Moldable fibrous sheet and a method for manufacturing same
Assignee: INDUSTRIELLE DES BOIS ET EMBALLAGES-CIBEM SA A CORP OF FRANCE Cie
•
Filing: 1985-03-19
•
Granted: 1987-07-14
•
Expires: 2005-03-19
Abstract
Abstract A moldable fibrous sheet having a cellulose fiber and textile fiber base, said sheet having a composition comprising from 5 to 95% by weight of cellulose fibers obtained by dry shredding, from about 0.5 to 10% of textile fibers having at least two half-waves per centimeter of length, said sheet being further formed by superimposing fine sheets sewn but not rigidly connected to each other. The sheet may be molded into shaped panels through a molding cycle between 15 seconds and 3 minutes, which panels may be used in automobile construction, furnishing and packing.
Inventors
- 👤 Michel Vernois
- 👤 Francois Paugam
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 07:08
CPC Classifications
D; D04; D04H; D04H1/00; D04H1/40; D04H1/42; D04H1/425; B; B27; B27N; B27N3/00; B27N3/08; B27N3/10; D04H1/4282; D04H1/4291; D04H1/4326; D04H1/435; D04H1/4374; D04H1/4382; D04H1/43835; D04H1/70; D04H1/74; Y; Y10; Y10T; Y10T428/00; Y10T428/249921; Y10T428/249922; Y10T428/27; Y10T428/29; Y10T428/2982; Y10T442/00; Y10T442/60; Y10T442/659; Y10T442/66
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
95 words
A moldable fibrous sheet formed by superimposing fine layers, said sheet having a cellulose fiber and textile fiber base, and having a composition comprising from 5 to 95% by weight of cellulose fibers obtained by dry shredding, from about 0.5 to 10% of undulated textile fibers having at least two half-waves of undulation per centimeter of length said undulated fibers by virtue of their undulation of at least two half-waves per container of length being mechanically bonded to other fibers in the sheet, said fine layers being sewn but not rigidly connected to each other.
Claim 2
Dependent Claim
95 words
A moldable fibrous sheet formed by superimposing fine layers, said sheet having a cellulose fiber and textile fiber base, and having a composition comprising from 5 to 95% by weight of cellulose fibers obtained by dry shredding, from about 0.5 to 10% of undulated textile fibers having at least two half-waves of undulation per centimeter of length said undulated fibers by virtue of their undulation of at least two half-waves per container of length being mechanically bonded to other fibers in the sheet, said fine layers being sewn but not rigidly connected to each other.
Claim 3
Dependent Claim
27 words
The fibrous sheet according to claim 1, in which said cellulose fibers are of wood obtained by thermomechanical means and have a residual humidity less than 15%.
Claim 4
Dependent Claim
42 words
The fibrous sheet according to claim 1, in which said undulated textile fibers have a length of at least 30 mm, with at least two half waves of undulation per centimeter and are formed from a material such as polypropylene and polyester.
Claim 5
Dependent Claim
75 words
The fibrous sheet according to claim 1, comprising from 5 to 80% by weight of cellulose fibers, from 0.5 to 10% by weight of said undulated textile fibers, and, in addition, from 5 to 60% by weight of a thermoplastic material selected from the group consisting of fibrils, fibers which are shorter than said textile fibers, and a powder of a material having a softening point less than 200° C., such as polyethylene and polypropylene.
Claim 6
Dependent Claim
28 words
The fibrous sheet according to claim 1, including up to 95% by weight of said cellulose fibers and from 0.5 to 10% by weight of said textile fibers.
Claim 7
Dependent Claim
35 words
The fibrous sheet according to claim 1, in which said fine layers have each a weight of 10 to 200 g/m 2 , for a weight of said sheet of about 2 kg/m 2 .
Claim 8
Independent Claim
131 words
A method for manufacturing a fibrous sheet comprising from 5 to 95% by weight of cellulose fibers obtained by dry shredding, from about 0.5 to 10% of opened textile fibers having at least two half-waves per centimeter of length, wherein the cellulose fibers are coated with a thermosetting resin, the thus coated fibers and said opened textile fibers are mixed together, the mixture thus obtained is carded in the form of one fine layer having a weight of 10 to 200 g/m 2 , said fine layer is folded up and the successive folds of said layer are superimposed on each other so as to form said sheet whose weight is adjusted to the desired value up to about 2 kg/m 2 , then said folds are sewn to each other.
Claim 9
Independent Claim
131 words
A method for manufacturing a fibrous sheet comprising from 5 to 95% by weight of cellulose fibers obtained by dry shredding, from about 0.5 to 10% of opened textile fibers having at least two half-waves per centimeter of length, wherein the cellulose fibers are coated with a thermosetting resin, the thus coated fibers and said opened textile fibers are mixed together, the mixture thus obtained is carded in the form of one fine layer having a weight of 10 to 200 g/m 2 , said fine layer is folded up and the successive folds of said layer are superimposed on each other so as to form said sheet whose weight is adjusted to the desired value up to about 2 kg/m 2 , then said folds are sewn to each other.
Claim 10
Independent Claim
146 words
A method for manufacturing a fibrous sheet comprising from 5 to 80% by weight of cellulose fibers, from 0.5 to 10% of opened textile fibers and from 5 to 60% by weight of a thermoplastic material which is selected from the group consisting of fibrils, fibers which are shorter than said textile fibers, and a powder of a material having a softening point less than 200° C., wherein the cellulose fibers, said opened textile fibers and the thermosplastic material are mixed together, the mixture thus obtained is carded into the form of a fine layer having a weight of 10 to 200 g/m 2 , then successive folds of said layer are superimposed on each other so as to form the sheet, and the weight of the sheet is adjusted to the desired value up to about 2 kg/m 2 , then said sheet is sewn.
Claim 11
Independent Claim
146 words
A method for manufacturing a fibrous sheet comprising from 5 to 80% by weight of cellulose fibers, from 0.5 to 10% of opened textile fibers and from 5 to 60% by weight of a thermoplastic material which is selected from the group consisting of fibrils, fibers which are shorter than said textile fibers, and a powder of a material having a softening point less than 200° C., wherein the cellulose fibers, said opened textile fibers and the thermosplastic material are mixed together, the mixture thus obtained is carded into the form of a fine layer having a weight of 10 to 200 g/m 2 , then successive folds of said layer are superimposed on each other so as to form the sheet, and the weight of the sheet is adjusted to the desired value up to about 2 kg/m 2 , then said sheet is sewn.
References Cited (Backward Citations)
US4331495A
Cited
US4474846A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-07-13 | 1991-01-12 | 1991-07-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-07-13 | 1995-01-12 | 1995-07-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-07-13 | 1999-01-12 | 1999-07-14 | $7700.00 | Window Closed / Lapsed |