Method of preparing tubular silica glass
Assignee: Seiko Epson Corp
•
Filing: 1985-10-01
•
Granted: 1987-07-14
•
Expires: 2005-10-01
Abstract
Abstract A method of preparing tubular silica glass is disclosed. The method includes the steps of first hydrolyzing silicon alkoxide with acid and then adding ultra-fine particle silica to form a sol solution. The sol solution is placed in a cylindrical container and gelled while rotating the cylindrical container to obtain a tubular gel. The tubular gel is dried and sintered to the tubular silica glass.
Inventors
- 👤 Haruo Osafune
- 👤 Sadao Kanbe
- 👤 Teiichiro Mori
- 👤 Masahisa Ikejiri
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 07:50
CPC Classifications
C; C03; C03B; C03B37/00; C03B37/01; C03B37/012; C03B37/014; C03B37/016; C03B19/00; C03B19/12; C03C; C03C1/00; C03C1/006; Y; Y02; Y02P; Y02P40/00; Y02P40/50; Y02P40/57; Y10; Y10S; Y10S65/00; Y10S65/901
Claims Analysis
Total Claims: 44
Claim 1
Independent Claim
93 words
A method of preparing tubular silica glass, comprising the steps of: preparing a solution of a silicon alkoxide hydrolyzed with an aqueous acid catalyst; adding ultra-fine particles of silica to the acid hydrolyzed silicon alkoxide solution to form a sol solution; adjusting the pH of the sol solution to between about 3 to 6; placing the sol solution into a cylindrical container; gelling the sol solution by rotating the container to obtain a tubular gel; drying the tubular gel to a dry gel; and sintering the dry gel to the tubular silica glass.
Claim 2
Independent Claim
93 words
A method of preparing tubular silica glass, comprising the steps of: preparing a solution of a silicon alkoxide hydrolyzed with an aqueous acid catalyst; adding ultra-fine particles of silica to the acid hydrolyzed silicon alkoxide solution to form a sol solution; adjusting the pH of the sol solution to between about 3 to 6; placing the sol solution into a cylindrical container; gelling the sol solution by rotating the container to obtain a tubular gel; drying the tubular gel to a dry gel; and sintering the dry gel to the tubular silica glass.
Claim 3
Dependent Claim
12 words
The method of claim 1 wherein the silicon alkoxide is silicon methoxide.
Claim 4
Dependent Claim
12 words
The method of claim 1 wherein the silicon alkoxide is silicon ethoxide.
Claim 5
Dependent Claim
36 words
The method of claim 1, wherein the ultra fine particle silica is added to the acid hydrolyzed silicon alkoxide solution in an amount from about 0.2 to 5 mols of silica per mol of silicon alkoxide.
Claim 6
Dependent Claim
58 words
The method of claim 1, wherein said ultra fine particle silica is selected from the group consisting of white carbon obtained by hydrolyzing SiCl 4 with an oxy-hydrogen flame burner, ultra fine particle silica obtained by a wet process using sodium silicon as a material and ultra fine particle silica obtained by hydrolyzing silicon alkoxide with ammonia water.
Claim 7
Dependent Claim
39 words
The method of claim 1, further including the step of: uniformly dispersing said ultra fine particle silica in said sol solution by ultrasonic vibration after the ultra fine particle silica is added to the acid hydrolyzed silicon alkoxide solution.
Claim 8
Dependent Claim
44 words
The method of claim 1, further including the step of: uniformly dispersing the ultra fine particle silica in the sol solution by removing masses from the sol solution using a centrifugal separator after the silica is added to the acid hydrolyzed silicon alkoxide solution.
Claim 9
Dependent Claim
28 words
The method of claim 1, further including the step of: adjusting the pH of the sol solution to between about 3 and 6 by addition of a base.
Claim 10
Dependent Claim
43 words
The method of claim 8, wherein said base is selected from the group consisting of ammonia water, ammonia gas, an aqueous solution of ammonia, triethylamine, an aqueous solution of triethylamine, pyridine, an aqueous solution of pyridine, aniline and an aqueous solution of aniline.
Claim 11
Dependent Claim
38 words
The method of claim 1, wherein the rotation of the rotating cylindrical container is controlled so that the maximum centrifugal gravity to which said sol solution is subjected is less than about 1,000 G (G=980 cm/second 2 ).
Claim 12
Dependent Claim
37 words
The method of claim 1, wherein in said cylindrical container has at least one lid covering the container and said lid is formed with openings covering less than about 50% of the surface area of the lid.
