Adhesion of rubber to aramid cords
Assignee: Aerojet Rocketdyne Holdings Inc
•
Filing: 1986-03-03
•
Granted: 1987-07-14
•
Expires: 2006-03-03
Abstract
Abstract An aqueous composition comprising an alkaline rubbery vinyl pyridine latex, a water dispersible or soluble epoxide and a polyfunctional amine can be used to treat a polyamide reinforcing element, e.g. a poly(p-phenylene terephthalamide) cord, to increase the adhesion of the cord to rubber. Further improvements in adhesion can be obtained if the cord before treatment with the aqueous composition is exposed to a cold gas plasma of air, N 2 , He, Ne or Ar or mixture thereof at up to about 300 watts of power for a few seconds to several minutes to improve its adhesion to rubber.
Inventors
- 👤 Satish C. Sharma
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 16:30
CPC Classifications
C; C08; C08J; C08J5/00; C08J5/04; C08J5/06; B; B29; B29D; B29D30/00; B29D30/0005; B29D2030/0011; C08J2321/00; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2913; Y10T428/2933; Y10T428/2938; Y10T428/2964; Y10T428/2967; Y10T428/2969
Claims Analysis
Total Claims: 28
Claim 1
Independent Claim
238 words
A method for adhering a poly(p-phenylene terephthalamide) reinforcing element to a rubber compound which comprises (I) treating said element with a composition comprising an aqueous alkaline dispersion of from about 10 to 50%, by weight of solids comprising (a) at least one rubbery vinyl pyridine copolymer latex, (b) at least one water soluble or dispersible epoxide having an average of from about 2 to 4 epoxide groups per molecule and (c) a water soluble or dispersible polyfunctional amine curing agent selected from the group consisting of primary, secondary and tertiary amines and mixtures of said amines, (b) being used in an amount of from about 10 to 30 parts by weight per 100 parts by weight of (a) on a dry weight basis and (c) being used in an amount of from about 2 to 8 parts by weight per 100 parts by weight of (a) on a dry weight basis, heating said treated element at a temperature of from about 200° to 600° F. for from about 300 to 5 seconds to remove essentially all of the water from said composition and to provide said element with a heat cured or heat set dry adhesive in an amount of up to about 20%, total by weight (dry) based on the weight of said reinforcing element, and (II) combining said dried and heat cured adhesive containing reinforcing element with an unvulcanized vulcanizable rubber compound and vulcanizing the same.
Claim 2
Independent Claim
238 words
A method for adhering a poly(p-phenylene terephthalamide) reinforcing element to a rubber compound which comprises (I) treating said element with a composition comprising an aqueous alkaline dispersion of from about 10 to 50%, by weight of solids comprising (a) at least one rubbery vinyl pyridine copolymer latex, (b) at least one water soluble or dispersible epoxide having an average of from about 2 to 4 epoxide groups per molecule and (c) a water soluble or dispersible polyfunctional amine curing agent selected from the group consisting of primary, secondary and tertiary amines and mixtures of said amines, (b) being used in an amount of from about 10 to 30 parts by weight per 100 parts by weight of (a) on a dry weight basis and (c) being used in an amount of from about 2 to 8 parts by weight per 100 parts by weight of (a) on a dry weight basis, heating said treated element at a temperature of from about 200° to 600° F. for from about 300 to 5 seconds to remove essentially all of the water from said composition and to provide said element with a heat cured or heat set dry adhesive in an amount of up to about 20%, total by weight (dry) based on the weight of said reinforcing element, and (II) combining said dried and heat cured adhesive containing reinforcing element with an unvulcanized vulcanizable rubber compound and vulcanizing the same.
Claim 3
Dependent Claim
42 words
A method according to claim 1 where said vinyl pyridine copolymer is a copolymer of from about 50 to 95% by weight of butadiene-1,3, from 5 to 40% by weight of a vinyl pyridine and 0 to 40% by weight of styrene.
Claim 4
Dependent Claim
45 words
A method according to claim 2 where said vinyl pyridine copolymer is a terpolymer of about 70% by weight of butadiene-1,3, 15% by weight of styrene and 15% by weight of 2-vinyl pyridine, said epoxide is glycerol diglycidyl ether and said amine is tetraethylene pentamine.
Claim 5
Dependent Claim
59 words
A method according to claim 1 where said reinforcing element before treatment with said composition is treated in a cold gas plasma for from about 2 seconds to 30 minutes at from about 10 to 300 watts of power and where said gas is selected from the group consisting of air, nitrogen, helium, neon and argon and mixture thereof.
Claim 6
Dependent Claim
44 words
A method according to claim 4 where said vinyl pyridine copolymer is a terpolymer of from about 60 to 80% by weight of butadiene-1,3, from about 7 to 32% by weight of styrene and from about 4 to 22% by weight of 2-vinyl pyridine.
Claim 7
Dependent Claim
49 words
A method according to claim 5 where said vinyl pyridine copolymeer is a terpolymer of about 70% by weight of butadiene-1,3, 15% by weight of styrene and 15% by weight of 2-vinyl pyridine, said epoxide is glycerol diglycidyl ether, said amine is tetraethylene pentamine and said gas is argon.
