Inorganic molding composition containing a lithogenous component

Claim 2

An inorganic, aqueous molding composition hardenable at low temperatures, which contains an alkali silicate solution, an inorganic, solid component reactive with the alkali silicate solution, and optionally proportions of fillers and auxiliary materials said composition containing 0.5-4.0 parts by weight of the inorganic solid component per part by weight of the alkali silicate solution; said solid component consisting essentially of (a) vitreous amorphous electrostatic precipitator ash having 45-60% by weight of vitreous SiO 2 , 25-35% by weight of Al 2 O 3 , and 8-11% by weight of Fe 2 O 3 , and/or (b) ground calcined bauxite, and the alkali silicate solution containing 1.2-2.5 moles of SiO 2 per mole of K 2 O and/or Na 2 O.

Claim 3

A molding composition according to claim 1, wherein the aqueous solution of alkali silicate is produced entirely or partially by dissolving amorphous disperse-pulverulent, aqueous silicic acid in an alkali hydroxide or in the aqueous solutions of the latter.

Claim 4

A molding composition according to claim 1, wherein components (a) and/or (b) are replaced, in part, with up to 10% by weight, by an oxide mixture of amorphous SiO 2 and aluminum oxide obtained as furnace filter dust.

Claim 5

A molding composition according to claim 2, wherein components (a) and/or (b) are replaced, in part, with up to 10% by weight, by an oxide mixture of amorphous SiO 2 and aluminum oxide obtained as furnace filter dust.

Claim 6

A molded part produced from a molding composition which contains an alkali silicate solution and an inorganic solid component reactive with the alkali silicate solution and optionally proportions of fillers and auxiliary agents, said composition containing 0.5-4.0 parts by weight of the inorganic solid component per part by weight of the alkali silicate solution; said solid component consisting essentially of (a) vitreous amorphous electrostatic precipitator ash having 45-60% by weight of vitreous SiO 2 , 25-35% by weight of Al 2 O 3 , and 8-11% by weight of Fe 2 O 3 and/or (b) ground calcined bauxite, and the alkali silicate solution containing 1.2-2.5 moles of SiO 2 per mole of K 2 O and/or Na 2 , wherein the solid component and the alkali silicate solution, as well as fillers are mixed together, the resultant molding composition is filled into a mold, the solidified molding composition is removed from the mold as a molded part and is optionally hardened at temperatures of at least 50°.

Claim 7

A molded part produced from a molding composition which contains an alkali silicate solution and an inorganic solid component reactive with the alkali silicate solution and optionally proportions of fillers and auxiliary agents, said composition containing 0.5-4.0 parts by weight of the inorganic solid component per part by weight of the alkali silicate solution; said solid component consisting essentially of (a) vitreous amorphous electrostatic precipitator ash having 45-60% by weight of vitreous SiO 2 , 25-35% by weight of Al 2 O 3 , and 8-11% by weight of Fe 2 O 3 and/or (b) ground calcined bauxite, and the alkali silicate solution containing 1.2-2.5 moles of SiO 2 per mole of K 2 O and/or Na 2 , wherein the solid component and the alkali silicate solution, as well as fillers are mixed together, the resultant molding composition is filled into a mold, the solidified molding composition is removed from the mold as a molded part and is optionally hardened at temperatures of at least 50°.

Claim 8

A molded part according to claim 5, wherein hardening takes place at 50°-100° C.

Claim 9

A molded part according to claim 5, wherein hardening takes place in the mold.

Claim 10

A molded part according to claim 6, wherein hardening takes place in the mold.

Claim 11

A molded part according to claim 5, wherein solidification occurs in the mold and hardening takes place after removing the molded part from the mold.

Claim 12

A molded part according to claim 6, wherein solidification occurs in the mold and hardening takes place after removing the molded part from the mold.

Claim 13

A molded part according to claim 5, wherein hardening takes place at 50°-500° C., preferably 50°-200° C., under pressure.

Claim 14

A molded part according to claim 5, wherein heating up to 500° C. is effected after solidification, as the hardening step or after a hardening step, under normal pressure or under elevated pressure.

Claim 15

A molded part according to claim 6, wherein heating up to 500° C. is effected after solidification, as the hardening step or after a hardening step, under normal pressure or under elevated pressure.

Claim 16

A molded part according to claim 7, wherein heating up to 500° C. is effected after solidification, as the hardening step or after a hardening step, under normal pressure or under elevated pressure.

Claim 17

A molded part according to claim 8, wherein heating up to 500° C. is effected after solidification, as the hardening step or after a hardening step, under normal pressure or under elevated pressure.

Claim 18

A molded part according to claim 9, wherein heating up to 500° C. is effected after solidification, as the hardening step or after a hardening step, under normal pressure or under elevated pressure.

Claim 19

A process for producing a molded part from a molding composition according to claim 5, wherein the molding composition is filled into a mold as fluid, the solidified molded composition is removed as an initially molded part and the initially molded part is hardened at temperatures of at least 50° C.