Solder composition

Assignee: McDonnell Douglas Corp
•
Filing: 1984-11-29
•
Granted: 1987-07-14
•
Expires: 2004-11-29
📄 Original PDF 🌐 Google Patents 🔄 Sync Now

Abstract

Abstract A test assembly for testing a high density circuit or a test board, which comprises a test head containing a mirror image circuit of the circuit to be tested on the test board, a plurality of test points on the test head circuit, the test points comprising a plurality of metal pads, and metal contacts soldered to the metal pads, the metal contacts being in the form of metal balls or flakes selected from the group consisting of brass, bronze or copper, of a size ranging from about 5 to about 30 mils. The test head is positiioned over the test board with the metal contacts on the test head in contact with corresponding test points on the high density circuit on the test board. Means are provided for connecting the circuit on the test head with a tester, thereby providing signals from the high density circuit under test through the test head circuit to the tester. A solder composition is provided which is especially adapted for soldering the metal contacts to the metal pads on the test head. Such solder composition comprises a liquid vehicle, finely divided solder metal dispersed in the vehicle, the solder metal having a particle size ranging from 40 to 70 microns, and additional metal particles dispersed in the vehicle, the additional particles being in the form of metal balls or flakes selected from the group consisting of brass, bronze and copper, the additional metal particles having a size ranging from about 5 to about 30 mils and being present in an amount ranging from about 5 to about 60% by weight of the total composition.

Inventors

  • 👤 Felix Barajas

Bibliographic Details

Application Number —
Jurisdiction US
Data Source google_patents
Last Synchronized 2026-11-02 20:34
CPC Classifications
G; G01; G01R; G01R1/00; G01R1/02; G01R1/06; G01R1/067; G01R1/073; G01R1/07307; G01R1/0735; B; B23; B23K; B23K35/00; B23K35/02; B23K35/0222; B23K35/0244; B23K35/025; B23K35/22; B23K35/36; H; H05; H05K; H05K3/00; H05K3/30; H05K3/32; H05K3/34; H05K3/3465; H05K3/3485; H05K1/00; H05K1/02; H05K1/0266; H05K1/0268; H05K2201/00; H05K2201/02; H05K2201/0203; H05K2201/0206; H05K2201/0215; H05K2201/0263; H05K2201/0266; H05K2203/00; H05K2203/16; H05K2203/163

Claims Analysis

Total Claims: 13
Claim 1
Independent Claim 140 words
A solder composition which comprises a liquid vehicle, said liquid vehicle containing a viscosity controlling agent and a flux, finely divided solder metal dispersed in said vehicle, said solder metal having a particle size ranging from 40 to 70 microns, said liquid vehicle being present in an amount of 10 to 14%, and said solder metal being present in an amount of 86 to 90%, by weight of total vehicle and solder metal in said composition, and additional metal particles dispersed in said vehicle, said additional particles being in the form of metal balls or flakes selected from the group consisting of brass, bronze and copper, said additional metal particles having a size ranging from about 5 to about 30 mils and being present in an amount ranging from about 5 to about 60% by weight of the total composition.
Claim 2
Dependent Claim 140 words
A solder composition which comprises a liquid vehicle, said liquid vehicle containing a viscosity controlling agent and a flux, finely divided solder metal dispersed in said vehicle, said solder metal having a particle size ranging from 40 to 70 microns, said liquid vehicle being present in an amount of 10 to 14%, and said solder metal being present in an amount of 86 to 90%, by weight of total vehicle and solder metal in said composition, and additional metal particles dispersed in said vehicle, said additional particles being in the form of metal balls or flakes selected from the group consisting of brass, bronze and copper, said additional metal particles having a size ranging from about 5 to about 30 mils and being present in an amount ranging from about 5 to about 60% by weight of the total composition.
Claim 3
Dependent Claim 16 words
The composition of claim 1, said flux being a rosin type flux or a paraffin wax.
Claim 4
Dependent Claim 16 words
The composition of claim 2, said flux being a rosin type flux or a paraffin wax.
Claim 5
Dependent Claim 24 words
The composition of claim 1, said solder metal being selected from the group consisting of tin, lead and silver, and alloys and mixtures thereof.
Claim 6
Dependent Claim 27 words
The composition of claim 4, said solder metal being alloys or mixtures of tin, lead and silver; tin and lead; tin and silver; and lead and silver.
Claim 7
Dependent Claim 44 words
The composition of claim 4, said thixotropic agent (a) being hydrogenated castor oil or carboxy methyl cellulose, said organic solvent (b) being 2-butoxy (ethyl) ethyl acetate, 2-butoxy ethyl acetate, ethylene glycol or beta-terpineol, and said flux (c) comprising abietic acid or a paraffin wax.
Claim 8
Dependent Claim 21 words
The composition of claim 4, wherein said vehicle consists of 0.5-10% of (a), 30-60% (b) and 20-65% of (c) by weight.
Claim 9
Dependent Claim 29 words
The composition of claim 4, said thixotropic agent (a) being hydrogenated castor oil, said organic solvent (b) being 2-butoxy (ethyl) ethyl acetate, and said flux (c) comprising abietic acid.
Claim 10
Dependent Claim 19 words
The composition of claim 4, said solder metal being an alloy of 62% tin, 2% silver and 36% lead.
Claim 11
Dependent Claim 28 words
The composition of claim 1, said additional metal particles being brass balls present in an amount of about 5 to about 35% by weight of the total composition.
Claim 12
Dependent Claim 145 words
A solder composition which comprises a liquid vehicle, said liquid vehicle containing (a) a thixotropic agent, (b) an organic solvent and (c) a flux, finely divided solder metal dispersed in said vehicle, said solder metal having a particle size ranging from 40 to 70 microns, said liquid vehicle being present in an amount of 10 to 14%, and said solder metal being present in an amount of 86 to 90%, by weight of total vehicle and solder metal in said composition, and additional metal particles dispersed in said vehicle, said additional particles being in the form of metal balls or flakes selected from the group consisting of brass, bronze and copper, said additional metal particles having a size ranging from about 5 to about 30 mils and being present in an amount ranging from about 5 to about 60% by weight of the total composition.
Claim 13
Dependent Claim 145 words
A solder composition which comprises a liquid vehicle, said liquid vehicle containing (a) a thixotropic agent, (b) an organic solvent and (c) a flux, finely divided solder metal dispersed in said vehicle, said solder metal having a particle size ranging from 40 to 70 microns, said liquid vehicle being present in an amount of 10 to 14%, and said solder metal being present in an amount of 86 to 90%, by weight of total vehicle and solder metal in said composition, and additional metal particles dispersed in said vehicle, said additional particles being in the form of metal balls or flakes selected from the group consisting of brass, bronze and copper, said additional metal particles having a size ranging from about 5 to about 30 mils and being present in an amount ranging from about 5 to about 60% by weight of the total composition.

References Cited (Backward Citations)

US4391742A Cited
US4535012A Cited
US4595605A Cited
US4595604A Cited
US4595606A Cited

USPTO Annuity & Maintenance Windows

Annuity Stage Window Opens Payment Deadline Surcharge Period Until Estimated Fee Status
3.5 Years (Year 4) 1990-07-13 1991-01-12 1991-07-14 $2000.00 Window Closed / Lapsed
7.5 Years (Year 8) 1994-07-13 1995-01-12 1995-07-14 $3760.00 Window Closed / Lapsed
11.5 Years (Year 12) 1998-07-13 1999-01-12 1999-07-14 $7700.00 Window Closed / Lapsed

Assigned Categories & Tags

No categories assigned to this patent yet.

Assign Category Tag