Abstract
Abstract There are provided carbon membranes for use in separation processes. These have a very narrow range of pore sizes, with a very sharp cutoff at the upper pore size, and thus they are suited for the separation of various constituents which differ but little in their size. The membranes can be of a varied configuration: sheet form, tubular form, assymetrical membranes and the like. There is provided a process for the production of such membranes by controlled pyrolysis of a carbon containing percursor material.
Inventors
- 👤 Abraham Soffer
- 👤 Jacob E. Koresh
- 👤 Shlomo Saggy
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 08:08
CPC Classifications
B; B01; B01D; B01D69/00; B01D69/02; B01D67/00; B01D67/0039; B01D67/0067; B01D67/0081; B01D67/0083; B01D71/00; B01D71/02; B01D71/021; C; C04; C04B; C04B35/00; C04B35/515; C04B35/52; C04B38/00; C04B38/0022; B01D2325/00; B01D2325/02; B01D2325/0283; B01D2325/20; C04B2111/00; C04B2111/00474; C04B2111/00793; C04B2111/00801
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
111 words
A carbon membrane for separating two gases having different size molecules in a range of 2.5 Å to 5.0 Å, wherein the molecules of each gas differ from one another in size by an amount not greater than 10%, said membrane having pores of a preselected size which also is in the range of 2.5 Å to 5.0 Å and which is intermediate the molecule sizes of the two gases to be separated, and said membrane having a pore size distribution which is such that the membrane has no significant number of pores which are 10% or greater in size than the smaller of the molecule sizes of the two gases.
Claim 2
Dependent Claim
111 words
A carbon membrane for separating two gases having different size molecules in a range of 2.5 Å to 5.0 Å, wherein the molecules of each gas differ from one another in size by an amount not greater than 10%, said membrane having pores of a preselected size which also is in the range of 2.5 Å to 5.0 Å and which is intermediate the molecule sizes of the two gases to be separated, and said membrane having a pore size distribution which is such that the membrane has no significant number of pores which are 10% or greater in size than the smaller of the molecule sizes of the two gases.
Claim 3
Dependent Claim
21 words
A carbon membrane according to claim 1, wherein the membrane is in sheet form and of from 1μ to 300μ thickness.
Claim 4
Dependent Claim
35 words
Carbon membranes according to claim 1, in the form of tubular fibers, of from 5μ to 1 mm diameter and with a wall thickness of 1μ to 300μ, depending on the diameter, of desired length.
Claim 5
Dependent Claim
21 words
A separation module of the shell and tube type comprising a plurality of hollow carbon fibers as claimed in claim 3.
Claim 6
Dependent Claim
36 words
A carbon membrane according to claim 1, wherein the carbon membrane is of assymetrical construction, and the active carbon membrane is 50μ to 300μ in thickness and supported by a porous support of adequate mechanical strength.
Claim 7
Dependent Claim
25 words
A separation module for the separation of gaseous mixtures comprising a plurallity of assymmetrical carbon membranes according to claim 5, in a membrane stack configuration.
Claim 8
Dependent Claim
31 words
A carbon membrane according to claim 1, wherein the carbon membrane is the product of pyrolysis of a carbon containing precursor at a temperature of from 250° C. to 2500° C.
Claim 9
Dependent Claim
32 words
A carbon membrane according to claim 1, wherein the carbon membrane is the product of pyrolysis of a suitable precursor and subsequent pore size manipulation by heat treatment or by controlled oxidation.
Claim 10
Dependent Claim
40 words
A process for the production of a carbon membrane for a separation process as claimed in claim 1, which comprises pyrolyzing under an inert atmosphere a mechanically heat stable carbon containing precursor material having the configuration of the final product.
Claim 11
Dependent Claim
20 words
A process according to claim 9 wherein the pyrolysis is effected at a temperature between 250° C. and 2500° C.
Claim 12
Dependent Claim
54 words
A process according to claim 9, wherein the precursor is cellulose, a cellulose derivative, a thermosetting polymer or peach tar mesophase having the configuration of the desired product, with the pore size range of the precursor being determined by the temperature of pyrolysis and being in the range of 2.5 Å to 5.0 Å.
References Cited (Backward Citations)
US3516791A
Cited
US3511031A
Cited
US3814642A
Cited
US3840649A
Cited
US4032430A
Cited
US4046709A
Cited
US4261832A
Cited
US4175153A
Cited
US4439349A
Cited
US4402928A
Cited
US4424145A
Cited
US4401588A
Cited
JPH118009A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-08-10 | 1991-02-09 | 1991-08-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-08-10 | 1995-02-09 | 1995-08-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-08-10 | 1999-02-09 | 1999-08-11 | $7700.00 | Window Closed / Lapsed |