Claim 8
Independent Claim
213 words
A method which comprises treating a poly)p-phenylene terephthalamide) reinforcing element with a composition comprising an aqueous alkaline dispersion of from about 10 to 50%, preferably from about 15 to 25%, by weight of solids comprising (a) at least one rubbery vinyl pyridine copolymer latex, (b) at least one water soluble or dispersible epoxide having an average of from about 2 to 4 epoxide groups per molecule and (c) a water soluble or dispersible polyfunctional amine curing agent selected from the group consisting of primary, secondary and tertiary amines and mixtures of said amines, (b) being used in an amount of from about 10 to 30 parts by weight per 100 parts by weight of )a) on a dry weight basis and (c) being used in an amount of from about 2 to 8 parts by weight per 100 parts by weight of (a) on a dry weight basis, heating said treated element at a temperature of from about 200° to 600° F. for from about 300 to 5 seconds to remove essentially all of the water from said composition and to provide said element with a heat cured or heat set dry adhesive in an amount of up to about 20%, total by weight (dry) based on the weight of said reinforcing element.
Claim 9
Independent Claim
213 words
A method which comprises treating a poly)p-phenylene terephthalamide) reinforcing element with a composition comprising an aqueous alkaline dispersion of from about 10 to 50%, preferably from about 15 to 25%, by weight of solids comprising (a) at least one rubbery vinyl pyridine copolymer latex, (b) at least one water soluble or dispersible epoxide having an average of from about 2 to 4 epoxide groups per molecule and (c) a water soluble or dispersible polyfunctional amine curing agent selected from the group consisting of primary, secondary and tertiary amines and mixtures of said amines, (b) being used in an amount of from about 10 to 30 parts by weight per 100 parts by weight of )a) on a dry weight basis and (c) being used in an amount of from about 2 to 8 parts by weight per 100 parts by weight of (a) on a dry weight basis, heating said treated element at a temperature of from about 200° to 600° F. for from about 300 to 5 seconds to remove essentially all of the water from said composition and to provide said element with a heat cured or heat set dry adhesive in an amount of up to about 20%, total by weight (dry) based on the weight of said reinforcing element.
Claim 10
Dependent Claim
41 words
A method according to claim 7 where said vinyl pyridine copolymer is a copolymer from about 50 to 95% by weight of butadiene-1,3, from 5 to 40% by weight of a vinyl pyridine and 0 to 40% by weight of styrene.
Claim 11
Dependent Claim
45 words
A method according to claim 8 where said vinyl pyridine copolymer is a terpolymer of about 70% by weight of butadiene-1,3, 15% by weight of styrene and 15% by weight of 2-vinyl pyridine, said epoxide is glycerol diglycidyl ether and said amine is tetraethylene pentamine.
Claim 12
Dependent Claim
59 words
A method according to claim 7 where said reinforcing element before treatment with said composition is treated in a cold gas plasma for from about 2 seconds to 30 minutes at from about 10 to 300 watts of power and where said gas is selected from the group consisting of air, nitrogen, helium, neon and argon and mixtures thereof.
Claim 13
Dependent Claim
44 words
A method according to claim 10 where said vinyl pyridine copolymer is a terpolymer of from about 60 to 80% by weight of butadiene-1,3, from about 7 to 32% by weight of styrene and from about 4 to 22% by weight of 2-vinyl pyridine.
Claim 14
Dependent Claim
49 words
A method according to claim 11 where said vinyl pyridine copolymer is a terpolymer of about 70% by weight of butadiene-1,3, 15% by weight of styrene and 15% by weight of 2-vinyl pyridine, said epoxide is glycerol diglycidyl ether, said amine is tetraethylene pentamine and said gas is argon.
Claim 15
Dependent Claim
135 words
A bonded composite material comprising a poly(p-phenylene terephthalamide) reinforcing element embedded in a vulcanized rubber, said element containing up to about 20%, by weight (dry) based on the weight of said element of a heat cured or heat set adhesive composition comprising (a) at least one rubbery vinyl pyridine copolymer, (b) at least one epoxide have an average of from 2 to 4 epoxide groups per molecule and (c) a polyfunctional amine curing agent selected from the group consisting of primary, secondary and tertiary amines and mixtures of said amines, (b) being used in an amount of from about 10 to 30 parts by weight per 100 parts by weight of (a) and (c) being used in an amount of from about 2 to 8 parts by weight per 100 parts by weight of (a).
Claim 16
Dependent Claim
135 words
A bonded composite material comprising a poly(p-phenylene terephthalamide) reinforcing element embedded in a vulcanized rubber, said element containing up to about 20%, by weight (dry) based on the weight of said element of a heat cured or heat set adhesive composition comprising (a) at least one rubbery vinyl pyridine copolymer, (b) at least one epoxide have an average of from 2 to 4 epoxide groups per molecule and (c) a polyfunctional amine curing agent selected from the group consisting of primary, secondary and tertiary amines and mixtures of said amines, (b) being used in an amount of from about 10 to 30 parts by weight per 100 parts by weight of (a) and (c) being used in an amount of from about 2 to 8 parts by weight per 100 parts by weight of (a).
