Method for producing high-strength inorganic cement articles
Assignee: Inax Corp
•
Filing: 1985-02-20
•
Granted: 1987-05-05
•
Expires: 2005-02-20
Abstract
Abstract A novel method for producing a high-strength inorganic cement article is provided. The method comprises kneading under high shearing force a cement mixture containing as essential components hydraulic cement, a hydrophilic organic binder and water, molding the kneaded mixture into an article having a water-to-solid weight ratio of not more than about 0.2, preliminarily hydrating the molded article, firing the preliminarily hydrated article at about 300° to about 1000° C., and then rehydrating the fired article. The resulting cement article has bending strength of not lower than about 200 kgf/sq.cm without fibrous reinforcing materials and has that of not lower than about 350 kgf/sq.cm when reinforced with heat-resistant fiber materials. The cement article can be advantageously glazed in the above mentioned method by applying a glazing agent to a desired surface of the preliminarily hydrated article and then firing the article.
Inventors
- 👤 Kazuo Ito
- 👤 Seiji Terabe
- 👤 Shozo Harada
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 19:00
CPC Classifications
C; C04; C04B; C04B20/00; C04B20/02; C04B20/04; C04B28/00; C04B28/02; C04B40/00; C04B40/02; C04B40/0263; C04B40/0268; C04B2111/00; C04B2111/00034; C04B2111/00068; C04B2111/00241; C04B2111/00301
Claims Analysis
Total Claims: 24
Claim 1
Independent Claim
123 words
A method for producing a high-strength inorganic cement article, which comprises kneading under high shearing force a cement mixture containing by weight as essential components 100 parts of hydraulic cement, about 0.5 to about 15 parts of a hydrophilic, substantially adhesive organic binder and water, said binder and said high shearing force being effective to promote adherence among cement mixture particles during said kneading step to thereby minimize inclusion of air and excess moisture in the kneaded mixture; molding the resulted kneaded mixture to an article having a water-to-solid weight ratio of not more than about 0.2; preliminarily hydrating the molded article; firing the resulting hydrated article at a temperature of about 300° to about 1000° C.; and then hydrating the fired article.
Claim 2
Independent Claim
123 words
A method for producing a high-strength inorganic cement article, which comprises kneading under high shearing force a cement mixture containing by weight as essential components 100 parts of hydraulic cement, about 0.5 to about 15 parts of a hydrophilic, substantially adhesive organic binder and water, said binder and said high shearing force being effective to promote adherence among cement mixture particles during said kneading step to thereby minimize inclusion of air and excess moisture in the kneaded mixture; molding the resulted kneaded mixture to an article having a water-to-solid weight ratio of not more than about 0.2; preliminarily hydrating the molded article; firing the resulting hydrated article at a temperature of about 300° to about 1000° C.; and then hydrating the fired article.
Claim 3
Dependent Claim
30 words
The method according to claim 1, in which the cement mixture contains not more than about 500 parts by weight of aggregate per 100 parts by weight of the cement.
Claim 4
Dependent Claim
17 words
The method according to claim 2, in which the aggregate used has a small thermal expansion coefficient.
Claim 5
Dependent Claim
22 words
The method according to claim 1, in which the cement mixture contains an effective amount of a substantially heat-resistant fibrous reinforcing material.
Claim 6
Dependent Claim
22 words
The method according to claim 1, in which the cement article has a bending strength of not lower than about 200 kgf/sq.cm.
Claim 7
Dependent Claim
32 words
The method according to claim 1, in which the cement mixture kneaded under high shearing force is molded into an article having a water-to-solid weight ratio of not more than about 0.18.
Claim 8
Dependent Claim
34 words
The method according to claim 1, in which the preliminarily hydrated article has a pore size (50% median) of not larger than about 100 millimicrons and a porosity of not more than about 50%.
Claim 9
Dependent Claim
33 words
The method according to claim 1, in which the cement article has a pore size (50% median) of not larger than about 300 millimicrons and a porosity of not more than about 45%.
Claim 10
Dependent Claim
50 words
The method according to claim 1, in which a glazing agent is applied onto the desired surface of the preliminarily hydrated article, the resulting article is fired at a temperature of from the melting temperature of the glazing agent to about 1000° C., and the fired article is then hydrated.
