Use of uncalcined/partially calcined ingredients in the manufacture of sintered pellets useful for gas and oil well proppants

Claim 2

A composite, sintered, spherical pellet suitable for gas and oil well proppant which is prepared from materials consisting essentially of clay materials, bauxitic materials and alumina, wherein said materials include at least one uncalcined or partially calcined ingredient selected from the group consisting of clay materials, bauxitic materials and dust collector fines produced during the calcination of clay materials and bauxitic materials, and alumina, said pellet having on a dry weight basis an alumina-to-silica ratio from about 9:1 to about 1:1 and at least about 6.51 percent by weight of other than alumina and silica, said pellet having an apparent specific gravity of less than 3.30.

Claim 3

The pellet of claim 1 wherein a plurality of said pellets has a permeability to distilled water at about 75° F. (24° C.) which decreases not more than about three-fourths when the pressure applied to said pellets is increased from 2000 to 10,000 psi (140-700 kg/cm 2 ).

Claim 4

The pellet of claim 1, wherein the pellet has an alumina-to-silica dry weight basis ration from about 4:1 to about 6.5:1.

Claim 5

The pellet of claim 1, wherein the pellet has an alumina-to-silica ratio of about 5:1.

Claim 6

The pellet of claim 1, 2 or 3 wherein said pellet is of an overall size ranging from about 0.1 to 2.5 millimeters and an apparent specific gravity from about 2.6 to 3.3.

Claim 7

The pellet of claim 1, wherein the pellet is at least 85 percent by weight of Al 2 O 3 and SiO 2 .

Claim 8

The pellet of claim 1, wherein the pellet is not more than about 82 percent by weight of Al 2 O 3 .

Claim 9

The pellet of claim 1 wherein the pellet is prepared from a mixture containing on a dry weight basis from about 20 to about 40 percent calcined bauxite, from about 4 to about 10 percent dust collector fines with the remainder being calcined clay.

Claim 10

The pellet of claim 1 wherein the pellet is prepared from a mixture containing on a dry weight basis from about 5 to about 30 percent uncalcined clay with the remainder being calcined bauxite and calcined clay.

Claim 11

The pellet of claim 1 wherein the pellet is prepared from a mixture containing on a dry weight basis from about 40 to about 70 percent uncalcined clay with the remainder being calcined bauxite.

Claim 12

A sintered, spherical composite pellet suitable for use as gas and oil well proppant, said pellet having an Al 2 O 3 /SiO 2 dry weight basis ratio from about 9:1 to about 1:1, said pellet having an apparent specific gravity of less than 3.30 g/cc and at least about 6.51 percent by weight of other than Al 2 O 3 and SiO 2 , said pellet being made by a process including the steps of: (a) Forming a particulate mixture from materials consisting essentially of clay materials, bauxitic materials and alumina wherein said materials include at least one uncalcined or partially calcined ingredient selected from the group consisting of clay materials, bauxitic materials and dust collector fines produced during the calcination of clay materials and bauxitic materials and alumina, having an average particle size of less than 15 microns in a high intensity mixture and at least about 6.51 percent on a dry weight basis other than Al 2 O 3 and SiO 2 ; (b) while stirring the mixture, adding sufficient water to cause formation of composite spherical pellets from the mixture; (c) drying the pellets until less than three (3) weight percent free moisture remains in the pellets; (d) furnacing the dried pellets at a furnace temperature ranging from about 1300° C. to about 1500° C. for a period sufficient to enable recovery of sintered, spherical, composite pellets having a bulk density from about 1.35 to 1.8 grams per cubic centimeter.

Claim 13

A sintered, spherical composite pellet suitable for use as gas and oil well proppant, said pellet having an Al 2 O 3 /SiO 2 dry weight basis ratio from about 9:1 to about 1:1, said pellet having an apparent specific gravity of less than 3.30 g/cc and at least about 6.51 percent by weight of other than Al 2 O 3 and SiO 2 , said pellet being made by a process including the steps of: (a) Forming a particulate mixture from materials consisting essentially of clay materials, bauxitic materials and alumina wherein said materials include at least one uncalcined or partially calcined ingredient selected from the group consisting of clay materials, bauxitic materials and dust collector fines produced during the calcination of clay materials and bauxitic materials and alumina, having an average particle size of less than 15 microns in a high intensity mixture and at least about 6.51 percent on a dry weight basis other than Al 2 O 3 and SiO 2 ; (b) while stirring the mixture, adding sufficient water to cause formation of composite spherical pellets from the mixture; (c) drying the pellets until less than three (3) weight percent free moisture remains in the pellets; (d) furnacing the dried pellets at a furnace temperature ranging from about 1300° C. to about 1500° C. for a period sufficient to enable recovery of sintered, spherical, composite pellets having a bulk density from about 1.35 to 1.8 grams per cubic centimeter.

Claim 14

The pellet of claim 11, wherein the mixture is intensively stirred during step (b).

Claim 15

The pellet of claim 11, wherein the particulate mixture has an average particle size of less than about 10 microns.

Claim 16

The pellet of claim 11, further comprising, prior to step (c), adding from about 5 to about 15 percent by weight of pellets of any of the ingredients of the mixture of step (a).

Claim 17

The pellet of claim 11 wherein the dried pellets are furnaced for a period from about 4 to about 8 minutes.

Claim 18

The pellet of claim 15 wherein prior to step (c) there is added from about 5 to 15 percent by weight of pellets of the mixture of step (a) while continuing to stir the pellets.

Claim 19

A plurality of pellets as described in claim 1, having a bulk density of between about 1.35 and 1.80 grams per cubic centimeter wherein said pellets are of a diameter from about 0.1 to about 2.5 millimeters.

