Trench sidewall isolation by polysilicon oxidation
Assignee: International Business Machines Corp
•
Filing: 1986-05-12
•
Granted: 1987-05-19
•
Expires: 2006-05-12
Abstract
Abstract Disclosed is a process of growing a conformal and etch-resistant silicon dioxide on a surface by forming a conformal layer of polysilicon and subjecting the polysilicon to thermal oxidation to completely convert the polysilicon into (poly) silicon oxide. Disclosed also is a method of forming an isolation trench in a semiconductor substrate having a high integrity oxide sidewall. After forming the trench in the substrate surface using a suitable etch mask and RIE, a single (thermal) oxide or dual (thermal) oxide and (CVD) nitride liner is formed on all trench surfaces. A conformal layer of undoped polysilicon is then formed (by. e.g. LPCVD) on the liner. By subjecting to thermal oxidation, the polysilicon is completely converted into a conformal (poly) silicon oxide layer having a thickness about 2.5 times that of the polysilicon layer. The resulting (poly) silicon oxide has the conformality of CVD oxide and the high etch resistance of thermally grown oxide. Alternatively, prior to forming the (poly) silicon oxide, the polysilicon layer is removed from the trench floor and the substrate surface in order to limit volume expansion of the polysilicon to a single direction perpendicular to the trench walls. The trench is filled with oxide, epitaxial silicon, polysilicon, polymers or metal, as desired. For achieving substrate contract through the trench, the trench bottom is opened up by RIE. Polysilicon is deposited with in-situ doping at a high temperature to fill the trench and simultaneously diffuse the dopant from the polysilicon fill into the underlying substrate to form a channel stop.
Inventors
- 👤 Inge G. Fulton
- 👤 James S. Makris
- 👤 Victor R. Nastasi
- 👤 Anthony F. Scaduto
- 👤 Anne C. Shartel
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 10:08
CPC Classifications
H; H10; H10W; H10W10/00; H10W10/01; H10W10/011; H10W10/014; H10W10/0148; H10W10/041; H10W10/10; H10W10/17; H10W10/40; H10W20/00; H10W20/01; H10W20/021; Y; Y10; Y10S; Y10S148/00; Y10S148/05
Claims Analysis
Total Claims: 30
Claim 1
Independent Claim
42 words
A method for thermally growing a uniform, conformal silicon dioxide layer on a non-oxidizable surface comprising: forming on said surface a conformal layer of polysilicon; and subjecting said polysilicon to thermal oxidation to completely convert said polysilicon to said silicon dioxide layer.
Claim 2
Independent Claim
42 words
A method for thermally growing a uniform, conformal silicon dioxide layer on a non-oxidizable surface comprising: forming on said surface a conformal layer of polysilicon; and subjecting said polysilicon to thermal oxidation to completely convert said polysilicon to said silicon dioxide layer.
Claim 3
Dependent Claim
14 words
The method as recited in claim 1 wherein said polysilicon forming is by deposition.
Claim 4
Dependent Claim
18 words
The claim as recited in claim 1 wherein said polysilicon forming is by low pressure chemical vapor deposition.
Claim 5
Dependent Claim
25 words
The method as recited in claim 1 wherein the thickness of said polysilicon layer is approximately 40% of the thickness of said silicon dioxide layer.
Claim 6
Dependent Claim
15 words
The method as recited in claim 1 wherein said non-oxidizable surface is silicon nitride surface.
Claim 7
Independent Claim
51 words
A method for thermally growing a conformal polysilicon oxide layer on the surface(s) of a groove, comprising: providing a semiconductor substrate including a groove therein, said groove having one or more surfaces; forming a conformal polysilicon layer on said surfaces; and thermally oxidizing to completely convert said polysilicon to polysilicon oxide.
Claim 8
Independent Claim
51 words
A method for thermally growing a conformal polysilicon oxide layer on the surface(s) of a groove, comprising: providing a semiconductor substrate including a groove therein, said groove having one or more surfaces; forming a conformal polysilicon layer on said surfaces; and thermally oxidizing to completely convert said polysilicon to polysilicon oxide.
Claim 9
Dependent Claim
17 words
The method as recited in claim 6 wherein said polysilicon forming is by chemical vapor deposition (CVD).
Claim 10
Dependent Claim
15 words
The method as in claim 7 wherein said CVD is accomplished at a low pressure.
Claim 11
Dependent Claim
15 words
The method as recited in claim 6 wherein said groove is either V-shaped or U-shaped.
Claim 12
Dependent Claim
16 words
The method as recited in claim 6 wherein said surfaces are coated with a non-oxidizable material.
Claim 13
Dependent Claim
14 words
The method as recited in claim 10, wherein said non-oxidizable material is silicon nitride.
Claim 14
Dependent Claim
90 words
A process for forming an isolation trench in a semiconductor substrate comprising: providing a semiconductor substrate covered with an insulator layer; forming a trench having substantially vertical surfaces and substantially horizontal surfaces in said substrate by etching an opening in said insulator layer followed by etching the underlying substrate in correspondence with said opening; depositing a conformal layer of polysilicon on said surfaces of the trench; thermally oxidizing to completely convert said polysilicon into polysilicon oxide layer; and filling said trench with a material which is compatible with said substrate.