Claim 17
Dependent Claim
44 words
A bonded composite material according to claim 13 where said vinyl pyridine copolymer is a copolymer of from about 50 to 95% by weight of butadiene-1,3, from 5 to 40% by weight of a vinyl pyridine and 0 to 40% by weight of styrene.
Claim 18
Dependent Claim
47 words
A bonded composite material according to claim 14 where said vinyl pyridine copolymer is a terpolymer of about 70% by weight of butadiene-1,3, 15% by weight of styrene and 15% by weight of 2-vinyl pyridine, said epoxide is glycerol diglycidyl ether and said amine is tetraethylene pentamine.
Claim 19
Dependent Claim
60 words
A bonded composite material according to claim 13 where said poly(p-phenylene terephthalamide) reinforcing element has been initially treated in a cold gas plasma for from about 2 seconds to 30 minutes at from about 10 to 300 watts of power and where said gas is selected from the group consisting of air, nitrogen, helium, neon and argon and mixtures thereof.
Claim 20
Dependent Claim
46 words
A bonded composite material according to claim 16 where said vinyl pyridine copolymer is a terpolymer of from about 60 to 80% by weight of butadiene-1,3, from about 7 to 32% by weight of styrene and from about 4 to 22% by weight of 2-vinyl pyridine.
Claim 21
Dependent Claim
51 words
A bonded composite material according to claim 17 where said vinyl pyridine copolymer is a terpolymer of about 70% by weight of butadiene-1,3, 15% by weight of styrene and 15% by weight of 2-vinyl pyridine, said epoxide is glycerol diglycidyl ether, said amine is tetraethylene pentamine and said gas is argon.
Claim 22
Dependent Claim
122 words
A poly(p-phenylene terephthalamide) reinforcing element containing up to about 20%, by weight (dry) based on the weight of said element of a heat cured or heat set adhesive composition comprising (a) at least one rubbery vinyl pyridine copolymer, (b) at least one epoxide have an average of from 2 to 4 epoxide groups per molecule and (c) a polyfunctional amine curing agent selected from the group consisting of primary, secondary and tertiary amines and mixtures of said amines, (b) being used in an amount from about 10 to 30 parts by weight per 100 parts by weight of (a) and (c) being used in an amount of from about 2 to 8 parts by weight per 100 parts by weight of (a).
Claim 23
Dependent Claim
122 words
A poly(p-phenylene terephthalamide) reinforcing element containing up to about 20%, by weight (dry) based on the weight of said element of a heat cured or heat set adhesive composition comprising (a) at least one rubbery vinyl pyridine copolymer, (b) at least one epoxide have an average of from 2 to 4 epoxide groups per molecule and (c) a polyfunctional amine curing agent selected from the group consisting of primary, secondary and tertiary amines and mixtures of said amines, (b) being used in an amount from about 10 to 30 parts by weight per 100 parts by weight of (a) and (c) being used in an amount of from about 2 to 8 parts by weight per 100 parts by weight of (a).
Claim 24
Dependent Claim
43 words
A reinforcing element according to claim 19 where said vinyl pyridine copolymer is a copolymer of from about 50 to 95% by weight of butadiene-1,3, from 5 to 40% by weight of a vinyl pyridine and 0 to 40% by weight of styrene.
Claim 25
Dependent Claim
46 words
A reinforcing element according to claim 20 where said vinyl, pyridine copolymer is a terpolymer of about 70% by weight of butadiene-1,3, 15% by weight of styrene and 15% by weight of 2-vinyl pyridine, said epoxide is glycerol diglycidyl ether and said amine is tetraethylene pentamine.
Claim 26
Dependent Claim
57 words
A reinforcing element according to claim 19 where said reinforcing element has been initially treated in a cold gas plasma for from about 2 seconds to 30 minutes at from about 10 to 300 watts of power and where said gas is selected from the group consisting of air, nitrogen, helium, neon and argon and mixtures thereof.
Claim 27
Dependent Claim
45 words
A reinforcing element according to claim 22 where said vinyl pyridine copolymer is a terpolymer of from about 60 to 80% by weight of butadiene-1,3, from about 7 to 32% by weight of styrene and from about 4 to 22% by weight of 2-vinyl pyridine.
Claim 28
Dependent Claim
50 words
A reinforcing element according to claim 23 where said vinyl pyridine copolymer is a terpolymer of about 70% by weight of butadiene-1,3, 15% by weight of styrene and 15% by weight of 2-vinyl pyridine, said epoxide is glycerol diglycidyl ether, said amine is tetraethylene pentamine and said gas is argon.
References Cited (Backward Citations)
US2817616A
Cited
GB1271883A
Cited
US3962518A
Cited
US3962011A
Cited
US3964950A
Cited
US4259404A
Cited
US4300972A
Cited
US4409055A
Cited
US4557967A
Cited
US4469748A
Cited
US4569963A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-07-13 | 1991-01-12 | 1991-07-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-07-13 | 1995-01-12 | 1995-07-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-07-13 | 1999-01-12 | 1999-07-14 | $7700.00 | Window Closed / Lapsed |