Hardenable cast iron and the method of making cast iron
Assignee: Ford Motor Co
•
Filing: 1985-09-05
•
Granted: 1987-05-19
•
Expires: 2005-09-05
Abstract
Abstract A method is disclosed for forming a surface hardenable cast iron article by development of metastable retained austenite in the cell boundary of a ductile or semiductile cast iron. The method comprises (a) controlling the solidification of a cast iron melt to extend the eutectic arrest time to 4-12 minutes, the melt having by weight percent a carbon equivalent (carbon plus one-third silicon) equal to 4.3-5.0, manganese 0.55-1.2, nickel 0.5-3.0, and the remainder essentially iron, the melt having been treated to form cell boundaries in the solidified iron with a high proportion of the manganese being segregated in the cell boundaries; (b) subjecting the solidified cast iron to an austempering heat treatment to permit the segregated manganese in the cell boundaries to form metastable retained austenite; and (c) terminating the heat treatment prior to the conversion of the metastable austenite to a stable microstructure. To obtain the benefits of wear resistance, the method further comprises using the heat treated cast iron by stressing a surface region thereof and transforming the microstructure of such surface region to martensite.
Inventors
- 👤 Bela V. Kovacs
- 👤 Roman M. Nowicki
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 22:55
CPC Classifications
C; C21; C21D; C21D7/00; C21D7/02; C21D7/04; C21D5/00
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
125 words
A method of forming a surface hardenable article of ductile or semiductile (compacted graphite) cast iron, comprising: (a) controlling the solidification of a melt of said cast iron to extend the eutectic arrest time to 4-12 minutes and to form a solidified article having cell boundaries with a high concentration of segregated manganese, the melt having by weight percent a carbon equivalent (carbon plus one-third silicon) equal to 4.3-5.0, manganese 0.55-1.2, nickel 0.5-3.0, and the remainder essentially ductile or semiductile iron chemistry; (b) subjecting the solidified cast iron to an austempering heat treatment to permit the segregated manganese in the cell boundaries to form metastable retained austenite; and (c) terminating the heat treatment prior to the conversion of the metastable austenite to a stable microstructure.
Claim 2
Independent Claim
125 words
A method of forming a surface hardenable article of ductile or semiductile (compacted graphite) cast iron, comprising: (a) controlling the solidification of a melt of said cast iron to extend the eutectic arrest time to 4-12 minutes and to form a solidified article having cell boundaries with a high concentration of segregated manganese, the melt having by weight percent a carbon equivalent (carbon plus one-third silicon) equal to 4.3-5.0, manganese 0.55-1.2, nickel 0.5-3.0, and the remainder essentially ductile or semiductile iron chemistry; (b) subjecting the solidified cast iron to an austempering heat treatment to permit the segregated manganese in the cell boundaries to form metastable retained austenite; and (c) terminating the heat treatment prior to the conversion of the metastable austenite to a stable microstructure.
Claim 3
Dependent Claim
44 words
The method as in claim 1, in which said melt is comprised of carbon in the weight percent range of 3.5-3.8, silicon in the weight percent range of 2.4-2.8, sulphur no greater than 0.015 weight percent, and phosphorus no greater than 0.06 weight percent.
Claim 4
Dependent Claim
62 words
The method as in claim 2, in which said melt is further characterized by the presence of molybdenum in the weight percent range of 0-0.5, or copper in the weight percent range of 0-3.0 as a partial substitute for nickel, nickel still being present in an effective amount to increase hardenability of the solidified cast iron and to substantially prevent pearlite formation.
Claim 5
Dependent Claim
26 words
The method as in claim 1, in which said melt solidifies as ductile iron with a content of magnesium in the weight percent range of 0.03-0.06.
Claim 6
Dependent Claim
25 words
The method as in claim 1, in which said melt solidifies as compacted graphite iron with magnesium present in the weight percent range of 0.02-0.03.
Claim 7
Dependent Claim
64 words
The method as in claim 1, in which said austempering heat treatment comprises heating said solidified iron to a temperature in the range of 1675°-1725° F. for a period to achieve substantial austenization of said iron and then quenching to the temperature range of 775°-825° F. for a period no greater than two hours to prevent the formation of bainite followed by air cooling.
