Titanium engine valve and method of making
Assignee: Ford Global Technologies LLC
•
Filing: 1985-12-24
•
Granted: 1987-06-30
•
Expires: 2005-12-24
Abstract
Abstract A method is disclosed for making a dual microstructure titanium based engine valve, wherein a first zone of the valve contains essentially a mixture of fine, equiaxed alpha and transformed beta crystalline grains which exhibit high tensile strength and high fatigue resistance, and a second zone of the valve which contains essentially a colony type microstructure exhibiting resistance to high temperature creep. The method comprises: (a) preparing a valve stock of forgeable mixed phase alpha/beta titanium based material; (b) hot working said first zone at a temperature below the beta transus temperature, (c) forging said second zone and, either simultaneously with said forging or subsequent thereto, heat treating said second zone at a temperature above (e.g., 25°-200° F. above) the beta transus temperature for a period of time to achieve beta processing followed by cooling to 1400° F. at a rate of 0.1-10.0° F./second; and (d) heat treating, immediately subsequent to either step (b) or step (c), at least the first zone at a temperature below the beta transus temperature (e.g., 25°-200° F. below) for a period of time to achieve alpha/beta processing.
Inventors
- 👤 John E. Allison
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 08:27
CPC Classifications
F; F01; F01L; F01L3/00; F01L3/02; B; B23; B23P; B23P15/00; B23P15/001; B23P15/002; C; C22; C22F; C22F1/00; C22F1/16; C22F1/18; C22F1/183; Y; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49229; Y10T29/49298
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
182 words
A method of making a dual microstructure titanium based engine valve, wherein a first zone of said valve contains essentially a mixture of fine, equiaxed alpha and transformed beta crystalline grains which exhibit high tensile strength and high fatigue resistance, and a second zone of said valve which contains essentially colony type alpha/beta crystalline grains exhibiting resistance to high temperature creep, the method comprising: (a) preparing valve stock for each of said zones of forgeable mixed phase alpha/beta titanium based material; (b) hot working said first zone at a temperature below the beta transus temperature; (c) forging said second zone and, either simultaneously with or subsequent thereto, heat treating said second zone at a temperature above the beta transus temperature for a period of time to achieve beta processing followed by cooling of said second zone to a temperature of 1400° F. at a rate of 0.1-10.0° F./second; and (d) heat treating, immediately subsequent to step (b) or step (c) at least said first zone at a temperature below the beta transus temperature for a period of time to achieve alpha/beta processing.
Claim 2
Independent Claim
182 words
A method of making a dual microstructure titanium based engine valve, wherein a first zone of said valve contains essentially a mixture of fine, equiaxed alpha and transformed beta crystalline grains which exhibit high tensile strength and high fatigue resistance, and a second zone of said valve which contains essentially colony type alpha/beta crystalline grains exhibiting resistance to high temperature creep, the method comprising: (a) preparing valve stock for each of said zones of forgeable mixed phase alpha/beta titanium based material; (b) hot working said first zone at a temperature below the beta transus temperature; (c) forging said second zone and, either simultaneously with or subsequent thereto, heat treating said second zone at a temperature above the beta transus temperature for a period of time to achieve beta processing followed by cooling of said second zone to a temperature of 1400° F. at a rate of 0.1-10.0° F./second; and (d) heat treating, immediately subsequent to step (b) or step (c) at least said first zone at a temperature below the beta transus temperature for a period of time to achieve alpha/beta processing.
Claim 3
Dependent Claim
26 words
The method as in claim 1, in which heat treating in step (d) is in the temperature range of 25°-200° F. below said beta transus temperature.
Claim 4
Dependent Claim
55 words
The method as in claim 1, in which said hot working of step (b) is carried out by extrusion of said first zone of the valve, and said forging of step (c) is carried out simultaneously with heating of said second zone to a temperature in the range 25°-200° F. above said beta transus temperature.
Claim 5
Dependent Claim
67 words
The method as in claim 1, in which said hot working of step (b) is carried out by extruding said first zone, and in step (c), forging of step (c) is carried out at a temperature above or below the beta transus temperature, followed by heating only said second zone to a temperature above the beta transus temperature for a period of time to achieve beta processing.
Claim 6
Dependent Claim
16 words
The method as in claim 1, in which in step (c) said second zone is forged.
Claim 7
Dependent Claim
28 words
The method as in claim 1, in which said first zone is extruded to form a stem and fillet, said second zone being forged to form a valve.
Claim 8
Dependent Claim
32 words
The method as in claim 6, in which beta processing is that which obtains a colony structure having a substantially uniform existence of long alpha platelets interspersed with films of beta grains.
Claim 9
Dependent Claim
18 words
The method as in claim 7, in which said colony structure has a colony size of 50-300 microns.
Claim 10
Dependent Claim
32 words
The method as in claim 1, in which alpha/beta processing is that which obtains a microstructure having a substantially uniform existence of mixed regions of alpha microstructure and regions of colony microstructure.
Claim 11
Dependent Claim
17 words
The method as in claim 9, in which said microstructure has a grain size of 5-50 microns.
Claim 12
Dependent Claim
28 words
The method as in claim 1, in which said zones are independent preforms during processing and are welded together following the process to form the completed engine valve.
Claim 13
Dependent Claim
18 words
The method as in claim 1, in which beta processing is carried out for at least 1/2 hour.
Claim 14
Dependent Claim
19 words
The method as in claim 1, in which said alpha/beta processing is carried out for at least 1/2 hour.
Claim 15
Dependent Claim
24 words
The method as in claim 1, in which said stock is comprised of Ti-6Al-4V alloy and has a beta transus temperature of 1850° F.
Claim 16
Dependent Claim
24 words
The method as in claim 1, in which said stock is comprised of Ti-6Al-2Sn-4Zr-2Mo-0.1Si alloy and has a beta transus temperature of 1835° F.
Claim 17
Dependent Claim
24 words
The method as in claim 1, in which said stock is comprised of Ti-5Al-5Sn-2Zr-4Mo-0.3Si alloy and has a beta transus temperature of 1760° F.
Claim 18
Dependent Claim
24 words
The method as in claim 1, in which said stock is comprised of Ti-5Al-6Sn-2Zr-1Mo-0.3Si alloy and has a beta transus temperature of 1860° F.
Claim 19
Dependent Claim
41 words
The method as in claim 1, in which said titanium based material contains alloying ingredients which function as alpha and beta stabilizing agents to provide a volume of beta phase which is not less than 5% and not greater than 40%.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-06-29 | 1990-12-29 | 1991-06-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-06-29 | 1994-12-29 | 1995-06-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-06-29 | 1998-12-29 | 1999-06-30 | $7700.00 | Window Closed / Lapsed |