US4484953A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of making ductile cast iron with improved strength
Assignee: Ford Motor Co
•
Filing: 1983-01-24
•
Granted: 1984-11-27
•
Expires: 2003-01-24
Abstract
Abstract A method of making ductile cast iron with a matrix of acicular ferrite and bainite is disclosed. A melt by weight of 3.0-3.6% carbon, 3.5-5.0% silicon, 0.7-5.0% nickel, 0-0.3% Mo, >0.015% S, >0.06% P (remainder Fe) is subjected to a nodularizing agent and solidified. The iron is then heat treated by heating to 1575°-1650° F. for 1-3 hours, quenched to 400°-775° F. at a rate of at least 275° F./min., held for 0.5-4 hours, and cooled to room temperature. The resulting ductile iron exhibits a yield strength of at least 80 ksi, a tensile strength of at least 140 ksi, elongation of at least 6%, and a hardness of at least 270 BHN.
Inventors
- 👤 Bela V. Kovacs
- 👤 Roman M. Nowicki
- 👤 Charles A. Stickels
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 16:33
CPC Classifications
C; C22; C22C; C22C37/00; C22C37/04
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
160 words
A method of making a ductile cast iron having a microstructure with a matrix consisting of ferrite and bainite, said cast iron exhibiting a tensile strength of at least 140 ksi, a yield strength of at least 80 ksi, and an elongation of 6-10%, the method comprising: (a) melting a ferrous alloy consisting essentially of by weight 3.0-3.6% carbon, 3.5-5.0% silicon, 0.7-5.0% nickel, 0-0.3% molybdenum, 0.2-0.4% manganese, not greater than 0.06% phosphorus, not greater than 0.015% sulphur, and the remainder essentially iron, said melted ferrous alloy being subjected to a nodularizing agent to form a ductile cast iron upon solidification and cooling; (b) heat treating said ductile cast iron by heating to 1575°-1650° F. for a period of 1-3 hours and immediately quenching to 675°-750° F. at a rate of at least 275° F./min.; and (c) holding said ductile cast iron in the temperature range of 400°-775° F. for a period of 0.5-4 hours followed by cooling to room temperature.
Claim 2
Independent Claim
160 words
A method of making a ductile cast iron having a microstructure with a matrix consisting of ferrite and bainite, said cast iron exhibiting a tensile strength of at least 140 ksi, a yield strength of at least 80 ksi, and an elongation of 6-10%, the method comprising: (a) melting a ferrous alloy consisting essentially of by weight 3.0-3.6% carbon, 3.5-5.0% silicon, 0.7-5.0% nickel, 0-0.3% molybdenum, 0.2-0.4% manganese, not greater than 0.06% phosphorus, not greater than 0.015% sulphur, and the remainder essentially iron, said melted ferrous alloy being subjected to a nodularizing agent to form a ductile cast iron upon solidification and cooling; (b) heat treating said ductile cast iron by heating to 1575°-1650° F. for a period of 1-3 hours and immediately quenching to 675°-750° F. at a rate of at least 275° F./min.; and (c) holding said ductile cast iron in the temperature range of 400°-775° F. for a period of 0.5-4 hours followed by cooling to room temperature.
Claim 3
Dependent Claim
30 words
The method as in claim 1, in which said ferrous alloy melt consists of about 3.0 C, 4.0% silicon, 1.3% nickel, 0.3% molybdenum, 0.2% manganese, the remainder being essentially iron.
Claim 4
Dependent Claim
48 words
The method as in claim 1, in which said heat treating is carried out by heating in the first stage to about 1600° F. for 2 hours and is immediately quenched to 725° F. and held for a period of about 2 hours before cooling to room temperature.
Claim 5
Dependent Claim
47 words
The method as in claim 1, in which the silicon is present in microripples in said ferrous alloy and is present in a critical microconcentration gradient whereby the silicon content in the ferrite is at least 1.5% by weight greater than the silicon content in the bainite.
Claim 6
Dependent Claim
20 words
The method as in claim 1, in which said nodularizing agent has an average particle size diameter of 1/4-1/6 inch.
