Particulate ceramic useful as a proppant
Assignee: 3M Co
•
Filing: 1984-01-18
•
Granted: 1987-07-14
•
Expires: 2004-01-18
Abstract
Abstract A two-phase ceramic particulate useful as a proppant in hydraulic fracturing operations is provided which comprises a vitreous matrix phase containing a crystalline alumina phase. The new ceramic particles are characterized by: (i) a concentration gradient of alumina which increases from very low in the center to relatively high near the surface of the particles; (ii) a fired density less than about 2.9 g/cc; and (iii) closed cell microporosity. Certain embodiments of the inventive ceramic particulate are also characterized by a Krumbein roundness of at least 0.8 and are chemically stable. The ceramic is made by a process comprising the steps of: a. mixing and pelletizing, with the aid of water, the dry raw materials including a mineral particulate such as nepheline syenite and a binder such as bentonite; b. drying the wet pelletizer product; c. mixing the dried pellets with a parting agent; and d. firing the mixture of pellets and parting agent at sufficient temperature and for sufficient time to cause vitrification to occur.
Inventors
- 👤 James L. Gibb
- 👤 James A. Laird
- 👤 George W. Lee
- 👤 William C. Whitcomb
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 22:51
CPC Classifications
E; E21; E21B; E21B43/00; E21B43/25; E21B43/26; E21B43/267; C; C04; C04B; C04B35/00; C04B35/01; C04B35/16; C04B35/18; C04B35/19; C09; C09K; C09K8/00; C09K8/60; C09K8/80; Y; Y10; Y10S; Y10S507/00; Y10S507/922; Y10S507/924; Y10T; Y10T428/00; Y10T428/29; Y10T428/2982; Y10T428/2991; Y10T428/2993; Y10T428/2996; Y10T428/2998
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
136 words
A particulate fired ceramic made from raw materials which comprise about: 50-97 parts by weight of mineral particulates; 3-50 parts by weight alumina; and at least one part by weight binder; wherein the mineral particulates comprise a ceramic mineral which melts below about 1300° C., does not substantially sublime or volatilize below 1300° C., vitrifies upon cooling, and has a fired density of less than about 2.9 grams per cubic centimeter; wherein the binder is characterized by adhering the mineral particulate and alumina powder together after pelletizing but before firing; and wherein the particulate ceramic itself is characterized by: (i) an outer region of the particles which is rich in alumina concentration as compared to the region near the center of the particles; and (ii) a fired density less than about 2.9 grams per cubic centimeter.
Claim 2
Dependent Claim
136 words
A particulate fired ceramic made from raw materials which comprise about: 50-97 parts by weight of mineral particulates; 3-50 parts by weight alumina; and at least one part by weight binder; wherein the mineral particulates comprise a ceramic mineral which melts below about 1300° C., does not substantially sublime or volatilize below 1300° C., vitrifies upon cooling, and has a fired density of less than about 2.9 grams per cubic centimeter; wherein the binder is characterized by adhering the mineral particulate and alumina powder together after pelletizing but before firing; and wherein the particulate ceramic itself is characterized by: (i) an outer region of the particles which is rich in alumina concentration as compared to the region near the center of the particles; and (ii) a fired density less than about 2.9 grams per cubic centimeter.
Claim 3
Dependent Claim
27 words
The particulate ceramic as recited in claim 1 which comprises a two-phase ceramic, having a vitreous matrix phase and a crystalline alumina phase within the vitreous phase.
Claim 4
Dependent Claim
14 words
The particulate ceramic of claim 2 in which the mineral particulate is nepheline syenite.
Claim 5
Dependent Claim
25 words
The particulate ceramic of claim 2 in which the mineral particulate comprises a mineral selected from the group consisting of basalt, feldspar, and mixtures thereof.
Claim 6
Dependent Claim
26 words
The particulate ceramic of claim 2 in which the mineral particulate comprises a mineral selected from the group consisting of shale, argillite, pyroxene, and mixtures thereof.
Claim 7
Dependent Claim
44 words
The particulate ceramic of claim 2 wherein the binder is selected from the group consisting of bentonite, sodium silicate, cellulose gum, starch, polyvinyl alcohol, polyvinyl acetate, and sodium lignosulphonate, and the amount of binder used is from about 1 to 10 parts by weight.
