Method of manufacturing isolated semiconductor devices
Assignee: Panasonic Holdings Corp
•
Filing: 1985-07-25
•
Granted: 1987-08-11
•
Expires: 2005-07-25
Abstract
Abstract Disclosed is a method of isolating a transistor perfectly by employing a selective oxidation technology (LOCOS technology). More particularly, vertical openings are formed in the surface of {100} silicon substrate, and oxidation resistant films are formed of this surface and in part of the side walls of these openings. In succession, by etching with an etchant having an orientation anisotropy, dents are formed at high precision in the side walls of the openings. By oxidizing using the oxidation resistant film as the mask, an oxide film growing out from a dent in the opening side wall is connected with another oxide film growing out from an adjacent dent. The transistor thus formed in the active region of the silicon electrically isolated from the substrate is small in parasitic capacitance and may be formed into a small size, so that it possesses the features suited to VLSI, that is, high speed, low power consumption, and processability to high density integration.
Inventors
- 👤 Kenji Kawakita
- 👤 Noboru Nomura
- 👤 Toyoki Takemoto
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 19:03
CPC Classifications
H; H10; H10P; H10P90/00; H10P90/19; H10P90/1904; H10P90/1906; H10W; H10W10/00; H10W10/01; H10W10/011; H10W10/041; H10W10/061; H10W10/10; H10W10/181; H10W10/40; H10W10/012; H10W10/014; H10W10/13; H10W10/17; Y; Y10; Y10S; Y10S148/00; Y10S148/05; Y10S148/115; Y10S438/00; Y10S438/973
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
162 words
A method of manufacturing a semiconductor device comprising: forming a plurality of first openings in a surface of a semiconductor substrate, the crystal plane orientation of said semiconductor substrate being {100}; forming an oxidation resistant film on said surface of said semiconductor substrate and on part of the side walls of the first openings; forming an etching resistant film on the bottom of said first openings; exposing said semiconductor substrate at the side walls of said first openings by removing said oxidation resistant film on said part of said side walls; forming second openings by orientation-dependent etching of the portion of said semiconductor substrate exposed at the side walls of said first openings; forming oxide films in said second openings using said oxidation resistant film as a mask so that said oxide films are buried into adjacent second openings and are connected to each other to define active regions of said semiconductor device; and filling the first openings with an insulator material.
Claim 2
Independent Claim
162 words
A method of manufacturing a semiconductor device comprising: forming a plurality of first openings in a surface of a semiconductor substrate, the crystal plane orientation of said semiconductor substrate being {100}; forming an oxidation resistant film on said surface of said semiconductor substrate and on part of the side walls of the first openings; forming an etching resistant film on the bottom of said first openings; exposing said semiconductor substrate at the side walls of said first openings by removing said oxidation resistant film on said part of said side walls; forming second openings by orientation-dependent etching of the portion of said semiconductor substrate exposed at the side walls of said first openings; forming oxide films in said second openings using said oxidation resistant film as a mask so that said oxide films are buried into adjacent second openings and are connected to each other to define active regions of said semiconductor device; and filling the first openings with an insulator material.
Claim 3
Dependent Claim
39 words
The method of manufacturing semiconductor device as set forth in claim 1, wherein the second openings are formed by etching using an etchant having its fastest etching speed on the plane of the semiconductor substrate with orientation of {100}.
Claim 4
Dependent Claim
37 words
The method of manufacturing semiconductor device as set forth in claim 2, wherein the etchant is potassium hydroxide, mixed solution of ethylenediamine and pyrocatechol, mixed solution of hydrazine and pyrocatechol, or their aqueous solution or mixed solution.
Claim 5
Independent Claim
139 words
A method of manufacturing semiconductor device comprising: forming a plurality of first opening in a surface of a semiconductor substrate of which the crystal plane orientation is {100}; forming an oxidation resistant film on said surface of said semiconductor substrate and surfaces of said first openings including bottom surfaces thereof; exposing said semiconductor substrate at the bottom surfaces of said first openings by removing said oxidation resistant film at said bottom surfaces; forming plural second openings, differing in size from each other, by orientation-dependent etching of the portion of said semiconductor substrate exposed at said first openings; forming oxide films in said second openings using said oxidation resistant film as a mask so that the oxide films are buried in the adjoining second openings and are connected with each other; and filling said first openings with an insulator material.
Claim 6
Independent Claim
139 words
A method of manufacturing semiconductor device comprising: forming a plurality of first opening in a surface of a semiconductor substrate of which the crystal plane orientation is {100}; forming an oxidation resistant film on said surface of said semiconductor substrate and surfaces of said first openings including bottom surfaces thereof; exposing said semiconductor substrate at the bottom surfaces of said first openings by removing said oxidation resistant film at said bottom surfaces; forming plural second openings, differing in size from each other, by orientation-dependent etching of the portion of said semiconductor substrate exposed at said first openings; forming oxide films in said second openings using said oxidation resistant film as a mask so that the oxide films are buried in the adjoining second openings and are connected with each other; and filling said first openings with an insulator material.
Claim 7
Dependent Claim
38 words
The method of manufacturing semiconductor device as set forth in claim 4, wherein said second openings are formed by etching using an etchant having its fastest etching speed on the plane of semiconductor substrate with orientation of {100}.
Claim 8
Dependent Claim
54 words
The method of manufacturing a semiconductor device as set forth in claim 4, wherein said first openings are formed with different depths in respective parts of the bottoms thereof in order to form second openings differing in size from each other for the orientation-dependent etching of said semiconductor substrate exposed to said first openings.
References Cited (Backward Citations)
US4104090A
Cited
JPS5612749A
Cited
US4520552A
Cited
US4437226A
Cited
US4485551A
Cited
JPS598346A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-08-10 | 1991-02-09 | 1991-08-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-08-10 | 1995-02-09 | 1995-08-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-08-10 | 1999-02-09 | 1999-08-11 | $7700.00 | Window Closed / Lapsed |