Polyethylene stretched film
Assignee: Tonen General Sekiyu KK
•
Filing: 1986-08-15
•
Granted: 1987-06-16
•
Expires: 2006-08-15
Abstract
Abstract An oriented film is prepared by crosslinking a sheet of polyethylene (preferably HDPE) containing particulate inorganic slip and antiblock additions to provide maximum crosslinking at the surfaces of the sheet and minimum orientation at its middle layer portion, and thereafter heating and stretching the film to obtain an oriented HDPE of high clarity film of improved moisture proof.
Inventors
- 👤 Yasushi Itaba
- 👤 Tadao Yoshino
- 👤 Yutaka Yoshifuji
- 👤 Keichiro Saito
- 👤 Jyoichi Tabuchi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 22:50
CPC Classifications
C; C08; C08J; C08J3/00; C08J3/24; C08J3/245; B; B29; B29C; B29C55/00; B29C55/02; C08J5/00; C08J5/18; B29K; B29K2023/00; B29K2023/04; B29K2023/06; C08J2323/00; C08J2323/02; C08J2323/04; C08J2323/06; Y; Y10; Y10T; Y10T428/00; Y10T428/26; Y10T428/263; Y10T428/264; Y10T428/268; Y10T428/31504; Y10T428/31855
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
156 words
An oriented polyethylene film produced by: (a) crosslinking opposite surfaces of a sheet of polyethylene having a density greater than 0.935 and containing from 0.02 to 1 part by weight per 100 parts by weight polyethylene of particulate inorganic compound selected from the group consisting of zeolite, silica, alumina, and bentonite, having an average particle size less than 20 microns, said crosslinking producing gel fractions in opposite outer layer portions of the sheet of 20-70% and a gel fraction in a middle layer portion of the sheet of 0-5%; and (b) heating and stretching the crosslinked sheet under conditions to orient the polyethylene molecules; said film having a haze value less than 7%, a coefficient of friction less than 0.6, a value of antiblocking less than 50 g/cm 2 , and a vapor transmission rate lower than Y=17X.sup.-1/2 where Y is the water transmission rate (g/m 2 /24 hours) and X is the film thickness (microns).
Claim 2
Dependent Claim
156 words
An oriented polyethylene film produced by: (a) crosslinking opposite surfaces of a sheet of polyethylene having a density greater than 0.935 and containing from 0.02 to 1 part by weight per 100 parts by weight polyethylene of particulate inorganic compound selected from the group consisting of zeolite, silica, alumina, and bentonite, having an average particle size less than 20 microns, said crosslinking producing gel fractions in opposite outer layer portions of the sheet of 20-70% and a gel fraction in a middle layer portion of the sheet of 0-5%; and (b) heating and stretching the crosslinked sheet under conditions to orient the polyethylene molecules; said film having a haze value less than 7%, a coefficient of friction less than 0.6, a value of antiblocking less than 50 g/cm 2 , and a vapor transmission rate lower than Y=17X.sup.-1/2 where Y is the water transmission rate (g/m 2 /24 hours) and X is the film thickness (microns).
Claim 3
Dependent Claim
24 words
An oriented polyethylene film as defined in claim 1 wherein the film is composed of HDPE and has a haze of less than 5%.
Claim 4
Dependent Claim
18 words
The film as defined in claim 2 wherein the film thickness is between about 10 and 50 microns.
Claim 5
Dependent Claim
134 words
An oriented polyethylene film comprising HDPE containing from 0.05 to 0.5 parts by weight per 100 parts of said HDPE of an inorganic compound selected from the group consisting of zeolite, silica, alumina, and bentonite, having an average particle size of between 0.1 to 10 microns, said film having (a) outer surface layer portions crosslinked to have a gel fraction of between 20 to 70%; (b) a middle layer portion having a gel fraction of between 0 and 5%; (c) a haze of less than 6%; (d) a coefficient of friction less than 0.6; (e) an antiblock value of less than 50 g/cm 2 ; and (f) a water vapor transmission rate (Y) lower than Y=17X.sup.-1/2 where Y is the water transmission rate (g/m 2 /24 hours) and X is the film thickness (microns).
Claim 6
Dependent Claim
134 words
An oriented polyethylene film comprising HDPE containing from 0.05 to 0.5 parts by weight per 100 parts of said HDPE of an inorganic compound selected from the group consisting of zeolite, silica, alumina, and bentonite, having an average particle size of between 0.1 to 10 microns, said film having (a) outer surface layer portions crosslinked to have a gel fraction of between 20 to 70%; (b) a middle layer portion having a gel fraction of between 0 and 5%; (c) a haze of less than 6%; (d) a coefficient of friction less than 0.6; (e) an antiblock value of less than 50 g/cm 2 ; and (f) a water vapor transmission rate (Y) lower than Y=17X.sup.-1/2 where Y is the water transmission rate (g/m 2 /24 hours) and X is the film thickness (microns).
Claim 7
Dependent Claim
18 words
The oriented polyethylene film of claim 4 wherein said HDPE has a density of at least 0.950 g/cc.
Claim 8
Dependent Claim
18 words
The oriented film of claim 4 wherein said HDPE has a MI of more than 0.05 g/10 min.
Claim 9
Dependent Claim
12 words
The film of claim 6 wherein the MI is 0.5-20 g/10 min.
References Cited (Backward Citations)
GB1270954A
Cited
US3563870A
Cited
US3886056A
Cited
US4101699A
Cited
US4226905A
Cited
GB2040804A
Cited
US4590020A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-06-15 | 1990-12-15 | 1991-06-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-06-15 | 1994-12-15 | 1995-06-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-06-15 | 1998-12-15 | 1999-06-16 | $7700.00 | Window Closed / Lapsed |