Claim 20

A process for manufacturing composite, sintered, spherical pellets suitable for use as gas and oil well proppant having an alumina-to-silica ratio on a dry-weight-basis from about 9:1 to about 1:1 and at least about 6.51 percent by weight of other than alumina and silica, said process comprising the steps of: (a) adding to a high-intensity mixer, in predetermined ratio, starting ingredients consisting essentially of clay materials, bauxitic materials and alumina wherein said materials include at least one uncalcined or partially calcined ingredient selected from the group consisting of clay materials, bauxite materials and dust collector fines produced during the calcination of clay materials and bauxitic materials, to materials consisting essentially of calcined clay materials and/or a member of the group of calcined bauxite materials, alumina or mixtures thereof, each ingredient having an average particle size of less than 15 microns; (b) stirring said starting ingredients to form a particulate mixture having an average particle size of less than 15 microns and at least about 6.51 percent on a dry weight basis of other than alumina and silica; (c) while stirring the mixture, adding sufficient water to cause formation of composite, spherical pellets from the mixture; (d) drying the pellets until less than ten (10) weight percent free moisture remains in the pellets; (e) furnacing the dried pellets at a furnace temperature of from about 1300° C. to about 1500° C. for a period sufficient to enable recovery of sintered, spherical, composite pellets having a bulk density of from about 1.35 to about 1.80 grams per cubic centimeter and at least about 6.51 percent by weight of other than alumina and silica.

Claim 21

A process for manufacturing composite, sintered, spherical pellets suitable for use as gas and oil well proppant having an alumina-to-silica ratio on a dry-weight-basis from about 9:1 to about 1:1 and at least about 6.51 percent by weight of other than alumina and silica, said process comprising the steps of: (a) adding to a high-intensity mixer, in predetermined ratio, starting ingredients consisting essentially of clay materials, bauxitic materials and alumina wherein said materials include at least one uncalcined or partially calcined ingredient selected from the group consisting of clay materials, bauxite materials and dust collector fines produced during the calcination of clay materials and bauxitic materials, to materials consisting essentially of calcined clay materials and/or a member of the group of calcined bauxite materials, alumina or mixtures thereof, each ingredient having an average particle size of less than 15 microns; (b) stirring said starting ingredients to form a particulate mixture having an average particle size of less than 15 microns and at least about 6.51 percent on a dry weight basis of other than alumina and silica; (c) while stirring the mixture, adding sufficient water to cause formation of composite, spherical pellets from the mixture; (d) drying the pellets until less than ten (10) weight percent free moisture remains in the pellets; (e) furnacing the dried pellets at a furnace temperature of from about 1300° C. to about 1500° C. for a period sufficient to enable recovery of sintered, spherical, composite pellets having a bulk density of from about 1.35 to about 1.80 grams per cubic centimeter and at least about 6.51 percent by weight of other than alumina and silica.

Claim 22

The process of claim 18 wherein the pellets are dried at a temperature between about 100° C. and about 300° C. until less than three (3) weight percent free moisture remains in the pellets.

Claim 23

The process of claim 18 wherein each ingredient of the particulate mixture has an average particle size of less than 10 microns.

Claim 24

The process of claim 18, further comprising, prior to step (d), adding from about 5 to about 15 percent of any of the ingredients given in step (a).

Claim 25

The process of claim 18, wherein the dried pellets are furnaced for a period from about 4 to about 20 minutes.

Claim 26

The process of claim 18, further comprising, prior to step (d), adding from about 5 to 15 percent of any of the ingredients given in step (a) while stirring the pellets.

Claim 27

A gas and oil well proppant comprising a plurality of composite, sintered, spherical pellets having a permeability to distilled water at about 75° F. (24° C.) which decreases not more than about three-fourths when the pressure applied to said pellets is increased from 2000 to 10,000 psi (140-700 kg/cm 2 ), said pellets being prepared from, on a dry weight basis, materials consisting essentially of clay materials, bauxitic materials and alumina wherein said materials include at least one uncalcined or partially calcined ingredient selected from the group consisting of clay materials, bauxitic materials and dust collector fines produced during calcination of clay materials and bauxitic materials, and alumina, or mixtures thereof, said pellets having an alumina-to-silica dry weight basis ratio from about 9:1 to about 1:1, said pellets having an apparent specific gravity of less than 3.30 and at least about 6.51 weight percent of other than alumina and silica and a diameter between about 0.1 and about 2.5 millimeters.

Claim 28

A gas and oil well proppant comprising a plurality of composite, sintered, spherical pellets having a permeability to distilled water at about 75° F. (24° C.) which decreases not more than about three-fourths when the pressure applied to said pellets is increased from 2000 to 10,000 psi (140-700 kg/cm 2 ), said pellets being prepared from, on a dry weight basis, materials consisting essentially of clay materials, bauxitic materials and alumina wherein said materials include at least one uncalcined or partially calcined ingredient selected from the group consisting of clay materials, bauxitic materials and dust collector fines produced during calcination of clay materials and bauxitic materials, and alumina, or mixtures thereof, said pellets having an alumina-to-silica dry weight basis ratio from about 9:1 to about 1:1, said pellets having an apparent specific gravity of less than 3.30 and at least about 6.51 weight percent of other than alumina and silica and a diameter between about 0.1 and about 2.5 millimeters.

Claim 29

The pellet of claim 1 wherein said pellet is prepared from a mixture consisting essentially of clay materials and bauxitic materials.

Claim 30

The method of claim 18 wherein fluxes are not added to the high-intensity mixer.