Process for providing lithium tantalum oxide coated tantalum articles with improved wear resistance
Assignee: North China Research Institute of Electro-optics
•
Filing: 1985-03-27
•
Granted: 1987-07-07
•
Expires: 2005-03-27
Abstract
Abstract A process for coating an article made of tantalum niobium or tantalum-niobium alloy with a film containing polycrystalline lithium metal oxide wherein the metal corresponds to the metal from which the article is made. More particularly, the process improves the surface properties including hardness, yield strength, elasticity and electrical properties so that the operating life can be increased and new application for such articles can be made. It is found that tantalum spinnerets treated in accordance with the process according to the present invention have longer operating life, clog less and produce a better quality fiber.
Inventors
- 👤 Liu Yu-Zhong
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 08:30
CPC Classifications
H; H01; H01G; H01G9/00; H01G9/0029; H01G9/0032; C; C25; C25D; C25D11/00; C25D11/02; C25D11/26; C25F; C25F3/00; C25F3/02; C25F3/08; F; F16; F16K; F16K25/00; F16K25/005; G; G21; G21C; G21C3/00; G21C3/02; G21C3/04; G21C3/06; G21C3/07; Y; Y02; Y02E; Y02E30/00; Y02E30/30
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
272 words
A process for making an article made of a metal selected from the group consisting of tantalum, niobium and an alloy of tantalum and niobium coated with a film comprising polycrystalline lithium-containing metal oxide, the process comprising: (a) cleaning the surface of the metal article to remove surface impurities by: (i) washing with an organic solvent; (ii) etching with a solution of a strong acid selected from the group consisting of hydrofluoric acid and a mixture of hydrofluoric acid and nitric acid under an applied anodic voltage; or (iii) a combination of the above; (b) immersing the cleaned article in a bath of an oxygen containing inorganic salt of lithium at a high temperature in the range of 400° C. to 580° C., and applying an anodic voltage in the range of about 3 to 50 volts to maintain a current density of about 2 to 20 mA/cm 2 for a period of about 0.1 to 10 hours to form said film on the surface of the article; and (c) post-treating the article by: (i) aging at a temperature of about 170° C. to 400° C. for about 1 to 4 hours; (ii) immersing the article in a solution of about 0.05% by weight of phosphoric acid and ethylene glycol at a temperature of about 90° C. to 100° C. and applying anodic voltage of about 500 volts to 600 volts for about 1 to 3 hours; (iii) immersing in dilute phosphoric acid at room temperature and applying an anodic voltage of about 350 volts to about 600 volts for at least 0.5 hours; or (iv) a combination of the above steps.
Claim 2
Dependent Claim
272 words
A process for making an article made of a metal selected from the group consisting of tantalum, niobium and an alloy of tantalum and niobium coated with a film comprising polycrystalline lithium-containing metal oxide, the process comprising: (a) cleaning the surface of the metal article to remove surface impurities by: (i) washing with an organic solvent; (ii) etching with a solution of a strong acid selected from the group consisting of hydrofluoric acid and a mixture of hydrofluoric acid and nitric acid under an applied anodic voltage; or (iii) a combination of the above; (b) immersing the cleaned article in a bath of an oxygen containing inorganic salt of lithium at a high temperature in the range of 400° C. to 580° C., and applying an anodic voltage in the range of about 3 to 50 volts to maintain a current density of about 2 to 20 mA/cm 2 for a period of about 0.1 to 10 hours to form said film on the surface of the article; and (c) post-treating the article by: (i) aging at a temperature of about 170° C. to 400° C. for about 1 to 4 hours; (ii) immersing the article in a solution of about 0.05% by weight of phosphoric acid and ethylene glycol at a temperature of about 90° C. to 100° C. and applying anodic voltage of about 500 volts to 600 volts for about 1 to 3 hours; (iii) immersing in dilute phosphoric acid at room temperature and applying an anodic voltage of about 350 volts to about 600 volts for at least 0.5 hours; or (iv) a combination of the above steps.
Claim 3
Dependent Claim
28 words
A process according to claim 1 wherein the lithium-containing metal oxide is selected from the group consisting of lithium tantalum oxide, lithium niobium oxide and a mixture thereof.
Claim 4
Dependent Claim
36 words
A processing according to claim 1 wherein step (a) comprises electrochemical etching in a solution of hydrofluric acid at an applied anodic voltage of about 2.5 volts to remove a surface layer of the metal body.
Claim 5
Dependent Claim
40 words
A process according to claim 1 wherein the oxygen containing inorganic salt of lithium is selected from the group consisting of lithium nitrate, a mixture of lithium nitrate and potassium nitrate and a mixture of lithium nitrate and lithium hydroxide.
Claim 6
Dependent Claim
30 words
A process according to claim 4 wherein the oxygen containing inorganic salt of lithium is lithium nitrate and the temperature is in the range of 420° C. to 580° C.
Claim 7
Dependent Claim
89 words
A process according to claim 1, wherein in step (b) the temperature of the melt is first controlled at above 500° C. and an applied anodic voltage in the range of about 3 volts to 35 volts is applied for about 1 to 3 hours; the temperature of the melt is then controlled at a temperature in the range of 420° C. to 460° C. and an applied voltage in the range of about 35 volts to 45 volts is applied to form the outer portion of the film.
Claim 8
Dependent Claim
88 words
A process according to claim 2 wherein in step (b) the temperature of the melt is first controlled at about 410° C. to 460° C. and an applied anodic voltage in the range of about 35 volts to 45 volts is applied for about 2 to 4 hours and then the temperature of the bath is controlled at a temperature about 500° C., and an applied anodic voltage in the range of about 3 volts to 35 volts is applied to form the outer portion of the film.
Claim 9
Dependent Claim
33 words
A process according to claim 1 wherein in step (c) the post treatment is carried out by procedure (iii) and an anodic voltage of about 350 volts is applied for about one hour.
Claim 10
Dependent Claim
33 words
A process according to claim 1 wherein in step (c) the post treatment is carried out by procedure (i) and the temperature during aging is maintained at about 170° C. to 250° C.
Claim 11
Dependent Claim
28 words
A process according to claim 1 wherein in step (c) the post treatment is carried out by procedure (ii) and the temperature is maintained at about 95° C.
Claim 12
Dependent Claim
99 words
A process according to claim 1 wherein the metal article is a spinneret made of tantalum and, wherein step (a) further comprises electro-chemical etching of the surface of the tantalum spinneret by immersing the spinneret in a solution containing hydrofluoric acid with an applied anodic voltage to remove a surface layer and enlarge the diameter of the capillary bores in the spinnent and wherein in step (b) the temperature of the melt is in the range of about 420° C. to 580° C., and the applied anodic voltage is in the range of about 3 volts to 40 volts.
Claim 13
Dependent Claim
26 words
A process according to claim 11 further comprising the step of removing the film coating on the exit side of the spinneret to expose tantalum metal.
Claim 14
Dependent Claim
13 words
A process according to claim 1 wherein the article is made of tantalum.
Claim 15
Dependent Claim
18 words
A process according to claim 13 wherein the film-coated tantalum metal has increased elasticity compared to noncoated tantalum.
Claim 16
Dependent Claim
16 words
A process according to claim 14 wherein the article is a polar plate of a capacitor.
Claim 17
Dependent Claim
22 words
A process according to claim 14 wherein the article is a substrate of an x-ray sensing element or a heat sensing element.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-07-06 | 1991-01-05 | 1991-07-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-07-06 | 1995-01-05 | 1995-07-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-07-06 | 1999-01-05 | 1999-07-07 | $7700.00 | Window Closed / Lapsed |