Pigmented, heat-sealable coating composition for application to oriented polyolefin films
Assignee: MOBILE OIL Corp A CORP OF
•
Filing: 1985-10-18
•
Granted: 1987-07-21
•
Expires: 2005-10-18
Abstract
Abstract A pigmented, heat-sealable coating composition for application to a primer-coated, oriented mono-layer or multilayer polyolefin film is provided which comprises a blend of (a) a binding and oxygen barrier effective amount of a heat-sealable polyvinylidene chloride homopolymer and/or polyvinylidene chloride copolymer containing at least about 50 weight percent copolymerized vinylidene chloride, (b) an amount of wax sufficient to result in a significant reduction in the coefficient of friction of a film to which the coating composition is applied and (c) an amount of pigment sufficient to result in a significant reduction in the light transmission property of a film to which the coating composition is applied. Oriented polyolefin films coated with the foregoing compositions possess excellent seal strength and hot tack properties, good blocking resistance, low coefficient of friction, low oxygen transmission rate and low light transmission.
Inventors
- 👤 Leland L. Liu
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 11:49
CPC Classifications
B; B32; B32B; B32B27/00; B32B27/32; B32B27/06; B32B27/08; B32B27/18; B32B27/20; B32B27/205; B32B27/30; B32B27/304; B32B3/00; B32B3/26; C; C08; C08J; C08J7/00; C08J7/04; C08J7/0427; C08J7/043; C08J7/046; C08J7/048; C08J7/052; C09; C09D; C09D127/00; C09D127/02; C09D127/04; C09D127/08; B32B2270/00; B32B2307/00; B32B2307/30; B32B2307/31; B32B2307/40; B32B2307/402; B32B2307/4026; B32B2307/50; B32B2307/514; B32B2323/00; B32B2323/10; B32B2391/00; C08J2323/00; C08J2323/02; Y; Y10; Y10T; Y10T428/00; Y10T428/249921; Y10T428/249953; Y10T428/249986; Y10T428/28; Y10T428/2813; Y10T428/2817; Y10T428/2822; Y10T428/2826; Y10T428/31504; Y10T428/31801; Y10T428/31855; Y10T428/31909; Y10T428/31913; Y10T428/3192
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
120 words
A pigmented heat-sealable coating composition for application to a primer-coated, oriented mono-layer or multi-layer polyolefin film which comprises a blend of (a) a binding and oxygen barrier heat-sealable polyvinylidene chloride homopolymer and/or polyvinylidene chloride copolymer, at a level of from about 50 to about 90 weight percent of the coating composition, containing at least about 50 weight percent copolymerized vinylidene chloride, (b) wax at a level of from about 1.5 to about 10 weight percent of the coating composition, to thereby result in a significant reduction in the coefficient of friction of a film to which the coating composition is applied and (c) pigment at a level of from about 15 to about 25 weight percent of the coating composition.
Claim 2
Dependent Claim
120 words
A pigmented heat-sealable coating composition for application to a primer-coated, oriented mono-layer or multi-layer polyolefin film which comprises a blend of (a) a binding and oxygen barrier heat-sealable polyvinylidene chloride homopolymer and/or polyvinylidene chloride copolymer, at a level of from about 50 to about 90 weight percent of the coating composition, containing at least about 50 weight percent copolymerized vinylidene chloride, (b) wax at a level of from about 1.5 to about 10 weight percent of the coating composition, to thereby result in a significant reduction in the coefficient of friction of a film to which the coating composition is applied and (c) pigment at a level of from about 15 to about 25 weight percent of the coating composition.
Claim 3
Dependent Claim
30 words
A mono-layer or multi-layer oriented polyolefin film having at least one exposed surface thereof coated with a primer, said primer-coated surface being coated with a coating composition of claim 1.
Claim 4
Dependent Claim
10 words
The oriented film of claim 2 formed from isotactic polypropylene.
Claim 5
Dependent Claim
25 words
The coating composition of claim 1 wherein polyvinylidene choloride copolymer component (a) contains from about 75% to about 92% by weight of copolymerized vinylidene chloride.
Claim 6
Dependent Claim
31 words
The coating composition of claim 1 wherein the polyvinylidene chloride homopolymer and/or copolymer component (a) is present at a level of from about 70 to about 80 percent by weight thereof.
Claim 7
Dependent Claim
30 words
The coating composition of claim 1 wherein wax component (b) is selected from the group consisting of vegetable wax, animal wax, mineral wax, artificial wax, synthetic wax and manufactured wax.
Claim 8
Dependent Claim
13 words
The coating composition of claim 1 wherein wax component (b) is carnauba wax.
Claim 9
Dependent Claim
19 words
The coating composition of claim 1 wherein polyvinylidene choloride homopolymer and/or copolymer component (a) is provided as a latex.
Claim 10
Dependent Claim
34 words
The coating composition of claim 1 wherein pigment component (c) is an inorganic material selected from the group consisting of titanium dioxide, calcium carbonate, clays, zinc oxide, antimony oxide, carbon black and iron oxides.
Claim 11
Dependent Claim
37 words
The coating composition of claim 1 wherein pigment component (c) is an organic material selected from the group consisting of toluidine red, para red, triphenylmethane pigment, xanthene pigment, thiazole pigment, quinoline pigment, anthraquinone pigment and phythalocyanine pigment.
References Cited (Backward Citations)
US2350292A
Cited
US2711996A
Cited
US2898237A
Cited
US3695923A
Cited
US4175977A
Cited
US4214039A
Cited
US4377616A
Cited
US4447494A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-07-20 | 1991-01-19 | 1991-07-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-07-20 | 1995-01-19 | 1995-07-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-07-20 | 1999-01-19 | 1999-07-21 | $7700.00 | Window Closed / Lapsed |