Claim 1

Independent Claim 278 words

In a process for metallizing a ceramic substrate which comprises adhesion promoting a surface of the substrate with a molten alkali metal compound; and subsequently electrolessly depositing a metal layer having thickness greater tha 5 micrometers on the adhesion promoted surface, the improvement which comprises: avoiding the formation of blisters between the electrolessly depsosited metal layer and the ceramic substrate by: admixing an adhesion promotion modifier comprising water with at least one alkali metal compound to provide an alkali metal composition, the adhesion promotion modifier when present in the composition is capable of modifying the alkali metal composition so that the molten composition adhesion promotes the ceramic surface to provide a microfaceted surface structure with larger grain size and greater weight loss in comparison to an adhesion promoted ceramic surface provided by the use of the molten alkali metal compound alone, the amount of adhesion promotion modifier being sufficient to lower the melting temperature of th alkali metal composition to between 145° C. and 240° F. and permit adhesion promotion of the ceramic surface for a time period between 1 and 200 minutes with the alkali metal composition in the molten state; heating the alkali metal composition at a temperature between 145° C. and 240° C. to render it molten; and contacting the molten alkali metal composition with the ceramic surface for a time period between 1 and 200 minutes and at a temperature between 145° C. and 240° C. to adhesion promote the ceramic surface; and subsequently electrolessly depositing a metal layer having a thickness greater than 5 micrometers on the adhesion promoted surface without the formation of blisters between the metal layer and the ceramic surface.

Claim 2

Dependent Claim 278 words

In a process for metallizing a ceramic substrate which comprises adhesion promoting a surface of the substrate with a molten alkali metal compound; and subsequently electrolessly depositing a metal layer having thickness greater tha 5 micrometers on the adhesion promoted surface, the improvement which comprises: avoiding the formation of blisters between the electrolessly depsosited metal layer and the ceramic substrate by: admixing an adhesion promotion modifier comprising water with at least one alkali metal compound to provide an alkali metal composition, the adhesion promotion modifier when present in the composition is capable of modifying the alkali metal composition so that the molten composition adhesion promotes the ceramic surface to provide a microfaceted surface structure with larger grain size and greater weight loss in comparison to an adhesion promoted ceramic surface provided by the use of the molten alkali metal compound alone, the amount of adhesion promotion modifier being sufficient to lower the melting temperature of th alkali metal composition to between 145° C. and 240° F. and permit adhesion promotion of the ceramic surface for a time period between 1 and 200 minutes with the alkali metal composition in the molten state; heating the alkali metal composition at a temperature between 145° C. and 240° C. to render it molten; and contacting the molten alkali metal composition with the ceramic surface for a time period between 1 and 200 minutes and at a temperature between 145° C. and 240° C. to adhesion promote the ceramic surface; and subsequently electrolessly depositing a metal layer having a thickness greater than 5 micrometers on the adhesion promoted surface without the formation of blisters between the metal layer and the ceramic surface.

Claim 3

Dependent Claim 100 words

The process of claim 1, further including after adhesion promoting said ceramic surface and before forming said metal layer thereon, the step of exposing said surface to an acidic halide solution containing one or more halides selected from the group consisting of chlorides, bromides and iodides in an amount greater than 0.5 moles halide per liter and sufficient to promote adsorpotion of catalyst on the surface and eliminate bare spots in an adherent metal layer formed on the surface or selected parts thereof; and treating said surface with a catalyst solution for rendering said surface receptive to deposition of metal.

Claim 4

Dependent Claim 116 words

The process of claim 1, further including, after adhesion promoting said ceramic surface and before forming said metal layer thereon, the step of exposing said surface to a adsorption promoter selected from the group consisting of ethoxylated non-ionic compounds and nitrogen-containing compounds, said nitriogen-containing compounds being selected from the group consisting of quaternary compounds, amine oxides, alkanolamines, amides, betaines, amino acids and guinidine derivatives, in an amount sufficient to, and at a pH which will promote adsorption of catalyst on the surface and eliminate bare spots in an adherent metal layer formed on the surface or selected parts thereof; and treating said surface with a catalyst solution for rendering said surface receptive to deposition of metal.

