Electrophotosensitive member having a depletion layer
Assignee: Minolta Co Ltd
•
Filing: 1985-07-10
•
Granted: 1987-07-28
•
Expires: 2005-07-10
Abstract
Abstract Though a-Si:Ge has a high absorption of long wave light, so that it can be used to improve the electrophotosensitive members in the sensitivity, and it is expected as photosensitive members for printers using semiconductor laser. However, a-Si:Ge has a tendency to prevent the movement of a carrier generated to lower a sensitivity and increase a residual potential. In the present invention, the above problems are improved by forming a depletion layer in a-Si:Ge layer to improve the mobility in forward direction of the carrier.
Inventors
- 👤 Izumi Osawa
- 👤 Isao Doi
- 👤 Toshiya Natsuhara
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 19:33
CPC Classifications
G; G03; G03G; G03G5/00; G03G5/02; G03G5/04; G03G5/08; G03G5/082; G03G5/08214; G03G5/08235
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
110 words
An electrophotosensitive member which comprises: a substrate; a first layer of amorphous silicon having a thickness of about 5 μm to 30 μm; a second photoconductive layer of amorphous silicon: germanium formed on said first layer and having a thickness of about 100 angstroms to 20 μm and including a depletion layer of amorphous silicon:germanium; and a third layer of amorphous silicon formed on said second layer and having a thickness of about 5 μm to 30 μm, said second layer being located at a distance from the surface of the substrate within a range of 20 to 80% of the total thickness of said first, second and third layers.
Claim 2
Dependent Claim
110 words
An electrophotosensitive member which comprises: a substrate; a first layer of amorphous silicon having a thickness of about 5 μm to 30 μm; a second photoconductive layer of amorphous silicon: germanium formed on said first layer and having a thickness of about 100 angstroms to 20 μm and including a depletion layer of amorphous silicon:germanium; and a third layer of amorphous silicon formed on said second layer and having a thickness of about 5 μm to 30 μm, said second layer being located at a distance from the surface of the substrate within a range of 20 to 80% of the total thickness of said first, second and third layers.
Claim 3
Dependent Claim
49 words
An electrophotosensitive member as claimed in claim 1 wherein the concentration of atoms in the second layer of amorphous silicon:germanium is represented as a Si.sub.(1-x) :Ge x H (x: numer of Ge atoms expressed by a ratio of Ge/(Si+Ge)) and its thickness d satisfies the relationship 0.07≦dx 2 ≦0.90.
Claim 4
Dependent Claim
28 words
An electrophotosensitive member as claimed in claim 2 wherein the second layer of amorphous silicon:germanium comprises a lower layer and an upper layer to form the depletion layer.
Claim 5
Dependent Claim
48 words
An electrophotosensitive member as claimed in claim 3 wherein the first layer of amorphous silicon and the lower layer of the second layer of amorphous silicon:germanium are P-type whereas the third layer of amorphous silicon and the upper layer of the second layer of amorphous silicon:germanium are N-type.
Claim 6
Dependent Claim
29 words
An electrophotosensitive member as claimed in claim 4 wherein said P-type layers include less than about 200 ppm of an impurity element in Group IIIA of the Periodic Table.
Claim 7
Dependent Claim
29 words
An electrophotosensitive member as claimed in claim 4 wherein said N-type layers include less than about 50 ppm of an impurity element in Group VA of the Periodic Table.
Claim 8
Dependent Claim
44 words
An electrophotosensitive member as claimed in claim 3 wherein the first layer of amorphous silicon and the lower layer of the second layer of amorphous silicon:germanium are N-type, whereas the third layer of amorphous silicon and the upper layer of amorphous silicon:germanium are P-type.
Claim 9
Dependent Claim
29 words
An electrophotosensitive member as claimed in claim 7 wherein said P-type layers include less than about 200 ppm of an impurity element in Group IIIA of the Periodic Table.
Claim 10
Dependent Claim
22 words
An electrophotosensitive member as claimed in claim 1 wherein the first layer further includes about 0.05 to 5 atomic % of oxygen.
Claim 11
Dependent Claim
22 words
An electrophotosensitive member as claimed in claim 1 wherein the third layer further includes less than about 35 atomic % of carbon.
Claim 12
Dependent Claim
127 words
An electrophotosensitive member which comprises a substrate having, in order, a first layer of amorphous silicon having a thickness of about 5 to 30 μm, a second photoconductive layer of amorphous silicon:germanium having a thickness of about 100 Å to 20 μm and including a depletion layer of amorphous silicon:germanium and a third layer of amorphous silicon having a thickness of about 5 to 30 μm and including carbon, said second layer of amorphous silicon:germanium being located at a distance from the substrate within 20 to 80% of the total thickness of the first, second and third layers, and having a thickness d which satisfies the relationship 0.07≦dx 2 ≦0.90 where x is the number of Ge atoms in the layer expressed by a ratio of Ge/(Si+Ge).
Claim 13
Dependent Claim
127 words
An electrophotosensitive member which comprises a substrate having, in order, a first layer of amorphous silicon having a thickness of about 5 to 30 μm, a second photoconductive layer of amorphous silicon:germanium having a thickness of about 100 Å to 20 μm and including a depletion layer of amorphous silicon:germanium and a third layer of amorphous silicon having a thickness of about 5 to 30 μm and including carbon, said second layer of amorphous silicon:germanium being located at a distance from the substrate within 20 to 80% of the total thickness of the first, second and third layers, and having a thickness d which satisfies the relationship 0.07≦dx 2 ≦0.90 where x is the number of Ge atoms in the layer expressed by a ratio of Ge/(Si+Ge).
References Cited (Backward Citations)
JPS56150753A
Cited
US4365013A
Cited
JPS57115552A
Cited
JPS58171038A
Cited
US4490450A
Cited
US4491626A
Cited
US4495262A
Cited
JPS58154850A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-07-27 | 1991-01-26 | 1991-07-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-07-27 | 1995-01-26 | 1995-07-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-07-27 | 1999-01-26 | 1999-07-28 | $7700.00 | Window Closed / Lapsed |