Anti-corrosion treatment for patterning of metallic layers

Claim 2

An improved method for defining interconnect patterns in an integrated circuit fabricated on a semiconductor wafer, said method having a step of etching a conductor layer and a subsequent step of etching a titanium-tungsten barrier layer which lies between a silicon substrate and said conductor layer, the improvement comprising the step of: immersing said wafer in a strong acid solution which will not etch the conductor layer, prior to said subsequent step of etching the titanium-tungsten barrier layer, so as to remove chlorides from the wafer; and immersing the wafer in a weak base solution, so as to remove from the wafer chlorides and fluorides remaining as a result of said step of etching said conductor layer.

Claim 3

The method of claim 1, wherein the step of immersing the wafer in a weak base solution is accomplished by the step of immersing the wafer in ammonium hydroxide.

Claim 4

The method of claim 1, wherein the step of immersing the wafer in a strong acid solution is accomplished by the step of immersing the wafer in nitric acid.

Claim 5

An improved method for defining interconnect patterns in an integrated circuit fabricated on a semiconductor wafer, said method having steps of forming a photoresist layer over a conductor layer, etching said conductor layer, and a subsequent step of etching a titanium-tungsten barrier layer which lies between a silicon substrate and said conductor layer, the improvement comprising the steps of: immersing said wafer in a strong acid solution which will not etch the conductor layer, so as to remove from the wafer and the photoresist layer chlorides remaining as a result of previously etching said conductor layer; immersing said wafer in a weak base solution so as to remove from the wafer remaining chlorides and fluorides; removing said photoresist layer from said etched conductor layer; and etching said titanium-tungsten barrier layer to complete the definition of said interconnect pattern.

Claim 6

An improved method for defining interconnect patterns in an integrated circuit fabricated on a semiconductor wafer, said method having steps of forming a photoresist layer over a conductor layer, etching said conductor layer, and a subsequent step of etching a titanium-tungsten barrier layer which lies between a silicon substrate and said conductor layer, the improvement comprising the steps of: immersing said wafer in a strong acid solution which will not etch the conductor layer, so as to remove from the wafer and the photoresist layer chlorides remaining as a result of previously etching said conductor layer; immersing said wafer in a weak base solution so as to remove from the wafer remaining chlorides and fluorides; removing said photoresist layer from said etched conductor layer; and etching said titanium-tungsten barrier layer to complete the definition of said interconnect pattern.

Claim 7

The method of claim 4 wherein the following step is performed: forming an anti-reflective coating layer intermediate said etched conductor layer and said photoresist layer.

Claim 8

The method of claim 4 wherein the step of immersing the wafer in a strong acid solution is accomplished by the step of immersing the wafer in nitric acid.

Claim 9

The method of claim 4 wherein the step of immersing the wafer in a weak base solution is accomplished by the step of immersing the wafer in ammonium hydroxide.

Claim 10

The method of claim 6 wherein the step of immersing the wafer in nitric acid is accomplished by the step of immersing the wafer in nitric acid for approximately ten seconds.

Claim 11

The method of claim 7 wherein the step of immersing the wafer in ammonium hydroxide is accomplished by the step of immersing the wafer in a dilution of ammonium hydroxide of approximately 500 to 1 of a 30 percent concentrate of ammonium hydroxide with water.

Claim 12

The method of claim 9 wherein the step of immersing the wafer in a dilution of ammonium hydroxide is accomplished by immersing the wafer in a dilution of ammonium hydroxide for approximately ten seconds.

Claim 13

The method of claim 4 wherein the step of removing said photoresist from said etched conductor layer is accomplished by the step of removing said photoresist layer by using an oxygen-based plasma.

Claim 14

The method of claim 5 wherein the following step is performed: removing said anti-reflective coating using a fluorine-based plasma etch.

Claim 15

The method of claim 5 wherein the following step is performed: removing said anti-reflective coating using a chemical etch.

Claim 16

An improved method for defining interconnect patterns in a semiconductor device fabricated on a semiconductor wafer, said semiconductor device having a silicon substrate, said method comprising the steps of: forming a titanium-tungsten barrier layer over said silicon substrate; forming a conductor layer over said titanium-tungsten barrier layer; forming a photoresist layer over said conductor layer; optically exposing said photoresist layer to define within said photoresist layer images of said interconnect patterns; developing said photoresist layer to expose a portion of said conductor layer; etching said exposed portion of said conductor layer to expose a portion of said titanium-tungsten barrier layer; plasma passivating said wafer to reduce the corrosion rate of said conductor layer in air; immersing said wafer in a strong acid solution which will not etch the conductor layer, so as to remove from the wafer and the photoresist layer chlorides remaining as a result of said etching of the conductor layer; immersing said wafer in a weak base solution so as to remove from the wafer remaining chlorides and fluorides; removing said photoresist layer from said etched conductor layer; and etching said exposed portion of said titanium-tungsten barrier layer.

Claim 17

An improved method for defining interconnect patterns in a semiconductor device fabricated on a semiconductor wafer, said semiconductor device having a silicon substrate, said method comprising the steps of: forming a titanium-tungsten barrier layer over said silicon substrate; forming a conductor layer over said titanium-tungsten barrier layer; forming a photoresist layer over said conductor layer; optically exposing said photoresist layer to define within said photoresist layer images of said interconnect patterns; developing said photoresist layer to expose a portion of said conductor layer; etching said exposed portion of said conductor layer to expose a portion of said titanium-tungsten barrier layer; plasma passivating said wafer to reduce the corrosion rate of said conductor layer in air; immersing said wafer in a strong acid solution which will not etch the conductor layer, so as to remove from the wafer and the photoresist layer chlorides remaining as a result of said etching of the conductor layer; immersing said wafer in a weak base solution so as to remove from the wafer remaining chlorides and fluorides; removing said photoresist layer from said etched conductor layer; and etching said exposed portion of said titanium-tungsten barrier layer.

Claim 18

The method of claim 14 wherein the following step is performed: forming an anti-reflective coating layer intermediate said conductor layer and said photoresist layer.

Claim 19

The method of claim 14 wherein the step of forming a conductor layer over said titanium-tungsten barrier layer is accomplished by the step of forming over said barrier layer a layer of material selected from the group consisting of aluminum and aluminum-copper-silicon alloy.

Claim 20

The method of claim 16 wherein the thickness of said layer of material selected from the group consisting of aluminum and aluminum-copper-silicon alloy is in the range of 7000-9000 Angstroms.

Claim 21

The method of claim 14 wherein the thickness of said titanium-tungsten barrier layer is in the range of 1500-2500 Angstroms.