Claim 11
Dependent Claim
22 words
The method according to claim 2, in which the cement article has a bending strength of not lower than about 200 kgf/sq.cm.
Claim 12
Dependent Claim
32 words
The method according to claim 2, in which the cement mixture kneaded under high shearing force is molded into an article having a water-to-solid weight ratio of not more than about 0.18.
Claim 13
Dependent Claim
34 words
The method according to claim 2, in which the preliminarily hydrated article has a pore size (50% median) of not larger than about 100 millimicrons and a porosity of not more than about 50%.
Claim 14
Dependent Claim
33 words
The method according to claim 2, in which the cement article has a pore size (50% median) of not larger than about 300 millimicrons and a porosity of not more than about 45%.
Claim 15
Dependent Claim
50 words
The method according to claim 2, in which a glazing agent is applied onto the desired surface of the preliminarily hydrated article, the resulting article is fired at a temperature of from the melting temperature of the glazing agent to about 1000° C., and the fired article is then hydrated.
Claim 16
Dependent Claim
30 words
The method according to claim 4, in which the cement mixture contains not more than about 500 parts by weight of aggregate per 100 parts by weight of the cement.
Claim 17
Dependent Claim
22 words
The method according to claim 4, in which the cement article has a bending strength of not lower than about 350 kgf/sq.cm.
Claim 18
Dependent Claim
32 words
The method according to claim 4, in which the cement mixture kneaded under high shearing force is molded into an article having a water-to-solid weight ratio of not more than about 0.18.
Claim 19
Dependent Claim
34 words
The method according to claim 4, in which the preliminarily hydrated article has a pore size (50% median) of not larger than about 100 millimicrons and a porosity of not more than about 50%.
Claim 20
Dependent Claim
33 words
The method according to claim 4, in which the cement article has a pore size (50% median) of not larger than about 300 millimicrons and a porosity of not more than about 45%.
Claim 21
Dependent Claim
50 words
The method according to claim 4, in which a glazing agent is applied onto the desired surface of the preliminarily hydrated article, the resulting article is fired at a temperature of from the melting temperature of the glazing agent to about 1000° C., and the fired article is then hydrated.
Claim 22
Independent Claim
175 words
A method for producing a high-strength inorganic cement article, which comprises kneading under high shearing force a cement mixture containing by weight as essential components 100 parts of hydraulic cement, about 0.5 to about 15 parts of a hydrophilic, substantially adhesive organic binder and water, said binder being effective to promote adherence among cement mixture particles during said step of kneading under high shearing force; molding the resulting kneaded mixture to an article having a water-to-solid weight ratio of not more than about 0.2; preliminarily hydrating the molded article; firing the resulting hydrated article at a temperature of about 300° to about 1000° C.; and then hydrating the fired article, said high shearing forces and said binder being effective to minimize inclusion of air and excess water in said mixture during said kneading step to an extent sufficient to impact a pore size (50% median) of not larger than about 100 millimicrons and a porosity of not more than about 50% to the preliminary hydrated molded article formed in said molding and preliminarily hydrating steps.
Claim 23
Independent Claim
175 words
A method for producing a high-strength inorganic cement article, which comprises kneading under high shearing force a cement mixture containing by weight as essential components 100 parts of hydraulic cement, about 0.5 to about 15 parts of a hydrophilic, substantially adhesive organic binder and water, said binder being effective to promote adherence among cement mixture particles during said step of kneading under high shearing force; molding the resulting kneaded mixture to an article having a water-to-solid weight ratio of not more than about 0.2; preliminarily hydrating the molded article; firing the resulting hydrated article at a temperature of about 300° to about 1000° C.; and then hydrating the fired article, said high shearing forces and said binder being effective to minimize inclusion of air and excess water in said mixture during said kneading step to an extent sufficient to impact a pore size (50% median) of not larger than about 100 millimicrons and a porosity of not more than about 50% to the preliminary hydrated molded article formed in said molding and preliminarily hydrating steps.
Claim 24
Dependent Claim
25 words
A method as claimed in claim 21 wherein the bending strength of the fired, hydrated article is not lower than about 200 Kgf/cm 2 .
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-05-04 | 1990-11-03 | 1991-05-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-05-04 | 1994-11-03 | 1995-05-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-05-04 | 1998-11-03 | 1999-05-05 | $7700.00 | Window Closed / Lapsed |