Claim 5

Dependent Claim 205 words

In a process for metallizing a ceramic substrate which comprises adhesion promoting a surface of the substrate with a molten alkali metal compound; and subsequently electrolessly depositing a copper layer having a thickness greater than 5 micrometers on the adhesion promoted surface using an electroless copper deposition bath, the electroless copper bath comprising copper ions, ethylenediaminetetraacetic acid (EDTA) and a reducing agent for the copper ions, the improvement which comprises: avoiding the formation of blisters between a subsequently electrolessly deposited metal layer and the substrate by: admixing water with at least one alkali metal compound to provide an alkali metal composition, the amount of water being sufficient to lower the melting temperature of the alkali metal composition to between 145° C. and 240° C. and permit adhesion promotion of the ceramic surface for a time period between 1 and 200 minutes with the alkali metal composition in a molten state; and heating the alkali metal composition at a temperature between 145° C. and 240° C. to render it molten, and contacting the molten alkali metal composition with the ceramic surface for a time period between 1 and 200 minutes and at a temperature between 145° C. and 240° C. to adhesion promote the ceramic surface.

Claim 6

Dependent Claim 205 words

In a process for metallizing a ceramic substrate which comprises adhesion promoting a surface of the substrate with a molten alkali metal compound; and subsequently electrolessly depositing a copper layer having a thickness greater than 5 micrometers on the adhesion promoted surface using an electroless copper deposition bath, the electroless copper bath comprising copper ions, ethylenediaminetetraacetic acid (EDTA) and a reducing agent for the copper ions, the improvement which comprises: avoiding the formation of blisters between a subsequently electrolessly deposited metal layer and the substrate by: admixing water with at least one alkali metal compound to provide an alkali metal composition, the amount of water being sufficient to lower the melting temperature of the alkali metal composition to between 145° C. and 240° C. and permit adhesion promotion of the ceramic surface for a time period between 1 and 200 minutes with the alkali metal composition in a molten state; and heating the alkali metal composition at a temperature between 145° C. and 240° C. to render it molten, and contacting the molten alkali metal composition with the ceramic surface for a time period between 1 and 200 minutes and at a temperature between 145° C. and 240° C. to adhesion promote the ceramic surface.

Claim 7

Dependent Claim 100 words

The process of claim 4 further including after adhesion pormoting said ceramic surface and before forming said metal layer thereon, the step of exposing said surface to an acidic halide solution containing one or more halides selected from the group consisting of chlorides, bromides and iodides in an amount greater than 0.5 moles halide per liter and sufficient to promote adsorption of catalyst on the surface and eliminate bare spots in an adherent metal layer formed on the surface or selected parts thereof; and treating said surface with a catalyst solution for rendering said surface receptive to deposition of metal.

Claim 8

Dependent Claim 16 words

The processs of claim 4 wherein said alkali metal compound is sodium hydroxide or potassium hydroxide.

Claim 9

Dependent Claim 18 words

The process of claim 4 wherein the alkali metal composition contains between 10 and 40% by weight water.

Claim 10

Dependent Claim 21 words

The process of claim 7 wherein said alkali metal composition is heated at a temperature between 160° C. and 180° C.

Claim 11

Dependent Claim 21 words

The process of claim 8 wherein said ceramic surface is adhesion promoted for a time period between 3 and 45 minutes.

Claim 12

Dependent Claim 21 words

The process of claim 8 wherein the alkali metal composition is heated at a temperature between 170° C. and 175° C.

Claim 13

Dependent Claim 21 words

The process of claim 10 wherein said ceramic surface is adhesion promoted for a time period between 5 and 15 minutes.

Claim 14

Dependent Claim 27 words

The process of claim 4 wherein the blister-free metal layer is electrolessly deposited on the ceramic surface to a thickness between a 5 micrometers and 75 micrometers.

