups in said backbone, said chlorinated interpolymer being substantially soluble in dioxane, tetrahydrofuran or 1,1,1-trichloroethane.
Claim 36
Dependent Claim
115 words
A plasticized polyvinyl halide composition, comprising: (a) a polyvinyl chloride resin; and (b) blended therewith, from about 3 to about 2000 parts by weight of a chlorinated ethylene-carbon monoxide interpolymer per 100 parts by weight of said polyvinyl chloride resin, said chlorinated interpolymer consisting essentially of: (i) a backbone of from about 65 to about 97 percent interpolymerized ethylene, and from about 3 to about 35 percent interpolymerized carbon monoxide, by weight of said backbone; and (ii) from about 3 to about 40 percent by weight of said chlorinated interpolymer of chlorine substituted substantially only at carbon atoms adjacent carbonyl groups in said backbone, said chlorinated interpolymer being substantially soluble in dioxane, tetrahydrofuran or 1,1,1-trichloroethane.
Claim 37
Dependent Claim
32 words
The composition of claim 30, wherein said composition comprises from about 3 to about 18 parts by weight of said chlorinated interpolymer per 100 parts by weight of said polyvinyl chloride resin.
Claim 38
Dependent Claim
32 words
The composition of claim 30, wherein said composition comprises from about 18 to about 65 parts by weight of said chlorinated interpolymer per 100 parts by weight of said polyvinyl chloride resin.
Claim 39
Dependent Claim
32 words
The composition of claim 30, wherein said composition comprises from about 40 to about 2000 parts by weight of said chlorinated interpolymer per 100 parts by weight of said polyvinyl chloride resin.
Claim 40
Dependent Claim
34 words
The composition of claim 30, wherein said backbone consists essentially of about 80 to about 92 percent by weight interpolymerized ethylene and from about 8 to about 20 percent by weight interpolymerized carbon monoxide.
Claim 41
Dependent Claim
59 words
The composition of claim 30, wherein said backbone further consists essentially of from 0 to about 27 percent by weight of said backbone of additional interpolymerized monomer selected from the group consisting of: α-olefin having 3 to 12 carbon atoms, α,β-ethylenically unsaturated carboxylic acids and alkyl esters, amides and nitriles thereof, alkenyl esters of carboxylic acids, and combinations thereof.
Claim 42
Dependent Claim
24 words
The composition of claim 30, wherein said chlorinated interpolymer consists essentially of from about 10 to about 24 percent by weight of said chlorine.
References Cited (Backward Citations)
US2351120A
Cited
US2495284A
Cited
US2541987A
Cited
US2599501A
Cited
US3156744A
Cited
US3790460A
Cited
US3689460A
Cited
US3694412A
Cited
US3780140A
Cited
US4616072A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-08-17 | 1991-02-16 | 1991-08-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-08-17 | 1995-02-16 | 1995-08-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-08-17 | 1999-02-16 | 1999-08-18 | $7700.00 | Window Closed / Lapsed |