Abstract A novel dual ion beam sputtering process for depositing thin films of high density is described. One of the ion beams contains relatively heavy sputtering ions, such as argon ions, for ejecting atoms from a target. The second ion beam is also directed at the target and contains ions having energies of at least 3 electron volts and less than 20 electron volts. The products of the beams are collected on a substrate as a thin film. High density, hydrogenated amorphous semiconductor films, oxide and nitride films, and other films, may be deposited according to the process. The films have densities nearly equal those observed for bulk samples of the same materials. Hydrogenated amorphous silicon films deposited by the process exhibit enhanced photoconductivity.
A process for depositing a hydrogenated amorphous silicon film on a substrate comprising: simultaneously directing a first beam of ions effective in sputtering and a second beam of hydrogen ions against a silicon target, said hydrogen ions having energies not exceeding about 20 electron volts, and collecting on said substrate the product of said beams as a film of hydrogenated amorphous silicon.
Claim 2
Dependent Claim
62 words
A process for depositing a hydrogenated amorphous silicon film on a substrate comprising: simultaneously directing a first beam of ions effective in sputtering and a second beam of hydrogen ions against a silicon target, said hydrogen ions having energies not exceeding about 20 electron volts, and collecting on said substrate the product of said beams as a film of hydrogenated amorphous silicon.
Claim 3
Dependent Claim
18 words
The process of claim 1 wherein said hydrogen ions have energies not less than about 3 electron volts.
Claim 4
Dependent Claim
14 words
The process of claim 1 wherein said ions effective in sputtering comprise argon ions.
Claim 5
Dependent Claim
23 words
The process of claim 1 including maintaining said substrate at a temperature of between 20° C. to 400° C. during said deposition process.
Claim 6
Dependent Claim
23 words
The process of claim 1 wherein said substrate is selected from the group consisting of glass, quartz, silicon, metallic elements and metal alloys.
Claim 7
Dependent Claim
20 words
The process of claim 1 including maintaining the ambient pressure during said deposition process between 0.13 to 1.3×10 -3 pascal.