Production of piezoelectric dielectric films by poling in stack form
Assignee: Arkema Inc
•
Filing: 1985-05-17
•
Granted: 1987-06-30
•
Expires: 2005-05-17
Abstract
Abstract A multi-layer stack of dielectric films containing at least one piezoelectric-sensitive (PES) film is subjected to a high dc field strength while the stack is maintained at an elevated temperature to induce piezoelectric properties in the PES films. Various stacking arrangements of the films in the multi-layer can be used to obtain enhanced piezoelectric properties for various PES films in the multi-layer stack.
Inventors
- 👤 Oliver S. Sprout
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 18:17
CPC Classifications
H; H01; H01G; H01G7/00; H01G7/02; H01G7/021; H01G7/023; H10; H10N; H10N30/00; H10N30/01; H10N30/04; H10N30/045; H10N30/09; H10N30/098; H10N30/50; Y; Y10; Y10S; Y10S310/00; Y10S310/80; Y10T; Y10T29/00; Y10T29/42; Y10T29/49; Y10T29/49002
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
146 words
A process for treating thin PES film to impart piezoelectric activity thereto comprising applying, to a multi-layer of dielectric film at least one layer of which is thin PES film selected from homopolymers, copolymers terpolymers, or mixtures or blends of vinylidene fluoride polymers, vinylfluoride polymers, vinylchloride polymers, and polyamides at a temperature between about room temperature and a temperature just below the melting point of the film, a high strength dc field, said multi-layer being disposed between a single set of oppositely charged electrodes with the outer layers in contact with the opposite electrodes until piezoelectric activity is induced to the extent of at least 5 pC/N in at least one of the PES films, thereafter cooling the PES film to below about 50° C. before or after removing the dc field, removing the dc field and thereafter grounding the PES film to remove surface charge.
Claim 2
Dependent Claim
146 words
A process for treating thin PES film to impart piezoelectric activity thereto comprising applying, to a multi-layer of dielectric film at least one layer of which is thin PES film selected from homopolymers, copolymers terpolymers, or mixtures or blends of vinylidene fluoride polymers, vinylfluoride polymers, vinylchloride polymers, and polyamides at a temperature between about room temperature and a temperature just below the melting point of the film, a high strength dc field, said multi-layer being disposed between a single set of oppositely charged electrodes with the outer layers in contact with the opposite electrodes until piezoelectric activity is induced to the extent of at least 5 pC/N in at least one of the PES films, thereafter cooling the PES film to below about 50° C. before or after removing the dc field, removing the dc field and thereafter grounding the PES film to remove surface charge.
Claim 3
Dependent Claim
18 words
The process of claim 1 wherein at least one PES film has a thickness below about 150 μm.
Claim 4
Dependent Claim
22 words
The process of claim 1 wherein the layer of PES film adjacent the positive electrode is substantially thinner than the adjacent layers.
Claim 5
Dependent Claim
21 words
The process of claim 1 wherein at least one PES film is formed from a high molecular weight vinylidene fluoride polymer.
Claim 6
Dependent Claim
16 words
The process of claim 4 where the high molecular weight vinylidene fluoride polymer is a homopolymer.
Claim 7
Dependent Claim
39 words
The process of claim 4 where the high molecular weight vinylidene fluoride polymer is a co-polymer of from about 65 to about 75 weight percent of vinylidene fluoride and from about 35 to about 25 weight percent of tetrafluoroethylene.
Claim 8
Dependent Claim
13 words
The process of claim 1 wherein at least one PES film is oriented.
Claim 9
Dependent Claim
13 words
The process of claim 7 wherein the oriented PES film is uniaxially oriented.
Claim 10
Dependent Claim
32 words
The process of claim 1 wherein the multi-layer to which the high strength dc field is applied is at a temperature in the range of from about 80° to about 110° C.
Claim 11
Dependent Claim
30 words
The process of claim 1 wherein the high strength dc field applied across the electrodes is from about 300 to about 1000 kilovolts per centimeter of thickness of the multi-layer.
Claim 12
Dependent Claim
22 words
The process of claim 10 wherein the field applied across the electrodes is gradually increased until the desired field strength is reached.
