Process for manufacturing highly porous mineralic bodies of polymorphic structure
Assignee: INSTITUT FOR ENERGETIK- A CORP OF EAST GERMAN DEMOCRAT REPUBLIC
•
Filing: 1984-05-29
•
Granted: 1987-07-14
•
Expires: 2004-05-29
Abstract
Abstract In order to produce mineralic bodies of high porosity, usable inter alia as adsorbers, purifiers and catalyst carriers, a predominantly mineralic mass with organic admixtures--both preferably obtained from industrial waste products--are subjected to a three-phase treatment. In a first phase, the mass is heated in an inert or reducing atmosphere to a sintering temperature between about 1000° C. and 1350° C. whereby the organic constituents are carbonized and partly penetrate the consolidating mineralic structure. In a second phase, still under the same nonoxidizing atmosphere and at the sintering temperature referred to, the mineralic structure is sintered into a coherent matrix. In a third phase, with reduction of the temperature to a lower level between about 600° and 1000° C. and exposure to the atmosphere, the carbonaceous substances occluded in the mineralic skeleton are burned off to increase its porosity.
Inventors
- 👤 Reiner Kinder
- 👤 Johannes Teubel
- 👤 Herbert Schuster
- 👤 Christine Fanslau
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 23:49
CPC Classifications
C; C04; C04B; C04B38/00; C04B38/0022; Y; Y10; Y10S; Y10S264/00; Y10S264/49
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
37 words
A process for manufacturing highly porous mineralic bodies for use as adsorbents with heterogeneous pore structure which can be subjected to temperatures in excess of 1000° C. and can be regenerated many times, comprising the steps of:
Claim 2
Dependent Claim
37 words
A process for manufacturing highly porous mineralic bodies for use as adsorbents with heterogeneous pore structure which can be subjected to temperatures in excess of 1000° C. and can be regenerated many times, comprising the steps of:
Claim 3
Dependent Claim
34 words
(a) producing a mixture consisting predominantly of mineralic matter including fly ash and alkaline-earth compounds with reactive organic admixtures up to 15% in terms of the carbon content by weight of the mineralic matter;
Claim 4
Dependent Claim
34 words
(a) producing a mixture consisting predominantly of mineralic matter including fly ash and alkaline-earth compounds with reactive organic admixtures up to 15% in terms of the carbon content by weight of the mineralic matter;
Claim 5
Dependent Claim
27 words
(b) heating said mixture in a nonoxidizing atmosphere to a sintering temperature of said mineralic matter between 1000° C. and 1350° C. for 30 to 180 minutes;
Claim 6
Dependent Claim
27 words
(b) heating said mixture in a nonoxidizing atmosphere to a sintering temperature of said mineralic matter between 1000° C. and 1350° C. for 30 to 180 minutes;
Claim 7
Dependent Claim
40 words
(c) maintaining said mixture at said sintering temperature in said nonoxidizing atmosphere for a period of 15 to 120 minutes and long enough to enable consolidation of said mineralic matter into a coherent structure interpenetrated by carbonized organic matter; and
Claim 8
Dependent Claim
40 words
(c) maintaining said mixture at said sintering temperature in said nonoxidizing atmosphere for a period of 15 to 120 minutes and long enough to enable consolidation of said mineralic matter into a coherent structure interpenetrated by carbonized organic matter; and
Claim 9
Dependent Claim
52 words
(d) exposing said structure to an oxidizing atmosphere at a reduced temperature for 30 to 240 minutes of 600° C. to 1000° C. and high enough to burn off and gasify the carbonized matter with a resulting increase of the porosity of said structure so that the pore configuration thereof is heterogeneous.
Claim 10
Dependent Claim
52 words
(d) exposing said structure to an oxidizing atmosphere at a reduced temperature for 30 to 240 minutes of 600° C. to 1000° C. and high enough to burn off and gasify the carbonized matter with a resulting increase of the porosity of said structure so that the pore configuration thereof is heterogeneous.
Claim 11
Dependent Claim
15 words
A process as defined in claim 1 wherein said reduced temperature is about 800° C.
Claim 12
Dependent Claim
30 words
A process as defined in claim 2 wherein step (b) lasts for substantially 60 minutes, step (c) lasts for substantially 30 minutes and step (d) lasts for substantially 120 minutes.
Claim 13
Dependent Claim
21 words
A process as defined in claim 1 wherein an inorganic salt is added to said composite mixture prior to step (b).
Claim 14
Dependent Claim
25 words
A process as defined in claim 4 wherein said inorganic salt is selected from the group consisting of chlorides, sulfates and carbonates of alkaline earths.
Claim 15
Dependent Claim
30 words
A process as defined in claim 1 wherein said organic admixtures amount, in terms of their carbon content, to a maximum of about 15% by weight of said mineralic matter.
Claim 16
Dependent Claim
40 words
A process as defined in claim 6 wherein said organic admixtures include compounds inert with reference to said mineralic matter, present in terms of their carbon content in a maximum amount of about 10% by weight of said mineralic matter.
Claim 17
Dependent Claim
38 words
A process as defined in claim 6 wherein said organic admixtures include compounds reactive with said mineralic matter, present in terms of their carbon content in a maximum amount of about 5% by weight of said mineralic matter.
Claim 18
Dependent Claim
23 words
A process as defined in claim 8 wherein said reactive compounds are selected from the group consisting of sodium stearate, bitumen and saccharose.
Claim 19
Dependent Claim
70 words
A process as defined in claim 6 wherein said organic admixtures include a combination of compounds inert with reference to said mineralic matter, present in terms of their carbon content in a maximum amount of about 10% by weight of said mineralic matter, and compounds reactive with said mineralic matter, present in terms of their carbon content in a maximum amount of about 5% by weight of said mineralic matter.
Claim 20
Dependent Claim
31 words
A process as defined in claim 10 wherein said reactive compounds are first interacted with said mineralic matter whereupon, after drying of the products of interaction, said inert compounds are added.
Claim 21
Dependent Claim
28 words
A process as defined in claim 6 wherein said mineralic matter and said organic admixtures are compacted into pellets before being subjected to the treatment of step (b).
References Cited (Backward Citations)
US2360929A
Cited
US2691598A
Cited
US2976598A
Cited
US3176054A
Cited
GB1058615A
Cited
US3917773A
Cited
US4002587A
Cited
US4166145A
Cited
US4191720A
Cited
US4424179A
Cited
US4439382A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-07-13 | 1991-01-12 | 1991-07-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-07-13 | 1995-01-12 | 1995-07-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-07-13 | 1999-01-12 | 1999-07-14 | $7700.00 | Window Closed / Lapsed |