Claim 8
Dependent Claim
13 words
The particulate ceramic of claim 2 which is characterized by closed cell microporosity.
Claim 9
Dependent Claim
19 words
The particulate ceramic of claim 2 which is characterized by particulates having a Krumbein roundness of at least 0.8.
Claim 10
Dependent Claim
51 words
The particulate ceramic of claim 8 characterized by a crush resistance value at an applied pressure of about 69 MPa of less than about 32 weight percent particles under 0.42 mm. in largest dimension resulting from an initial sample having a particle size distribution ranging from about 0.85 to 0.42 mm.
Claim 11
Dependent Claim
26 words
The particulate ceramic as recited in claim 8 having a fracture conductivity at an applied pressure of about 69 MPa of at least about 2480 millidarcy-feet.
Claim 12
Dependent Claim
11 words
An hydraulic fracturing fluid containing the ceramic particulates of claim 8.
Claim 13
Dependent Claim
30 words
A method of hydraulic fracturing comprising pumping a fluid into a subterranean formation to open fractures therein, and placing within said fractures proppants comprising the particulate ceramic of claim 8.
Claim 14
Dependent Claim
133 words
A particulate ceramic made from raw materials comprising about: 50 to 97 parts by weight mineral particulates and at least one part by weight binder wherein the mineral particulates comprise a ceramic mineral which melts below about 1300° C., does not substantially sublime or volatilize below 1300° C., vitrifies upon cooling, and has a fired density of less than about 2.9 grams per cubic centimeter; wherein the binder is characterized by adhering the mineral particulates together after pelletizing but before firing; which raw materials are mixed and the resulting mixture formed into pellets which are fired in the presence of alumina and wherein the particulate ceramic itself is characterized by: (i) a vitreous core having an outer layer comprising alumina; and (ii) a fired density less than about 2.9 grams per cubic centimeter.
Claim 15
Dependent Claim
133 words
A particulate ceramic made from raw materials comprising about: 50 to 97 parts by weight mineral particulates and at least one part by weight binder wherein the mineral particulates comprise a ceramic mineral which melts below about 1300° C., does not substantially sublime or volatilize below 1300° C., vitrifies upon cooling, and has a fired density of less than about 2.9 grams per cubic centimeter; wherein the binder is characterized by adhering the mineral particulates together after pelletizing but before firing; which raw materials are mixed and the resulting mixture formed into pellets which are fired in the presence of alumina and wherein the particulate ceramic itself is characterized by: (i) a vitreous core having an outer layer comprising alumina; and (ii) a fired density less than about 2.9 grams per cubic centimeter.
Claim 16
Dependent Claim
28 words
The particulate ceramic of claim 13 in which the mineral particulate is selected from the group consisting of nepheline syenite, basalt, feldspar, shale, argillite, pyroxene, and mixtures thereof.
Claim 17
Dependent Claim
13 words
The particulate ceramic of claim 14 wherein the mineral particulate is nepheline syenite.
Claim 18
Dependent Claim
24 words
The particulate ceramic of claim 13 wherein the binder is selected from the group consisting of bentonite, sodium silicate, cellulose gum, and sodium lignosulphonate.
References Cited (Backward Citations)
US2566117A
Cited
US3026930A
Cited
US3155162A
Cited
US3373815A
Cited
US3376930A
Cited
US3399727A
Cited
US3486706A
Cited
US3690622A
Cited
US3929191A
Cited
US4072193A
Cited
US4068718A
Cited
DE2921336A1
Cited
US4257810A
Cited
GB2037727A
Cited
CA1117987A
Cited
EP0087852A1
Cited
US4427068A
Cited
US4623630A
Cited
US4427068B1
Cited
US4491482A
Cited
DE3223024A1
Cited
EP0101855A1
Cited
US4522731A
Cited
EP0116369A2
Cited
US4493875A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-07-13 | 1991-01-12 | 1991-07-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-07-13 | 1995-01-12 | 1995-07-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-07-13 | 1999-01-12 | 1999-07-14 | $7700.00 | Window Closed / Lapsed |