Structural insulating panel and method of making the panel
Assignee: Chem-Tronics Inc
•
Filing: 1986-06-20
•
Granted: 1987-08-18
•
Expires: 2006-06-20
Abstract
Abstract A structural panel having superior insulating properties which comprises a sheet of polyimide foam material having a metal layer on at least one surface, the metal layer being diffused into the foam structure, providing a superior metal-to-foam bond. The polyimide foam has excellent insulating and structural properties and is highly resistant to high temperatures and open flames. The metal layer adds considerable structural strength, since the diffusion of metal into the foam produces a three-dimensional metal structure rather than the usual planar surface film. The metal layer is applied to the foam sheet by chemical vapor deposition under conditions which improve the diffusion of the metal into the foam.
Inventors
- 👤 John C. Monsees
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 13:05
CPC Classifications
C; C08; C08J; C08J9/00; C08J9/36; C08J9/365; C23; C23C; C23C16/00; C23C16/06; C23C16/56; C08J2379/00; C08J2379/04; Y; Y10; Y10T; Y10T428/00; Y10T428/249921; Y10T428/249953; Y10T428/249955; Y10T428/249958; Y10T428/249971; Y10T428/249972; Y10T428/249987; Y10T428/24999; Y10T428/31504; Y10T428/31678; Y10T428/31681; Y10T428/31721
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
109 words
A structural insulating panel comprising: a polyimide foam sheet having surface discontinuities or interstices extending into the foam surface and constituting at least about 1 percent of the foam surface area; and a layer of metal on at least one foam surface having a substantially planar outer surface and extending into said discontinuities and interstices with the area in a plane parallel to the foam surface at a depth of from about 0.03 to 0.50 inch being substantially 50% metal and 50% polyimide; whereby said metal layer is very firmly adhesively and mechanically bonded to said foam and has a three-dimensional structure within the foam providing improved structural strength.
Claim 2
Dependent Claim
109 words
A structural insulating panel comprising: a polyimide foam sheet having surface discontinuities or interstices extending into the foam surface and constituting at least about 1 percent of the foam surface area; and a layer of metal on at least one foam surface having a substantially planar outer surface and extending into said discontinuities and interstices with the area in a plane parallel to the foam surface at a depth of from about 0.03 to 0.50 inch being substantially 50% metal and 50% polyimide; whereby said metal layer is very firmly adhesively and mechanically bonded to said foam and has a three-dimensional structure within the foam providing improved structural strength.
Claim 3
Dependent Claim
20 words
The panel according to claim 1 wherein said metal is nickel or an alloy having nickel as the primary constituent.
Claim 4
Dependent Claim
21 words
The panel according to claim 1 wherein said metal layer has an average thickness of from about 0.015 to 0.125 inch.
Claim 5
Dependent Claim
23 words
The panel according to claim 1 wherein said metal layer consists essentially of nickel and has an average thickness of about 0.06 inch.
Claim 6
Dependent Claim
30 words
The panel according to claim 1 wherein said 50 percent metal, 50 percent polyimide, layer lies at a depth of from about 0.125 to 0.250 inch below the foam surface.
Claim 7
Dependent Claim
27 words
The panel according to claim 1 further including a layer of fiberous material in contact with said surface of said foam and embedded within said metal layer.
Claim 8
Dependent Claim
38 words
The panel according to claim 1 wherein the thicknesses of said foam sheet and said metal layer are selected so as to give an average metal layer thickness of about 25 to 30 percent of the panel thickness.
Claim 9
Independent Claim
221 words
The method of making a structural insulating panel which comprises the steps of: providing a foam sheet having at least one surface with discontinuities and interstices extending into the foam surface, said discontinuities and interstices covering at least about 1 percent of the foam surface area; placing said foam sheet into a vacuum chamber and closing said chamber; reducing the pressure in said chamber; purging said chamber of air and other reactive gases; introducing into said chamber at least one gas capable of decomposition to produce at least one elemental metal; heating said chamber to a temperature above the decomposition temperature of said gas but below the degradation temperature of said foam; allowing said metal to deposit on said foam surface and diffuse into said interstices and discontinuities until the area in a plane parallel to the foam surface at a depth of from about 0.03 to 0.5 inch is substantially 50% metal and 50% resin; continuing said deposition until a metal layer having an average thickness of from about 0.001 to 0.5 inch results; and removing said sheet from said chamber; whereby a metal layer is formed on the foam surface having a substantially planar outer surface and an inner surface extending into said discontinuites and interstices so that the metal layer is firmly mechanically bonded to said foam sheet.
Claim 10
Independent Claim
221 words
The method of making a structural insulating panel which comprises the steps of: providing a foam sheet having at least one surface with discontinuities and interstices extending into the foam surface, said discontinuities and interstices covering at least about 1 percent of the foam surface area; placing said foam sheet into a vacuum chamber and closing said chamber; reducing the pressure in said chamber; purging said chamber of air and other reactive gases; introducing into said chamber at least one gas capable of decomposition to produce at least one elemental metal; heating said chamber to a temperature above the decomposition temperature of said gas but below the degradation temperature of said foam; allowing said metal to deposit on said foam surface and diffuse into said interstices and discontinuities until the area in a plane parallel to the foam surface at a depth of from about 0.03 to 0.5 inch is substantially 50% metal and 50% resin; continuing said deposition until a metal layer having an average thickness of from about 0.001 to 0.5 inch results; and removing said sheet from said chamber; whereby a metal layer is formed on the foam surface having a substantially planar outer surface and an inner surface extending into said discontinuites and interstices so that the metal layer is firmly mechanically bonded to said foam sheet.
Claim 11
Dependent Claim
12 words
The method according to claim 8 wherein said metal is predominantly nickel.
Claim 12
Dependent Claim
13 words
The method according to claim 8 wherein said gas is primarily nickel carbonyl.
Claim 13
Dependent Claim
23 words
The method according to claim 8 wherein said metal layer is formed to an average thickness of from about 0.015 to 0.125 inch.
Claim 14
Dependent Claim
24 words
The method according to claim 8 wherein said metal layer is predominantly nickel and is formed to an average thickness of about 0.06 inch.
Claim 15
Dependent Claim
38 words
The method according to claim 8 wherein the thicknesses of said foam sheet and said metal layer are selected so as to give an average metal layer thickness of about 25 to 30 percent of the panel thickness.
Claim 16
Dependent Claim
41 words
The method according to claim 8 further including the steps of laying a sheet of fiberous material on said foam surface prior to closing said chamber and of continuing metal deposition until said fiberous sheet is embedded in said metal layer.
Claim 17
Dependent Claim
35 words
The method according to claim 8 further including the step of heating said chamber to a temperature of from about 200° to 280° C. for about 10 to 60 minutes prior to introducing said gas.
Claim 18
Dependent Claim
23 words
The method according to claim 8 further including the step of purging said chamber with an inert gas prior to introducing said gas.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-08-17 | 1991-02-16 | 1991-08-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-08-17 | 1995-02-16 | 1995-08-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-08-17 | 1999-02-16 | 1999-08-18 | $7700.00 | Window Closed / Lapsed |