Claim 13
Dependent Claim
142 words
A process for treating thin PES film to impart piezoelectric activity thereto comprising applying, to a multi-layer of film at least one layer of which is thin PES film at a temperature between about room temperature and a temperature just below the melting point of the film, a high strength dc field, said multi-layer being comprised of a biaxially oriented film, prepared by suspension polymerization, positioned adjacent to at least one unoriented film, prepared by emulsion polymerization and being disposed between a single set of oppositely charged electrodes with the outer layers in contact with the opposite electrodes until piezoelectric activity is induced to at least one of the PES films, thereafter cooling the PES film to below about 50° C. before or after removing the dc field, removing the dc field and thereafter grounding the PES film to remove surface charge.
Claim 14
Dependent Claim
142 words
A process for treating thin PES film to impart piezoelectric activity thereto comprising applying, to a multi-layer of film at least one layer of which is thin PES film at a temperature between about room temperature and a temperature just below the melting point of the film, a high strength dc field, said multi-layer being comprised of a biaxially oriented film, prepared by suspension polymerization, positioned adjacent to at least one unoriented film, prepared by emulsion polymerization and being disposed between a single set of oppositely charged electrodes with the outer layers in contact with the opposite electrodes until piezoelectric activity is induced to at least one of the PES films, thereafter cooling the PES film to below about 50° C. before or after removing the dc field, removing the dc field and thereafter grounding the PES film to remove surface charge.
Claim 15
Dependent Claim
145 words
A process for treating thin PES film to impart piezoelectric activity thereto comprising applying, to a multi-layer of film at least one layer of which is thin PES film at a temperature between about room temperature and a temperature just below the melting point of the film, a high strength dc field, said multi-layer being comprised of an uniaxially oriented film, prepared by suspension polymerization, positioned adjacent to at least one biaxially oriented film, prepared by emulsion or suspension polymerization and being disposed between a single set of oppositely charged electrodes with the outer layers in contact with the opposite electrodes until piezoelectric activity is induced in at least one of the PES films, thereafter cooling the PES film to below about 50° C. before or after removing the dc field, removing the dc field and thereafter grounding the PES film to remove surface charge.
Claim 16
Dependent Claim
145 words
A process for treating thin PES film to impart piezoelectric activity thereto comprising applying, to a multi-layer of film at least one layer of which is thin PES film at a temperature between about room temperature and a temperature just below the melting point of the film, a high strength dc field, said multi-layer being comprised of an uniaxially oriented film, prepared by suspension polymerization, positioned adjacent to at least one biaxially oriented film, prepared by emulsion or suspension polymerization and being disposed between a single set of oppositely charged electrodes with the outer layers in contact with the opposite electrodes until piezoelectric activity is induced in at least one of the PES films, thereafter cooling the PES film to below about 50° C. before or after removing the dc field, removing the dc field and thereafter grounding the PES film to remove surface charge.
Claim 17
Dependent Claim
146 words
A process for treating thin PES film to impart piezoelecrric activity thereto comprising applying, to a multi-layer of film at least one layer of which is thin PES film at a temperature between about room temperature and a temperature just below the melting point of the film, a high strength dc field, said multi-layer being comprised of an uniaxially or biaxially oriented film, prepared by emulsion polymerization, positioned adjacent to at least one other emulsion polymerized film having the same orientation and being disposed between a single set of oppositely charged electrodes with the outer layers in contact with the opposite electrodes until piezoelectric activity is induced in at least one of the PES films, thereafter cooling the PES film to below about 50° C. before or after removing the dc field, removing the dc field and thereafter grounding the PES film to remove surface charge.
Claim 18
Dependent Claim
146 words
A process for treating thin PES film to impart piezoelecrric activity thereto comprising applying, to a multi-layer of film at least one layer of which is thin PES film at a temperature between about room temperature and a temperature just below the melting point of the film, a high strength dc field, said multi-layer being comprised of an uniaxially or biaxially oriented film, prepared by emulsion polymerization, positioned adjacent to at least one other emulsion polymerized film having the same orientation and being disposed between a single set of oppositely charged electrodes with the outer layers in contact with the opposite electrodes until piezoelectric activity is induced in at least one of the PES films, thereafter cooling the PES film to below about 50° C. before or after removing the dc field, removing the dc field and thereafter grounding the PES film to remove surface charge.
References Cited (Backward Citations)
US3316620A
Cited
US3943614A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-06-29 | 1990-12-29 | 1991-06-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-06-29 | 1994-12-29 | 1995-06-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-06-29 | 1998-12-29 | 1999-06-30 | $7700.00 | Window Closed / Lapsed |