Claim 13
Dependent Claim
66 words
The method of claim 1, wherein the sol solution is gelled at a temperature between about 5° and 60° C. and dried at a temperature between about 20° C. and 120° C. and the temperature is raised from the gelling temperature to the drying temperature at a rate of less than about 120° C. per hour to yield the dry gel by a contraction drying method.
Claim 14
Dependent Claim
30 words
The method of claim 1, wherein the sintering of the dry gel includes the steps of (1) removing absorbed water, (2) removing carbon and (3) making the dry gel non-porous.
Claim 15
Dependent Claim
57 words
The method of claim 13, wherein absorbed water is removed by at least one step of heating the dry gel to a first selected temperature between about 20° and 400° C. at a rate of less than about 400° C. per hour and maintaining said dry gel at the first selected temperature for at least one hour.
Claim 16
Dependent Claim
58 words
The method of claim 13, wherein carbon is removed by at least one step of heating the dry gel to a second selected temperature between about 400° and 1100° C. at a heating rate of between about 30° and 400° C. per hour and maintaining the dry gel at said second selected temperature for at least 3 hours.
Claim 17
Dependent Claim
45 words
The method of claim 13, where the dry gel is made non-porous by at least one step of heating the dry gel to a third selected temperature between about 1000° and 1400° C. at a heating rate between about 30° and 400° C. per hour.
Claim 18
Dependent Claim
44 words
The method of claim 1 wherein the ultra fine particle silica is formed by hydrolyzing a second solution of silicon alkoxide with a base catalyst and the second solution is mixed with the acid hydrolyzed solution of silicon alkoxide to form the sol solution.
Claim 19
Dependent Claim
12 words
The method of claim 17 wherein the silicon alkoxide is silicon methoxide.
Claim 20
Dependent Claim
12 words
The method of claim 17, wherein the silicon alkoxide is silicon ethoxide.
Claim 21
Dependent Claim
23 words
The method of claim 17 wherein the silica particles in the second solution have a diameter of between about 0.01 and 1.0 μm.
Claim 22
Dependent Claim
41 words
The method of claim 17 further comprising the step of concentrating said second solution to adjust the concentration of the silica to between about 0.15 and 1.0 g/cc before mixing said second solution with said acid hydrolyzed solution of silicon alkoxide.
Claim 23
Dependent Claim
54 words
The method of claim 17, wherein the acid hydrolyzed silicon alkoxide solution and the second solution are mixed so that the amount of silica in the acid hydrolyzed silicon alkoxide solution M(A) with respect to the amount of silica in the second solution M(B) is between about 0.2 and 3, namely, M(A)/M(B)=0.2 to 3.
Claim 24
Dependent Claim
68 words
The method of claim 1, wherein the pH of the mixture of the acid hydrolyzed silicon alkoxide solution and the second solution is adjusted before gelation to between about 3 and 6 by adjusting the pH of either or both the acid hydrolyzed silicon alkoxide solution and the second solution before mixing, or by adjusting the pH of the sol solution after mixture of the two preparatory solutions.
Claim 25
Dependent Claim
20 words
The method of claim 17, wherein the sol is placed into a cylindrical container and gelled while rotating the container.
Claim 26
Dependent Claim
38 words
The method of claim 24, wherein the speed of rotation of the rotating cylindrical container is controlled so that the maximum centrifugal gravity acting upon the sol solution is less than about 1000 G (G=980 cm/second 2 ).
Claim 27
Dependent Claim
36 words
The method of claim 17, wherein the cylindrical container has lids covering both ends of the cylindrical container and the lids have openings amounting to less than about 10% of the surface area of the lid.
Claim 28
Dependent Claim
46 words
The method of claim 17, wherein said wet gel is removed from said cylindrical container and placed into a second container having openings amounting to less than about 10% of the surface area of said second container, said wet gel being dried in said second container.
Claim 29
Dependent Claim
52 words
The method of claim 17, wherein said sol is gelled at a temperatue of between about 5° and 60° C. and dried by raising the temperature to between about 40° and 160° C. at a heating rate of less than about 120° C. per hour to yield the dry gel by contracting.
Claim 30
Dependent Claim
46 words
The method of claim 17, wherein the sintering of the dry gel includes the steps of (1) removing absorbed water, (2) removing carbon, (3) accelerating the dehydrating conentration reaction, (4) closing the pores of the dry gel and (5) making the dry gel a clear glass.