Claim 7
Dependent Claim
65 words
A ferritic-bainitic ductile cast iron composition, consisting essentially by weight of 3.0-3.6% carbon, 3.5-5.0% silicon, 0.7-5.0% nickel, 0-0.3% molybdenum, 0.2-0.4% manganese, less than 0.06% phosphorus, less than 0.015% sulphur, 0.02-0.06% magnesium, and the remainder essentially iron, said composition being particularly characterized by a microstructure having a matrix with 70-85% bainite, 15-30% acicular ferrite, and 0-2% massive austenite, the graphite nodules being dispersed throughout the matrix.
Claim 8
Dependent Claim
65 words
A ferritic-bainitic ductile cast iron composition, consisting essentially by weight of 3.0-3.6% carbon, 3.5-5.0% silicon, 0.7-5.0% nickel, 0-0.3% molybdenum, 0.2-0.4% manganese, less than 0.06% phosphorus, less than 0.015% sulphur, 0.02-0.06% magnesium, and the remainder essentially iron, said composition being particularly characterized by a microstructure having a matrix with 70-85% bainite, 15-30% acicular ferrite, and 0-2% massive austenite, the graphite nodules being dispersed throughout the matrix.
Claim 9
Dependent Claim
31 words
The composition as in claim 6, in which said composition exhibits a tensile strength of at least 140 ksi, a yield strength of at least 80 ksi, an elongation of 6-10%.
Claim 10
Dependent Claim
20 words
The composition as in claim 7, in which said composition additionally exhibits a hardness level of at least 270 BHN.
Claim 11
Independent Claim
155 words
A method of making a ductile cast iron having a microstructure with a matrix consisting essentially of ferrite and bainite, said cast iron exhibiting a tensile strength of at least 140 ksi, a yield strength of at least 80 ksi, and an elongation of 6-10%, the method comprising: (a) melting a ferrous alloy comprising by weight 3.0-3.6% carbon, 3.5-5.0% silicon, 0.2-0.4% manganese, and the remainder essentially iron except for the presence of selected bainite formers and low phosphorus and sulfur, the melted ferrous alloy being subjected to a nodularizing agent to form ductile cast iron upon solidification and cooling; (b) heat treating said ductile iron by heating to 1575°-1650° F. for a period of 1-3 hours and immediately quenching to 675°-750° F. at a rate of at least 275° F./min; and (c) holding said ductile iron in the temperature range of 400°-775° F. for a period of 0.5-4 hours followed by cooling to room temperature.
Claim 12
Independent Claim
155 words
A method of making a ductile cast iron having a microstructure with a matrix consisting essentially of ferrite and bainite, said cast iron exhibiting a tensile strength of at least 140 ksi, a yield strength of at least 80 ksi, and an elongation of 6-10%, the method comprising: (a) melting a ferrous alloy comprising by weight 3.0-3.6% carbon, 3.5-5.0% silicon, 0.2-0.4% manganese, and the remainder essentially iron except for the presence of selected bainite formers and low phosphorus and sulfur, the melted ferrous alloy being subjected to a nodularizing agent to form ductile cast iron upon solidification and cooling; (b) heat treating said ductile iron by heating to 1575°-1650° F. for a period of 1-3 hours and immediately quenching to 675°-750° F. at a rate of at least 275° F./min; and (c) holding said ductile iron in the temperature range of 400°-775° F. for a period of 0.5-4 hours followed by cooling to room temperature.
References Cited (Backward Citations)
US2324322A
Cited
US3549430A
Cited
US3600159A
Cited
US3673004A
Cited
US3702269A
Cited
SU753923A1
Cited
JPS54133420A
Cited
JPS5627747A
Cited
JPS5630453A
Cited
JPS57131321A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-11-27 | 1988-05-28 | 1988-11-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-11-27 | 1992-05-28 | 1992-11-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-11-27 | 1996-05-28 | 1996-11-27 | $7700.00 | Window Closed / Lapsed |