Mesoporous carbons
Assignee: Individual
•
Filing: 1981-04-28
•
Granted: 1984-03-27
•
Expires: 2001-04-28
Abstract
Abstract The disclosed invention relates to mesoporous carbon which is useful as a catalyst or adsorbent for large organic molecules. Said carbon composition comprises a regular assembly of carbon particles thus allowing an accurate pre-determination of the size and size disbtribution of the pores and creating less tortuous pathways of interconnected pores. A method of preparation of said mesoporous carbon has been disclosed.
Inventors
- 👤 Douglas H. Everett
- 👤 Stephen G. Bligh
- 👤 Fernando Rojas
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 21:18
CPC Classifications
B; B01; B01J; B01J37/00; B01J37/0009; B01J37/0018; B01J20/00; B01J20/02; B01J20/20; B01J21/00; B01J21/18; C; C01; C01B; C01B32/00; C01B32/05
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
119 words
An adsorbant carbon comprising a form-stable assembly of a family of contiguous carbon particles wherein the surfaces of adjacent contiguous particles define interstitial pores characterised in that (a) the maximum diameters of at least 90% by number of the particles of the family lie in the range 8 to 3000 nm, (b) the root mean square deviation of the maximum diameters of the particles of the family is less than 15% and Ser. No. 336,396 - Everett et al. (c) in at least one section of the adsorbant carbon, particles are cubic or hexagonal close packed to an extent that the volume of interstitial pores in said section is from 18 to 40% of the volume of said section.
Claim 2
Dependent Claim
119 words
An adsorbant carbon comprising a form-stable assembly of a family of contiguous carbon particles wherein the surfaces of adjacent contiguous particles define interstitial pores characterised in that (a) the maximum diameters of at least 90% by number of the particles of the family lie in the range 8 to 3000 nm, (b) the root mean square deviation of the maximum diameters of the particles of the family is less than 15% and Ser. No. 336,396 - Everett et al. (c) in at least one section of the adsorbant carbon, particles are cubic or hexagonal close packed to an extent that the volume of interstitial pores in said section is from 18 to 40% of the volume of said section.
Claim 3
Dependent Claim
40 words
A modification of the carbon claimed in claim 1 characterised in that the assembly of particles is such that the volume of the interstitial pores in said section is from above 30 to 40% of the volume of said section.
Claim 4
Dependent Claim
88 words
A carbon as claimed in claim 1 characterised in that the assembly of carbon particles comprises one or more families of spheroidal carbon particles wherein (a) the maximum diameters of at least 90% by number of the particles of said family lie in the range 3 to 1000 nm. (b) the root mean square deviation of the maximum diameters of the particles of said family is less than 15% and the number average maximum diameter of the particles of any family differs from that of any other family.
Claim 5
Dependent Claim
17 words
A carbon as claimed in claim 1, which is substantially free from micropores in the carbon particles.
Claim 6
Independent Claim
140 words
A method for making adsorbant carbon characterised in that (a) a colloidal dispersion of a family of spheroidal particles of carbonisable organic polymer is formed in a liquid wherein the maximum diameters of at least 90% by number of the particles of the family lie in the range 10 to 3500 nm and the root mean square deviation of those maximum diameters within a family is less than 15%. (b) the particles are caused to deposit from the liquid by a packing force exerted on them, (c) the deposited particles are heated to a temperature which is below the softening point of the polymer but which is high enough to cause at least partial degradation of the polymer and thereby create a form-stable assembly of particles and (d) the form-stable assembly is heated to ensure complete carbonisation of the polymer.
Claim 7
Independent Claim
140 words
A method for making adsorbant carbon characterised in that (a) a colloidal dispersion of a family of spheroidal particles of carbonisable organic polymer is formed in a liquid wherein the maximum diameters of at least 90% by number of the particles of the family lie in the range 10 to 3500 nm and the root mean square deviation of those maximum diameters within a family is less than 15%. (b) the particles are caused to deposit from the liquid by a packing force exerted on them, (c) the deposited particles are heated to a temperature which is below the softening point of the polymer but which is high enough to cause at least partial degradation of the polymer and thereby create a form-stable assembly of particles and (d) the form-stable assembly is heated to ensure complete carbonisation of the polymer.
Claim 8
Dependent Claim
89 words
A method as claimed in claim 5 characterised in that the colloidal dispersion comprises one or more families of spheroidal particles of carbonisable organic polymer wherein (a) the maximum diameters of at least 90% by number of the particles of said the family lie in the range 10 to 3500 nm, (b) the root mean square deviation of those maximum diameters within said family is less than 15% and (c) the number average maximum diameter of the particles of any such family differs from that of any other family.
Claim 9
Dependent Claim
20 words
A method as claimed in claim 5 or claim 6 characterised in that the packing force is provided by centrifuging.
Claim 10
Dependent Claim
49 words
A method as claimed in claim 5 or claim 6 characterised in that the particles are caused to deposit from the liquid by evaporating the liquid and the packing force is exerted on the particles by means of the surface tension of the liquid prior to completion of evaporation.
Claim 11
Dependent Claim
44 words
A method according to claim 5 or claim 6 characterised in that the particles are caused to deposit from the liquid by forcing the liquid under hydrostatic pressure through a membrane which is imperveous to the particles whereby the particles deposit on the membrane.
Claim 12
Dependent Claim
43 words
A method as claimed in claim 5 or claim 6 characterised in that the form-stable assembly of deposited particles is heated to a temperature of from 700° to 2500° C. to close micropores in the carbon particles and to sinter together contiguous particles.
Claim 13
Dependent Claim
13 words
A metallic catalyst supported on an adsorbant carbon as claimed in claim 1.
Claim 14
Dependent Claim
15 words
A metallic catalyst supported on an adsorbant carbon prepared by the method of claim 5.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-03-27 | 1987-09-26 | 1988-03-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-03-27 | 1991-09-26 | 1992-03-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-03-27 | 1995-09-26 | 1996-03-27 | $7700.00 | Window Closed / Lapsed |