Claim 15

Dependent Claim 193 words

A process for producing a blister-free metal layer having a thickness greater than 5 micrometers on a surface of a ceramic substrate without blisters between the metal layer and the substrate, which process comprises the steps: providing an alkali metal composition containing water and between 0.35 and 0.9 mole fraction of an alkali metal compound; heating the alkali metal composition at a temperature between 145° C. and 240° C. to render it molten; contacting the ceramic surface with the molten alkali metal composition for a time period sufficient to adhesion promote the ceramic surface, the mole fraction of said alkali metal compound present in said alkali metal composition being selected to adjust the surface topography of the adhesion promoted surface so that grains of the metal which are to be subsequently deposited on the surface with an electroless metal deposition bath adhere to the surface without the formation of blisters between the metal layer and the ceramic surface; activating the adhesion promoted surface to render it receptive for adherent metal deposition; and electrolessly depositing with the electroless metal deposition bath the blister-free metal layer having the desired thickness without the formation of blisters.

Claim 16

Dependent Claim 193 words

A process for producing a blister-free metal layer having a thickness greater than 5 micrometers on a surface of a ceramic substrate without blisters between the metal layer and the substrate, which process comprises the steps: providing an alkali metal composition containing water and between 0.35 and 0.9 mole fraction of an alkali metal compound; heating the alkali metal composition at a temperature between 145° C. and 240° C. to render it molten; contacting the ceramic surface with the molten alkali metal composition for a time period sufficient to adhesion promote the ceramic surface, the mole fraction of said alkali metal compound present in said alkali metal composition being selected to adjust the surface topography of the adhesion promoted surface so that grains of the metal which are to be subsequently deposited on the surface with an electroless metal deposition bath adhere to the surface without the formation of blisters between the metal layer and the ceramic surface; activating the adhesion promoted surface to render it receptive for adherent metal deposition; and electrolessly depositing with the electroless metal deposition bath the blister-free metal layer having the desired thickness without the formation of blisters.

Claim 17

Dependent Claim 16 words

The process of claim 13 wherein the alkali metal compound is sodium hydroxide or potassium hydroxide.

Claim 18

Dependent Claim 22 words

The process of claim 13 wherein the alkali metal composition contains between 0.4 and 0.6 mole fraction of an alkali metal compound.

Claim 19

Dependent Claim 21 words

The process of claim 15 wherein the alkali metal composition is heated at a temperature between 170° C. and 175° C.

Claim 20

Dependent Claim 26 words

The process of claim 13 wherein the blister-free metal layer is electrolessly deposited on the ceramic surface to a thickness between 5 micrometers and 75 micrometers.

Claim 21

Dependent Claim 28 words

The process of claim 13 wherein the ceramic surface is contacted with the molten alkali metal composition by immersing the ceramic substrate in the molten alkali metal composition.

Claim 22

Dependent Claim 21 words

The process of claim 13 wherein the ceramic surface is adhesion promoted for a time period between 5 and 15 minutes.

Claim 23

Dependent Claim 27 words

The process of claim 2 wherein said acid halide solution constitutes part of said catalyst solution used for rendering said ceramic surface receptive to deposition of metal.

Claim 24

Dependent Claim 27 words

The process of claim 5 wherein said acid halide solution constitutes part of said catalyst solution used for rendering said ceramic surface receptive to deposition of metal.

Annuity Stage	Window Opens	Payment Deadline	Surcharge Period Until	Estimated Fee	Status
3.5 Years (Year 4)	1990-05-18	1990-11-17	1991-05-19	$2000.00	Window Closed / Lapsed
7.5 Years (Year 8)	1994-05-18	1994-11-17	1995-05-19	$3760.00	Window Closed / Lapsed
11.5 Years (Year 12)	1998-05-18	1998-11-17	1999-05-19	$7700.00	Window Closed / Lapsed

Process for avoiding blister formation in electroless metallization of ceramic substrates

Abstract

Inventors

Bibliographic Details

Claims Analysis

References Cited (Backward Citations)

USPTO Annuity & Maintenance Windows

Assigned Categories & Tags

Assign Category Tag