Claim 31
Dependent Claim
55 words
The method of claim 17, wherein the sintering of the dry gel includes the steps of (1) removing absorbed water, (2) removing carbon, (3) accelerating the dehydrating concentration reaction, (4) removing OH groups, (5) removing chloride or fluoride, (6) closing the pores of the dry gel and (7) making the dry gel a clear glass.
Claim 32
Dependent Claim
59 words
The method of claim 29 wherein absorbed water is removed by at least one step of heating the dry gel to a first selected temperature between about 20° and 400° C. at a heating rate of less than about 400° C. per hour and maintaining said dry gel at said first selected temperature for at least about 1 hour.
Claim 33
Dependent Claim
59 words
The method of claim 30 wherein absorbed water is removed by at least one step of heating the dry gel to a first selected temperature between about 20° and 400° C. at a heating rate of less than about 400° C. per hour and maintaining said dry gel at said first selected temperature for at least about 1 hour.
Claim 34
Dependent Claim
43 words
The method of claim 29, wherein carbon is removed by at least one step of heating the dry gel to a second selected temperature between about 400° and 900° C. at a heating rate of from about 30° to 400° C. per hour.
Claim 35
Dependent Claim
43 words
The method of claim 30, wherein carbon is removed by at least one step of heating the dry gel to a second selected temperature between about 400° and 900° C. at a heating rate of from about 30° to 400° C. per hour.
Claim 36
Dependent Claim
62 words
The method of claim 29, wherein the dehydrating concentration reaction is accelerated by at least one step of heating the dry gel to a third selected temperature between about 900° and 1200° C. at a heating rate of from about 30° to 400° C. per hour and maintaining said dry gel at said third selected temperature for at least about 30 minutes.
Claim 37
Dependent Claim
62 words
The method of claim 30, wherein the dehydrating concentration reaction is accelerated by at least one step of heating the dry gel to a third selected temperature between about 900° and 1200° C. at a heating rate of from about 30° to 400° C. per hour and maintaining said dry gel at said third selected temperature for at least about 30 minutes.
Claim 38
Dependent Claim
65 words
The method of claim 30, wherein OH groups are removed by flowing a gas selected from the group consisting of He, O 2 , N 2 , Ar and mixtures thereof, and an OH group removing agent in an amount from about 1 to 40% with respect to gas flowing into the oven at a temperature in the range between about 700° and 1100° C.
Claim 39
Dependent Claim
38 words
The method of claim 37, wherein said OH group removing agent is selected from the group consisting of Cl, SOCl, SF 6 , CF 4 , C 2 F 6 , C 3 F 8 and mixtures thereof.
Claim 40
Dependent Claim
61 words
The method of claim 30, wherein, after removing OH groups, chloride or fluoride is removed by flowing a gas selected from the group consisting of He, Ar, N 2 , and mixtures thereof, in an amount from about 1 to 100% with respect to gas flowing into the oven at a temperature in the range between about 800° and 1200° C.
Claim 41
Dependent Claim
79 words
The method of claim 29, wherein the pores are closed in the dry gel by at least one step of (1) pulling a vacuum in the oven, or (2) flowing He gas into the oven, while heating the dry gel to a fourth selected temperature between about 900° and 1350° C. at a heating rate of from about 30° to 400° C. per hour and maintaining the dry gel at said fourth selected temperature for at least one hour.
Claim 42
Dependent Claim
79 words
The method of claim 30, wherein the pores are closed in the dry gel by at least one step of (1) pulling a vacuum in the oven, or (2) flowing He gas into the oven, while heating the dry gel to a fourth selected temperature between about 900° and 1350° C. at a heating rate of from about 30° to 400° C. per hour and maintaining the dry gel at said fourth selected temperature for at least one hour.
Claim 43
Dependent Claim
28 words
The method of claim 29, wherein the dry gel is made into a clear glass by heating to a fifth selected temperature between about 1200° to 1600° C.
Claim 44
Dependent Claim
28 words
The method of claim 30, wherein the dry gel is made into a clear glass by heating to a fifth selected temperature between about 1200° to 1600° C.
References Cited (Backward Citations)
US4173459A
Cited
GB2023571A
Cited
US4324576A
Cited
US4417910A
Cited
US4419115A
Cited
US4574063A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-07-13 | 1991-01-12 | 1991-07-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-07-13 | 1995-01-12 | 1995-07-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-07-13 | 1999-01-12 | 1999-07-14 | $7700.00 | Window Closed / Lapsed |