Claim 15
Dependent Claim
90 words
A process for forming an isolation trench in a semiconductor substrate comprising: providing a semiconductor substrate covered with an insulator layer; forming a trench having substantially vertical surfaces and substantially horizontal surfaces in said substrate by etching an opening in said insulator layer followed by etching the underlying substrate in correspondence with said opening; depositing a conformal layer of polysilicon on said surfaces of the trench; thermally oxidizing to completely convert said polysilicon into polysilicon oxide layer; and filling said trench with a material which is compatible with said substrate.
Claim 16
Dependent Claim
14 words
The process as in claim 12 further comprising removing said insulator by wet etching.
Claim 17
Dependent Claim
24 words
The process as in claim 12 further comprising thermally oxidizing said trench to form a thin oxide trench liner prior to said polysilicon deposition.
Claim 18
Dependent Claim
17 words
The process as in claim 12 wherein said polysilicon deposition is by low pressure chemical vapor deposition.
Claim 19
Dependent Claim
33 words
The process as in claim 12 where said trench filling comprises: removing said polysilicon oxide from said horizontal surfaces and exposing said semiconductor substrate thereunder; and depositing doped polysilicon to fill said trench.
Claim 20
Dependent Claim
19 words
The process as in claim 16 wherein said doped polysilicon is of the same conductivity type as said substrate.
Claim 21
Dependent Claim
43 words
The process as in claim 17 further comprising depositing said polysilicon at a high temperature in the range 900°-1000° C. to simultaneously diffuse some of the dopant from said doped polysilicon into the underlying substrate and form a channel stop below said trench.
Claim 22
Dependent Claim
22 words
The process as in claim 18 wherein the thickness of said conformal polysilicon layer is about 40% of said polysilicon oxide layer.
Claim 23
Dependent Claim
104 words
A process for forming an isolation trench in a semiconductor substrate comprising: providing a semiconductor substrate having on a surface thereof an insulator layer; forming a trench in said substrate by etching an opening in said insulator and the underlying substrate in correspondence with said opening; depositing a thin conformal layer of polysilicon on the trench walls and floor and on said insulator layer; converting said polysilicon layer into polysilicon oxide by thermal oxidation of said polysilicon; filling the trench with polysilicon; and removing said insulator by wet etching while maintaining in tact said polysilicon oxide on the trench walls near the substrate surface.
Claim 24
Dependent Claim
104 words
A process for forming an isolation trench in a semiconductor substrate comprising: providing a semiconductor substrate having on a surface thereof an insulator layer; forming a trench in said substrate by etching an opening in said insulator and the underlying substrate in correspondence with said opening; depositing a thin conformal layer of polysilicon on the trench walls and floor and on said insulator layer; converting said polysilicon layer into polysilicon oxide by thermal oxidation of said polysilicon; filling the trench with polysilicon; and removing said insulator by wet etching while maintaining in tact said polysilicon oxide on the trench walls near the substrate surface.
Claim 25
Dependent Claim
30 words
The process as in claim 20 further comprising: thermally oxidizing to form a silicon dioxide liner for said trench; and depositing a layer of silicon nitride on said oxide liner.
Claim 26
Dependent Claim
40 words
The process as in claim 21 further comprising: removing said conformal polysilicon layer by anisotropic reactive ion etching from the floor of said trench and from said insulator layer prior to said conversion of said polysilicon into said polysilicon oxide.
Claim 27
Dependent Claim
74 words
The process as in claim 22 wherein said polysilicon filling comprises: depositing by chemical vapor deposition polysilicon doped with the same conductivity type dopant as said substrate at a high temperature of about 900°-1000° C. to completely fill said trench and obtain a thick doped polysilicon layer atop said insulator while simultaneously diffusing dopant the polysilicon filling said trench into the substrate in correspondence with said trench forming a channel stop under said trench.
Claim 28
Dependent Claim
29 words
The process as in claim 23 further comprising etching to remove said thick polysilicon layer and recessing said polysilicon filling said trench utilizing said nitride as an etch mask.
Claim 29
Dependent Claim
32 words
The process as in claim 24 further comprising prior to said wet etching step thermally oxidizing the upper portion of said recessed polysilicon filling said trench to form a polysilicon oxide cap.
Claim 30
Dependent Claim
26 words
The process as in claim 20 further comprising prior to filling said trench removing by reactive ion etching the polysilicon oxide layer in said trench bottom.
References Cited (Backward Citations)
US3966577A
Cited
US4104086A
Cited
US4139442A
Cited
US4256514A
Cited
US4238278A
Cited
US4222792A
Cited
US4356211A
Cited
US4544576A
Cited
US4509249A
Cited
US4582565A
Cited
US4571819A
Cited
US4626317A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-05-18 | 1990-11-17 | 1991-05-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-05-18 | 1994-11-17 | 1995-05-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-05-18 | 1998-11-17 | 1999-05-19 | $7700.00 | Window Closed / Lapsed |