Abstract A hollow fiber membrane of a cellulose ester for dialysis of body liquids, such as blood, and a method are described. The membrane, which has a membrane thickness of less than 20μ, and a yield strength S b (g/filament) after heat-treatment at 80° C. for 20 hours satisfies the following formula (I): 0.90≦S.sub.b /S.sub.a ≦1.10 (I) wherein S a represents the yield strength (g/filament) of the hollow fiber membrane which is measured before heat treatment. The membrane has excellent dialysis performance while keeping excellent storage stability and excellent UFR retention during storage and during hemodialysis. A spinning solution of a cellulose ester is extruded through cyclic slits around an inner tube of a spinneret while a core solution is simultaneously extruded through the inner tube of the spinneret. The extruded spinning solution is passed through a gaseous atmosphere, entered into an aqueous coagulation bath, passed through a glycerin bath, dried, reeled onto a bobbin in the form of fibers and heat-treated on the bobbin.
A method for producing a hollow fiber membrane of a cellulose ester useful for dialysis of body liquids, such as blood, which has a membrane thickness of less than 20μ but not less than 5μ, having a suitable ultra filtration rate retention, and a yield strength S b (g/filament) after heat-treatment at 80° C. for 20 hours satisfying the following formula (I): 0.90≦S.sub.b /S.sub.a ≦1.10 (I) wherein S a represents the yield strength (g/filament) of the hollow fiber membrane measured before heat treatment, which comprises the steps of: extruding a spinning solution of a cellulose ester having a concentration of the cellulose ester of 27 to 37% by weight through cyclic slits around an inner tube of a spinneret having a double tube structure, while extruding simultaneously a core solution through the inner tube of the spinneret; passing the spinning solution extruded from the cyclic slits through a gaseous atmosphere; entering the same into an aqueous coagulation bath having a water content of 65 to 90% by weight; washing the coagulated hollow fibers with hot water of 40° to 80°; passing through a glycerin bath having a glycerin concentration of 25 to 60% by weight and a temperature of glycerin of 35° to 80°; drying with hot air of 60° to 80°; reeling up onto a bobbin; and heat-treating the reeled fibers under a humidity of 10 to 20 g-H 2 O/kg-dry air and a dry-bulb temperature of 60° to 100°.
Claim 2
Independent Claim
241 words
A method for producing a hollow fiber membrane of a cellulose ester useful for dialysis of body liquids, such as blood, which has a membrane thickness of less than 20μ but not less than 5μ, having a suitable ultra filtration rate retention, and a yield strength S b (g/filament) after heat-treatment at 80° C. for 20 hours satisfying the following formula (I): 0.90≦S.sub.b /S.sub.a ≦1.10 (I) wherein S a represents the yield strength (g/filament) of the hollow fiber membrane measured before heat treatment, which comprises the steps of: extruding a spinning solution of a cellulose ester having a concentration of the cellulose ester of 27 to 37% by weight through cyclic slits around an inner tube of a spinneret having a double tube structure, while extruding simultaneously a core solution through the inner tube of the spinneret; passing the spinning solution extruded from the cyclic slits through a gaseous atmosphere; entering the same into an aqueous coagulation bath having a water content of 65 to 90% by weight; washing the coagulated hollow fibers with hot water of 40° to 80°; passing through a glycerin bath having a glycerin concentration of 25 to 60% by weight and a temperature of glycerin of 35° to 80°; drying with hot air of 60° to 80°; reeling up onto a bobbin; and heat-treating the reeled fibers under a humidity of 10 to 20 g-H 2 O/kg-dry air and a dry-bulb temperature of 60° to 100°.
Claim 3
Dependent Claim
40 words
The method according to claim 1, wherein the starting cellulose ester is washed with a mixed solvent of acetone/water of 55:45 by volume, and wherein the cellulose ester is extracted at a ratio of not higher than 0.5% by weight.