Method of and device for drawing an optical fiber from a solid preform consisting substantially of SiO2 and doped SiO2
Assignee: Plasma Optical Fibre BV
•
Filing: 1983-09-28
•
Granted: 1987-06-16
•
Expires: 2003-09-28
Abstract
Abstract Optical fibres are drawn from a solid preform which consists substantially of SiO 2 and doped SiO 2 . After leaving the heating zone, the fiber is guided through a space having a laminar gas flow to restrict the temperature drop across the fiber so that no extra stresses are incorporated in the fiber upon cooling. A device for performing this method comprises a quartz pipe through which the fiber is guided and in which a laminar gas flow is maintained.
Inventors
- 👤 Aart A. Van Der Giessen
- 👤 Victor A. van der Hulst
- 👤 Petrus J. Janssen
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 21:01
CPC Classifications
C; C03; C03B; C03B37/00; C03B37/01; C03B37/02; C03B37/025; C03B37/029; C03B37/027; C03B2205/00; C03B2205/60; C03B2205/80; C03B2205/81; C03B2205/82; C03B2205/90
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
154 words
A method of drawing an optical fiber from a solid preform comprising SiO 2 and doped SiO 2 , said method comprising the steps of: heating an end of the preform to a temperature above 2000° C. in a furnace; drawing an optical fiber from the heated end of the preform out of the furnace; and flowing a gas through the furnace to heat the gas to substantially the temperature of the fiber at the end of the preform, and then flowing the hot gas out of the furnace along the fiber at substantially the same speed as the fiber is drawn from the furnace, wherein the gas flow is laminar flow and the ggs flows along the fiber for a selected time and distance chosen to assure that the temperature gradient in the fiber is always less than that at which stresses are produced which would increase the optical attenuation of the fiber.
Claim 2
Independent Claim
154 words
A method of drawing an optical fiber from a solid preform comprising SiO 2 and doped SiO 2 , said method comprising the steps of: heating an end of the preform to a temperature above 2000° C. in a furnace; drawing an optical fiber from the heated end of the preform out of the furnace; and flowing a gas through the furnace to heat the gas to substantially the temperature of the fiber at the end of the preform, and then flowing the hot gas out of the furnace along the fiber at substantially the same speed as the fiber is drawn from the furnace, wherein the gas flow is laminar flow and the ggs flows along the fiber for a selected time and distance chosen to assure that the temperature gradient in the fiber is always less than that at which stresses are produced which would increase the optical attenuation of the fiber.
Claim 3
Dependent Claim
23 words
A method as claimed in claim 1, wherein each portion of the fiber passes through the gas flow for at least 0.1 second.
Claim 4
Dependent Claim
16 words
A method as claimed in claim 2, wherein the gas does not attack the furnace material.
Claim 5
Dependent Claim
25 words
A method as claimed in claim 2, wherein the gas is heated in the furnace to a temperature within 200° C. of the fiber temperature.
Claim 6
Dependent Claim
25 words
A method as claimed in claim 1, wherein the gas is heated in the furnace to a temperature within 200° C. of the fiber temperature.
Claim 7
Independent Claim
165 words
A device for drawing an optical fiber from a solid preform comprising SIO 2 and doped SiO 2 , said device comprising: means for heating an end of the preform to a temperature at which an optical fiber can be drawn from the preform; means for drawing an optical fiber from the heated end of the preform out of the heating means; means for flowing a gas through the heating means to heat the gas to substantially the temperature of the fiber at the end of the preform, and then flowing the hot gas out of the heating means along the fiber at substantially the same speed as the fiber is drawn from the heating means, wherein the gas flow is laminar flow and the gas flows along the fiber for a selected time and distance chosen to assure that the temperature gradient in the fiber is always less than that at which stresses are produced which would increase the optical attenuation of the fiber.
Claim 8
Independent Claim
165 words
A device for drawing an optical fiber from a solid preform comprising SIO 2 and doped SiO 2 , said device comprising: means for heating an end of the preform to a temperature at which an optical fiber can be drawn from the preform; means for drawing an optical fiber from the heated end of the preform out of the heating means; means for flowing a gas through the heating means to heat the gas to substantially the temperature of the fiber at the end of the preform, and then flowing the hot gas out of the heating means along the fiber at substantially the same speed as the fiber is drawn from the heating means, wherein the gas flow is laminar flow and the gas flows along the fiber for a selected time and distance chosen to assure that the temperature gradient in the fiber is always less than that at which stresses are produced which would increase the optical attenuation of the fiber.
Claim 9
Dependent Claim
25 words
A device as claimed in claim 6, wherein the means for flowing the gas out of the furnace along the fiber comprises a quartz tube.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-06-15 | 1990-12-15 | 1991-06-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-06-15 | 1994-12-15 | 1995-06-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-06-15 | 1998-12-15 | 1999-06-16 | $7700.00 | Window Closed / Lapsed |