Claim 8
Dependent Claim
21 words
The method as in claim 6, in which said austenization temperature is maintained for a period of at least two hours.
Claim 9
Dependent Claim
22 words
The method as in claim 1, in which said manganese is present in said melt in the weight percent range of 0.8-1.2.
Claim 10
Dependent Claim
30 words
The method as in claim 1, in which said melt is solidified in a manner so that at least 75% of said manganese is segregated within the cell boundaries thereof.
Claim 11
Independent Claim
172 words
A method of making a more wear resistant cast iron shape, comprising: (a) controlling the solidification of a cast iron melt to extend the eutectic arrest time to 4-12 minutes and to form a solidified cast iron shape, said melt having by weight percent a carbon equivalent (carbon plus one-third silicon) equal to 4.3-5.0, at least 0.8 manganese, nickel 0.5-3.0, and the remainder essentially iron, said melt having been treated to form cell boundaries in the solidified iron with a high proportion of said manganese being segregated in said cell boundaries; (b) subjecting said solidified cast iron shape to an austempering heat treatment to permit said segregated manganese in cell boundaries to form metastable retained austenite; (c) terminating said heat treatment prior to the conversion of said metastable austenite retained to a stable microstructure; and (d) using said heat treated cast iron shape in a manner to transform a selected surface region of said metastable retained austenite to martensite by stressing said surface region, said martensite having a high resistance to wear.
Claim 12
Independent Claim
172 words
A method of making a more wear resistant cast iron shape, comprising: (a) controlling the solidification of a cast iron melt to extend the eutectic arrest time to 4-12 minutes and to form a solidified cast iron shape, said melt having by weight percent a carbon equivalent (carbon plus one-third silicon) equal to 4.3-5.0, at least 0.8 manganese, nickel 0.5-3.0, and the remainder essentially iron, said melt having been treated to form cell boundaries in the solidified iron with a high proportion of said manganese being segregated in said cell boundaries; (b) subjecting said solidified cast iron shape to an austempering heat treatment to permit said segregated manganese in cell boundaries to form metastable retained austenite; (c) terminating said heat treatment prior to the conversion of said metastable austenite retained to a stable microstructure; and (d) using said heat treated cast iron shape in a manner to transform a selected surface region of said metastable retained austenite to martensite by stressing said surface region, said martensite having a high resistance to wear.
Claim 13
Dependent Claim
17 words
The method as in claim 10, in which said use is carried out by rolling or burnishing.
Claim 14
Dependent Claim
30 words
The method as in claim 10, in which said use is carried out in a manner to provide a level of stress in an amount of at least 80,000 psi.
Claim 15
Dependent Claim
26 words
The method as in claim 10, in which the selected surface region of said cast iron shape is characterized by a hardness of about 50-60 Rc.
Claim 16
Dependent Claim
57 words
A ductile or semiductile cast iron composition characterized by a matrix consisting of acicular high carbon austenite and ferrite and a cell boundary containing meta-stable retained austenite and manganese in an amount ranging from 3-10 weight percent of the material in the cell boundary, said retained austenite being convertible to martensite upon the application of mechanical stress.
Claim 17
Dependent Claim
57 words
A ductile or semiductile cast iron composition characterized by a matrix consisting of acicular high carbon austenite and ferrite and a cell boundary containing meta-stable retained austenite and manganese in an amount ranging from 3-10 weight percent of the material in the cell boundary, said retained austenite being convertible to martensite upon the application of mechanical stress.
Claim 18
Dependent Claim
44 words
The composition as in claim 14, in which the core of said composition is characterized by a toughness of 50-60 ft/lb (impact strength), a yield strength of at least about 100 ksi, a tensile strength of 130-140 ksi, and a hardness of 28-32 Rc.
References Cited (Backward Citations)
US2885284A
Cited
US4096002A
Cited
JPS541223A
Cited
JPS5959825A
Cited
US4484953A
Cited
JPS60106944A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-05-18 | 1990-11-17 | 1991-05-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-05-18 | 1994-11-17 | 1995-05-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-05-18 | 1998-11-17 | 1999-05-19 | $7700.00 | Window Closed / Lapsed |