Method of preparing interfacings of heat sinks with electrical devices
Assignee: Bergquist Co Inc
•
Filing: 1986-01-21
•
Granted: 1987-08-11
•
Expires: 2006-01-21
Abstract
Abstract A relatively thin broad-area dielectric interfacing composed of dual filled layers of compliant silicone rubber in sandwiching relation to a porous glass-cloth carrier, one of the layers being pre-vulcanized and the other being subsequently cured and bonded in place once the composite interfacing has been applied to heat-sink surfaces adapted for abutment with the device for the intended heat transfer. The soft rubber interfacing offers good dielectric and insulating and voltage-breakdown characteristics even when well loaded with thermally-conductive oxides, and intimate voidless surface contacts and high-quality thermal matching are fostered both along abutting compliant surfaces of the pre-cured portion of the interfacing and along fully bonded surfaces of the portion cured in situ. Processing which makes such interfacing eminently practical and particularly advantageous to the user includes initial application of filled uncured rubber to one side of a sheet of the porous carrier, followed by its vulcanization and then by application of a further uncured amount to the opposite side of the carrier. A protective peel-off plastic covering is used to facilitate handling and release-cutting of desired smaller wafer configurations from the large area composite. Uncured sides of the smaller peeled wafers are then mated with appropriate parts of heat sinks and cured.
Inventors
- 👤 Herbert J. Fick
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 06:24
CPC Classifications
H; H10; H10W; H10W40/00; H10W40/20; H10W40/25; H10W40/251; H10W40/60; H10W40/611; H10W40/231; H10W40/235; Y; Y10; Y10S; Y10S156/00; Y10S156/918; Y10S156/919; Y10S156/922; Y10T; Y10T156/00; Y10T156/10; Y10T156/1052; Y10T156/11; Y10T428/00; Y10T428/31504; Y10T428/31652; Y10T428/31663; Y10T442/00; Y10T442/10; Y10T442/102; Y10T442/133
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
292 words
The method of preparing an interfacing for conducting heat between an electronic device or the like and a heat sink having complementary surfaces disposed to confront and communicate heat therefrom, comprising the steps of: (a) producing a first thin and substantially amorphous layer of heat-conducting material having compliant properties of an elastomeric substance when cured; (b) curing said layer to a dry and relatively firm state, applying and sticking to one side of said first layer a second thin layer of uncured heat-conducting material in a substantially amorphous condition; (c) temporarily covering the exposed side of said second layer while it is in an uncured condition with a strippable liner removable to expose the material thereof for attachment to and subsequent curing and bonding with said complementary surfaces, said uncured material being one which tends to adhere to said first layer and said complementary surfaces and being controllably curable to form a permanent bond with both said one side of said first layer and said complementary surfaces of the heat sink; (d) said steps of producing a first and second layer are carried out using a material consisting essentially of silicone rubber having relatively minute particles of heat-conducting material distributed therethrough and by applying the material in the substantially amorphous state to one side of a relatively thin carrier consisting essentially of glass fibers before curing it to form the first layer; and (e) said method further comprising the steps of stripping the liner away to expose the uncured material of the second layer, pressing the exposed uncured material of the second layer into substantially voidless engagement with the said complementary surfaces of a heat sink, and, while so pressing the material of the said second layer, curing that material in place.
Claim 2
Independent Claim
292 words
The method of preparing an interfacing for conducting heat between an electronic device or the like and a heat sink having complementary surfaces disposed to confront and communicate heat therefrom, comprising the steps of: (a) producing a first thin and substantially amorphous layer of heat-conducting material having compliant properties of an elastomeric substance when cured; (b) curing said layer to a dry and relatively firm state, applying and sticking to one side of said first layer a second thin layer of uncured heat-conducting material in a substantially amorphous condition; (c) temporarily covering the exposed side of said second layer while it is in an uncured condition with a strippable liner removable to expose the material thereof for attachment to and subsequent curing and bonding with said complementary surfaces, said uncured material being one which tends to adhere to said first layer and said complementary surfaces and being controllably curable to form a permanent bond with both said one side of said first layer and said complementary surfaces of the heat sink; (d) said steps of producing a first and second layer are carried out using a material consisting essentially of silicone rubber having relatively minute particles of heat-conducting material distributed therethrough and by applying the material in the substantially amorphous state to one side of a relatively thin carrier consisting essentially of glass fibers before curing it to form the first layer; and (e) said method further comprising the steps of stripping the liner away to expose the uncured material of the second layer, pressing the exposed uncured material of the second layer into substantially voidless engagement with the said complementary surfaces of a heat sink, and, while so pressing the material of the said second layer, curing that material in place.
Claim 3
Dependent Claim
61 words
The method of preparing an interfacing as set forth in claim 1 wherein said steps of producing a first thin layer and curing same is carried out using a material consisting essentially of silicone rubber having relatively minute particles of heat-conducting material distributed therethrough, and wherein said first thin layer is produced with a thickness of the order of 21/2-3 mils.
Claim 4
Dependent Claim
53 words
The method of preparing an interfacing as set forth in claim 2 wherein the step of applying and sticking the second thin layer is carried out using substantially the same material as that of the first layer and producing a thickness thereof which is substantially the same as that of the first layer.
Claim 5
Dependent Claim
61 words
The method of preparing an interfacing as set forth in claim 1 wherein said steps of producing a first thin layer and curing same are carried out by applying the heat-conducting material in the substantially amorphous state to one side of a relatively thin carrier and curing the material into bonded relation with the said one side of the first layer.
Claim 6
Dependent Claim
27 words
The method of preparing an interfacing as set forth in claim 4 wherein said steps are performed using a thin porous carrier consisting essentially of glass fibers.
Claim 7
Dependent Claim
54 words
The method of preparing an interfacing as set forth in claim 5 wherein said steps are performed using a carrier in the form of a woven fabric and involves causing some of the silicone rubber and minute particles to penetrate the fabric and become cured along the said one side of the first layer.
Claim 8
Dependent Claim
60 words
The method of preparing an interfacng as set forth in claim 1 in which the steps of applying said second layer and temporarily covering said second layer are performed using layers and a liner of relatively large area, and comprising the further step of die-cutting a plurality of relatively small-area interfacing wafers therefrom while the liner is protectively in place.
Claim 9
Dependent Claim
31 words
The method of preparing an interfacing as set forth in claim 1 wherein the said further step is performed using a strippable liner of material selected from high-density polyethylene and polypropylene.
Claim 10
Dependent Claim
39 words
The method of preparing an interfacing as set forth in claim 1 wherein each of the curings of the first and second layers is carried out using a peroxide as a curing agent for up to about thirty minutes.
References Cited (Backward Citations)
CA600823A
Cited
US25184A
Cited
US1843432A
Cited
US2732318A
Cited
USRE25184E
Cited
US3187226A
Cited
US3261396A
Cited
US3229757A
Cited
US3611046A
Cited
US3391242A
Cited
US3611065A
Cited
US3694182A
Cited
US4092697A
Cited
US4151547A
Cited
US4299715A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-08-10 | 1991-02-09 | 1991-08-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-08-10 | 1995-02-09 | 1995-08-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-08-10 | 1999-02-09 | 1999-08-11 | $7700.00 | Window Closed / Lapsed |